Polymerization-Crosslinking of N-Methylolacrylamide in Cotton Fabric

Abstract

Several variations of polymerization-crosslinking of N-methylolacrylamide (NMA) in cotton were explored to clarify factors critical to achievement of resilience with superior retentions of strength and abrasion resistance in fabric. Per sulfate catalysis simultaneously initiated both polymerization and crosslinking reactions of NMA in cotton fabric; the results from dry-cure reactions fell in the conventional range of textile performance properties achieved by treatment of cotton fabric with agents such as dimethyloldihydroxyethyleneurea. Wet-cure reactions carried out in scaled bags at or above 100°C resulted in low resilience, high retentions of strength-abrasion resistance, and large increases in stiffness, the last attributed to fiber bonding in yarns. Wet-cure reactions conducted at or below 80°C caused little stiffness, and only in these cases was a subsequent catalyzed dry-cure reaction effective in raising resilience with good retentions of strength and abrasion resistance. Inclusion of alkali metal phosphates in the persulfate-initiated reaction of NMA with cotton in a pad-dry-cure caused retentions of abrasion resistance to be very substantially improved and retentions in breaking and tearing strengths to be significantly improved at durable-press appearance ratings of 4.5. These results are attributed to relatively sequential but rapid polymerization and crosslinking reactions, to reduction in formation of oxymethylene crosslinks, and possibly to reduced molccular degradation of the cellulose.

Get full access to this article

View all access options for this article.

References

Asnes, H. , Eden, C. , and Larking, R. , Crosslinking of Cotton by Graft Polymerization with Vinyl Monomers, Textile Res. J. 39, 1110 1116 (1969).

Bailey, T.L.W. , Jr. and Rollins, M.L. , Some Applications of Microscopy to Cotton Research, Textile Res. J. 15, 1-6 (1945).

Bertoniere, X.R. , Martin, L.F. , Blouin, F.A. , and Rowland, S.P. , Effects of Polymerization Parameters of Methylolated Melamines upon the Wet-Fixation, Durable-Press Process for Treating Cotton Fabrics, Textile Res. J. 44, 140-146 (1974).

Bertoniere, N.R. and Rowland, S.P. , Improved Durable-Press Cotton via Polymeric X-Methylol Reagents, Textile Res. J. 46, 311 318 (1976).

Doshi, B.A. and Varghese, J. , Studies on the Use of Acry I-amidc and Its Methylol Derivative as Finishing Agents for Cotton Textiles, Colourage 20, 29-34 (1973).

Dziedziela, W.M. and Rosiak, J. , Reactions of N-Methylolacrylamide in Radiation-Chemical Modification of Cotton Fabrics, J. Polymer Sci. Smyp. No. 47, 273-283 (1974).

Gardon, J.L. , Free Radical-Catalyzed Reaction of the Acrylamidomethyl Ether of Cotton, J. Polymer Sci. A-2, 2657-2672 (1964).

Hobart, S.R. , An Investigation of the Reversibility of N-Methylolacrylamide Crosslinks on Cotton , Textile Res. J. 37, 380-390 (1967).

Hollies, N.R.S. and Getchell, N.F. , Wet-Fixation Process for Improved Durable-Press Cotton, Textile Res. J. 37, 70-76 (1967).

10.

Kamel, M. , Hebeish, A. , Allam, M. , and Al-Aref, A., Creation of Reactive Centers on Cotton. II, J. Appl. Polymer Sci. 17, 2725-2733 (1973 ).

11.

Kamogawa, H. , Murase, R. , and Sekiya, T. , Polymerization and Condensation Reaction of N-Methylolacrylamide within Cotton Fabric, Textile Res. J. 30, 774-781 (1960).

12.

Rowland, S.P. , Bertoniere, N.R. , and Martin, L.F. , The Development of Abrasion Resistance and Breaking Strength in Durable-Press Cotton Fabrics, Textile Res. J. 44, 595-599 (1974).

13.

Rowland, S.P. , Cirino, V.O. , and Bullock, A.L. , How the Structure of Crosslinked Cotton Affects Fabric Performance, Textile Chem. Color. 1, 450-457 (1969).

14.

Segal, L. and Timpa, J.D. , Strength Losses and Structural Changes in Cotton Fabric Crosslinked with Dimethylolethyleneurea , Textile Res. J. 43, 185 194 (1973).

15.

Walsh, W.K. and Rutherford, H.A. , Delayed Cure with Ionizing Radiation, Textile Res. J. 37, 89 93 ( 1967).

16.

Welo, L.A. , Ziifle, H.M. , and McDonald, A.W. , Swelling Capacities of Fibers in Water. II: Centrifuge Studies, Textile Res. J. 22, 261 273 ( 1952).