Evaluation of the crimp formability of side-by-side PLA/PTT bicomponent fibers

Abstract

To explore the feasibility of developing bio-based elastic fibers, bio-based polylactide (PLA) and polytrimethylene terephthalate (PTT) were selected for fabrication of side-by-side bicomponent fibers using bi-constituent melt-spinning technology. The structure development and performance of PLA/PTT bicomponent fibers was investigated using thermal mechanical analysis, differential scanning calorimetry, and wide-angle X-ray diffraction in order to evaluate the crimp formability of PLA/PTT bicomponent fibers. The PLA and PTT components could form regular boundary structure and exhibit excellent interface compatibility by regulation of the rheological behavior of the two melts. In the fiber forming process, the PTT component in PLA/PTT bicomponent fibers experienced higher tensile stress, and thereby enhanced the crystal and oriented structure development, while the structural evolution of the PLA component was inhibited. The difference in the structure of the two components causes the imbalance force existence in the PLA/PTT fibers, which is the main reason of fiber crimp. In addition, the crimp formability of the PLA/PTT fibers could be enhanced by expanding the shrinkage stress difference between the two components, which could be realized by increasing the PTT ratio in PLA/PTT bicomponent fiber or draw ratio. The maximum crimp extension that could be achieved was 85% for the bicomponent fibers with PLA30/PTT70 ratio at a draw ratio of 4.2.

Keywords

PLA/PTT bicomponent fiber side-by-side bicomponent fiber self-crimping crimp-formation ability

Get full access to this article

View all access options for this article.

References

Zhu

New developments in elastic fibers.

Polym Rev 2008; 48(2): 275–301.

Song

Structure and elasticity of elastic fiber and its dyeing and finishing (I).

Dyeing Finish 2006; 8: 44–46.

Han

, et al. Study on hyperbranched polyesters as rheological modifier for Spandex spinning solution. Polym Int 2006; 55(8): 898–903.

Chen

Wang

Tensile and fracture behaviors of PET/PTT side-side bicomponent filament.

Int J Polym Anal Ch 2010; 15(3): 147–154.

Luo

Wang

, et al. External configuration and crimp parameters of PTT (Polytrimethylene terephthalate)/PET (Polyethylene terephthalate) conjugated fiber. Fiber Polym 2009; 10(4): 508–512.

TH.

Melt spinning and drawing process of PET side-by-side bicomponent fibers.

J Appl Polym Sci 2006; 101(3): 1362–1367.

Choi

Kim

SY.

Effects of interface on the dynamic mechanical properties of PET/nylon 6 bicomponent fibers.

J Appl Polym Sci 1999; 74(8): 2083–2093.

Prahsarn

Klinsukhon

Roungpaisan

, et al. Self-crimped bicomponent fibers containing polypropylene/ethylene octene copolymer. Mater Lett 2013: 232–234.

Ayad

Cayla

Rault

, et al. Influence of rheological and thermal properties of polymers during melt spinning on bicomponent fiber morphology. J Mater Eng Perform 2016; 25(8): 3296–3302.

10.

Suaria

Achtypi

Perold

, et al

. Microfibers in oceanic surface waters: A global characterization.

Sci Adv 2020; 6(23): 8493.

11.

Zhang

Garrison

Madbouly

, et al. Recent advances in vegetable oil-based polymers and their composites. Prog Polym Sci 2017; 91–143.

12.

Nagarajan

Mohanty

Misra

, et al. Reactive compatibilization of poly trimethylene terephthalate (PTT) and polylactic acid (PLA) using terpolymer: Factorial design optimization of mechanical properties. Mater Design, 2016; 110: 581–591.

13.

Lin

Song

Huang

, et al. Rheology of poly(lactic acid)/poly(trimethylene terephthalate) blends compatibilized by clay or maleic anhydride-grafted poly(ethylene-octene) elastomer. J Polym Eng 2019; 39(3): 248–253.

14.

Padee

Thumsorn

J W

, et al. Preparation of Poly(lactic acid) and Poly(trimethylene terephthalate) blend fibers for textile application. Energy Procedia 2013: 534–541.

15.

Rwei

Lin

, et al. Study of self-crimp polyester fibers. Polym Eng Sci 2005; 45(6): 838–845.

16.

Denton

MJ.

The crimp curvature of bicomponent fibres

. J Text I 1982; 73(6): 253–263.

17.

Southern

Ballman

RL.

Additional observations on stratified bicomponent flow of polymer melts in a tube.

J Polym Sci Pol Phys 1975; 13(4): 863–869.

18.

Han

CD.

A study of coextrusion in a circular die.

J Appl Polym Sci 1975; 19(7): 1875–1883.

19.

TH.

Effects of spinning and drawing conditions on the crimp contraction of side-by-side poly(trimethylene terephthalate) bicomponent fibers. J Appl Polym Sci 2006; 102(2): 1322–1327.

20.

Okihara

Tsuji

Kawaguchi

, et al. Crystal structure of stereocomplex of poly(L-lactide) and poly(D-lactide). J Macromol Sci B 1991; 30(1–2): 119–140.

21.

Takasaki

Ito

Kikutani

, et al. Development of stereocomplex crystal of polylactide in high-speed melt spinning and subsequent drawing and annealing processes. J Macromol Sci B 2003; 42(3): 403–420.

22.

Kathiervelu

Polytrimethylene terephthalate (PTT) fibres. Synthetic Fibres 2002; 31 (4): 11–12.

23.

Che

Locker

Lee

, et al. Plastic deformation of semicrystalline polyethylene by X-ray scattering: Comparison with atomistic simulations. Macromolecules 2013; 46(13): 5279–5289.

24.

Ran

Fang

Zong

, et al. Structural changes during deformation of Kevlar fibers via on-line synchrotron SAXS/WAXD techniques. Polymer 2001; 42(4): 1601–1612.

25.

Tian

Chen

, et al. Structure and property development of aromatic copolysulfonamide fibers during wet spinning process. J Appl Polym Sci 2015; 132(31): 42343.

26.

Martin

Avérous

Poly(lactic acid): plasticization and properties of biodegradable multiphase systems.

Polymer 2001; 42(14): 6209–6219.

27.

Zhang

Study of poly(trimethylene terephthalate) as an engineering thermoplastics material.

J Appl Polym Sci 2004; 91(3): 1657–1666.

28.

Pan

Liang

Cao

, et al. Layered metal phosphonate reinforced poly (l -lactide) composites with a highly enhanced crystallization rate. Acs Appl Mater Inter 2009; 1(2): 402–411.

29.

Hill

Cuculo

JA.

An experimental study of threadline dynamics with emphasis on the effect of molecular weight on the elongational viscosity of melt-spun poly(ethylene terephthalate). J Appl Polym Sci 1974; 18(9): 2569–2588.