Contribution to the Study of the Porous Structure of Polyacrylonitrile (PAN) Fibers The Effects of Heat Treatments

Abstract

The porous fraction of PAN fibers, as shown by the formation in situ of silver sulfide, consists of radial paths which may or may not be associated with different distributions of micropores. The radial paths generally originate from microlobes or surface faults. The size of these porous zones, their number, and their mode of distribution in the structure itself are generally affected by technological operations involving tension and heat treatment. During the dry heat treatments, the fibers have a tendency to collapse, with a simultaneously decrease of the void sizes and appearance of new gaps of the same sort that characterized the original sample. The wet-phase treatments are usually accompanied by swelling of the fibers, limited when fibers are maintained at constant length. The introduction of water molecules into the struc ture produces distortions in the ordered zones and the structural rearrangement that results eliminates the initial porosity but leaves many fine micropores which are localized in the periphery of the fibers. This latter effect can be compared to a fiber-skin rupture.

Keywords

Wet-spun PAN fibers dry-spun PAN fibers PAN fibers. Nitrogen water. Temperature. Pore distribution fine structure microlobes swelling distortion line-broadening orientation. Porous structure. X-ray diffraction stain ing electron microscopy light microscopy annealing wet heat treatment dry heat treatment heat treatments.

Get full access to this article

View all access options for this article.

References

Cernia, E. , Acrylic Fibers in "Man-Made Fibers: Science and Technology," Interscience Vol. 3. New York, 1968, pp. 135-198.

Diemunsch, J., Chabert , and Banderet , A. , Contribution à l'Étude de la Sorption des Fibres Textiles, I.T.F. Bull. 117, 201-227 (1965).

Feichtmayr, F. and Wurz, A. , The Interaction Forces between Polyacrylonitrile Fibres and Disperse and Cationic Dyes, J. Soc Dyers Colourists 77, 626-637 (1961).

Hagege, R. , Kassenbeck, P. , Meimoun, D. , and Parisot, A. , Electron Microscopy of Cellulosic Structures by Inclusion of Stainable Unsaturated Polymers, Textile Res. J. 39, 1015-1023 (1969).

Happey, F. , Preferred Orientation in Organic Polycrystalline Materials, in " X-Ray Diffraction by Polycrystalline Materials," London , Chapman and Hall 1960, pp. 481-496.

Holland, U.P. , Mitchell, S.B. , Munter , W.L. , and Lindenmeyer, Ph., Crystal Structure and Morphology of Polyacrylonitrile in Dilute Solution . J. Polymer Sci. 145-151 (1962).

Jacquemart, J. and Monrocq, R. , Technique Rapide de Microtomie pour le Laboratoire Textile, I.T.F. Bull 120, 763-776 (1965).

Klug-Alexander "X-Ray Diffraction Procedures For Polycrystalline and Amorphous Materials," New York, Wiley, 1954, pp. 490-538.

Legrand, C. and Gervais, H. , Brevet C.N.R.S., n° 1,400,555 (1965).

10.

Mezhirov, M.S. , and Pakshver, E.A. , Causes For the Formation of Radial Pores in Polyacrylonitrile Fibres, Khim. Volakna No. 3, 13-16 (1968).

11.

Saum, A.M. , Intermolecular Association in Organic Nitriles; the CN Dipole-Pair Bond, J. Polymer Sci. 42, 57-66 (1960).

12.

Sotton, M. , Développement d'une Technique de Révélation des Structures Poreuses. Application aux Hauts Polymères Fibreux, C. R. Acad. Sc. Paris 270, B, 1261-1264 (1970 ).

13.

Sotton, M. , Hagege, R. , and Jacquemart, J. , Résultats Relatifs à l'Étude des Structures Poreuses des Fibres Textiles en Microscopies Optique et Électronique, I.T.F. Bull. 150. 763-783 (1970).

14.

Sotton, M. , Bouriot, P. , and Jacquemart, J. , Internal Reports, I.T.F. Physics Laboratory, 1969.

15.

Sotton, M. and Vialard, A.M. , Influence des Traitements Thermiques sur la Structure Poreuse des Fibres de Polyacrylonitrile, C.R.Acad. Sc. Paris 272, C, 1281-1384 (1971).

16.

Statton, W.O. , Small-Angle X-Ray Studies of Polymers in "Newer Methods of Polymer Characterization," New York, Interscience 1964, pp. 231-278.

17.

Statton, W.O. , An X-Ray Crystallinity Index Method with Application to Poly (Ethylene Terephtalate), J. Appl. Polymer Sci. 7, 803-815 (1963).

18.

Stefani, R. , Chevreton, M. , Garnier , M. and Eyraud, C. , Crystalline Structure of Polyacrylonitrile , C.R. Acad. Sci. 251, 2174-2176 (1960 ).

19.

Takeda, Hiromu and Nukushina, Yasuhiko , Influence of Drying Temperature and Humidity on the Internal Structure of Acrylic Fibres During Drying, Textiles Res. J. 34, 173-175 (1964).

20.

Masao, Takahashi , Nukushina, Yasuhiko , Kosugi, Setsuko , Effect of Fiber-Forming Conditions on the Microstructure of Acrylic Fiber, Textile Res. J. 34, 87-97 (1964).

21.

Trillat, J.J. and Legrand, C. , Récentes Techniques de Rayons X Adaptées à l'Étude des Fibres, I.T.F. Bull. 96, 7-27 (1961).

22.

Wegener, H. and Egbers, G. , Mechanisch-Technologische Eigenschaften und Struktur eines Unbehandelten und eines Thermisch Behandelten Polyacrylnitril Copolymerisates. Textile-Industrie 11, 864-871 (1966).

23.

Wenger, P. and Buckert, R. , "Treatise on Qualitative Chemical Analysis," University Library. Geneva, Georg. and Co.