Shear Flow Properties and Melt Spinning of Thermoplastic Polyvinyl Alcohol Melts

Abstract

Polyvinyl alcohol (PVA) is a water-soluble polymer, which is difficult to process in melt form owing to its poor processability and thermoplasticity. The thermoplastic polyvinyl alcohol (TPVA) prepared in this study is a brand new material for use in melt spinning. Satisfactory processability of TPVA can be obtained efficiently by using the plasticization method. First, the shear flow properties of TPVA made with various compositions were investigated. The experimental results indicate that, besides decreased viscosity, increased plasticizer loading and decreased degrees of polymerization of TPVA caused a decrease in the non-Newtonian property and increased the temperature sensitivity of the viscosity. Additionally, under the given experimental conditions, all the TPVA melts with various compositions demonstrated satisfactory flowability and spinnability and no melt fracture occurred. With regard to spinability, the TPVA melts displayed decreasing spinnability as the plasticizer loading was increased or the degree of polymerization was decreased. Moreover, the failure of TPVA melts is mainly attributed to ductile rupture. Observation of the WAXD patterns of the TPVA as-spun fibers indicates difficulty in improving the crystallinity and orientation of TPVA, which was due to the addition of plasticizer and the use of partially hydrolyzed PVA. Furthermore, processing under appropriate spinning conditions and avoiding excessively high temperature can maintain considerable water solubility of TPVA, benefiting its application in conjugate spinning

Get full access to this article

View all access options for this article.

References

Asaletha, R. , Groeninckx, G. , Kumaran, M. G. , and Thomas, S. , Melt Rheology and Morphology of Physically Compatibilized Natural Rubber-Polystyrene Blends by the Addition of Natural Rubber-g-Polystyrene , J. Appl. Polym. Sci. 69, 2673-2690 (1999).

Bocayuva, L. R. , Gomes, A. S. , Oliverira, C. M. F. , and Amorim, M. C. V. , Rheological Properties of Blends of Polycarbonate with Poly(ethylene oxide) , Polym. Test. 19, 321-327 (2000).

Cogswell, F. N. , “Polymer Melt Rheology,” John Wiley & Sons, New York , 1981, pp. 25, 135.

Covas, J. A. , Nóbrega, J. M. , and Maia, J. M. , Rheological Measurements Along an Extruder with an On-Line Capillary Rheometer , Polym. Test. 19, 165-176 (2000).

Finch, C. A. , “Polyvinyl Alcohol Properties and Applications,” John Wiley & Sons, New York , 1973.

Finch, C. A. , “Polyvinyl Alcohol Developments,” John Wiley & Sons, New York , 1992.

Han, C. D. , “Rheology in Polymer Processing,” Academic Press, New York , 1976.

Haralabakopoulos, A. A. , Tsiourvas, D. , and Paleos, C. M. , Modification of Poly(vinyl alcohol) with Aliphatic and Aromatic Epoxides in the Molten Phase , J. Appl. Polym. Sci. 62, 1597-1604 (1996).

Hsieh, T. -T. , Tiu, C. , and Simon, G. P. , Melt Rheology of Aliphatic Hyperbranched Polyesters with Various Molecular Weights , Polymer 42, 1931-1939 (2001).

10.

Koizumi, T. , and Usui, S. , The Dependence of Shear and Elongational Viscosity on the Molecular Weight of Poly(vinylidene fluoride) , J. Appl. Polym. Sci. 71, 2381-2384 (1999).

11.

Laba, D. , “Rheological Properties of Cosmetics and Toiletries,” Marcel Dekker, New York , 1993, pp. 18.

12.

Liang, J. Z. , and Ness, J. N. , Investigation on the Melt Flow Properties of Polyethylene and Polypropylene Blends , Polym. Test. 16, 379-389 (1997).

13.

Liang, J. Z. , and Ness, J. N. , Studies on melt flow properties of low density and linear low density polyethylene blends in capillary extrusion , Polym. Test. 16, 173-184 (1997).

14.

Liang, J. Z. , and Ness, J. N. , Relationship Between melt shear viscosity and molecular parameters based on high impact polystyrenes in capillary extrusion , Polym. Test. 18, 37-46 (1999).

15.

Liu, Z. , Feng, Y. , and YI, X. , Thermoplastic Starch/PVAI Compounds: Preparation, Processing, and Properties , J. Appl. Polym. Sci. 74, 2667-2673 (1999).

16.

Mckelvey, J. M. , “Polymer Processing,” John Wiley & Sons, New York , 1962.

17.

Nakajima, T. , “Advanced Fiber Spinning Technology,” Woodhead Publishing, Cambridge, UK , 1994.

18.

Oommen, Z. , Zachariah S. R. , Thomas, S. , Groeninckx, G. , Moldenaers, P. , and Mewis, J. , Melt Rheology and Morphology of Uncompatibilized and In Situ Ccompatibilized Nylon-6/Ethylene Propylene Rubber Blends , J. Appl. Polym. Sci. 92, 252-264 (2004).

19.

Tsebrenko, M. V. , Rezanova, N. M. , and Tsebrenko, I. A. , Fiber-Forming Properties of Polymer Mixture Melts and Properties of Fibers on Their Basis , Polym. Eng. Sci. 39, 2395-2402 (1999).