A New Cellulose Based Carbon Fiber from a Lyocell Precursor

Abstract

The structure and properties of lyocell and viscose rayon fibers are compared in this paper. SAXS results show that the rayon precursor has a higher ratio of larger microvoids, WAXD curves show that both fibers have a monoclinic crystalline structure, but lyocell fibers have higher crystallinity and a larger crystal size. The morphology of lyocell and rayon, observed by scanning electron microscopy (SEM), is the same with an average diameter of 10.6 μm, but different distributions. A Gaussian statistical analysis indicates that the single-strand strength of lyocell fibers is twice as high as for rayon precursors, which have a wider strength distribution. Similar TGA curves show the same pyrolysis mechanism, and based on this, lyocell fibers are proposed as high performance carbon fiber precursors. Lyocell fibers are successfully carbonized under conditions identical to those for manufacturing rayon-based carbon fibers. The two kinds of carbon fibers are compared by SEM and a Weibull statistical analysis.

Get full access to this article

View all access options for this article.

References

Akzo , Cellulose Fibers and Films, Production-form Cellulose Solution in Solvent Comprising Mixture of Amine Oxide and Non-solvent for Cellulose, U.S. Patent 4416698, 1980.

Jayatilaka, A.S. , and Trustrum , K. , Statistical Approach to Brittle Fracture, J. Mater. Sci. 12, 1426-1430 (1977).

Konkin, A.A. , "Production of Cetiulose-based Carbon Material ," Elsevier Science Publishers, Berlin, Germany, 1985, pp. 283-285.

Lenz, J. , Schurz, J. , and Eichinger, D. , Properties and Structure of Lyocell and Viscose-type Fibres in the Swollen State, Lenzinger Ber. 74, 19-25 (1994).

Manders, P.W. , and Chou, T.W. , Variability of Carbon and Glass Fibers, and the Strength of Aligned Composites, J. Reinf. Plast Comp. 2, 43-59 (1983).

Masters, K.J. , and Mcenaney, B. , The Development of Structure and Microporosity in Cellulose Carbon, Carbon 22(6), 595 (1984).

Mohamed, R. Mili. Bouchaour. Toufik, and Merle, Paul. Estimation of Weibull Parameters from Loose-bundle Tests, Compos. Sci. Technol. 56, 831-834 (1996).

Schmidt, D.L. , and Craig, R.D. , Advanced Carbon Fabric, Phenolics for Thermal Protection Application, AD A116829, 1982.

Wu, Qilin , and Pan, Ding , Study of the Crystalline Structure of Rayon Fibers During Heat-treatment Using X-Ray Diffraction (in Chinese) , J. China Textile Univ. 24(6), 92-94 ( 1998).

10.

Yang, Xugang , and Chen, Huifang , Morphological Structure of Rayon Fibers during Carbonizing Process (in Chinese), J. China Textile Univ. 23(4), 1-7 (1997).