Thermal Adaptability and Hand of Wool Fabric Treated with High Molecular Weight Polyethylene Glycol and a Softener

Abstract

The aim of this study is to enhance the thermal adaptability of wool fabric by a treatment with high molecular weight polyethylene glycol (PEG-8000), and to improve the PEG-finished fabric's hand by treatment with a softener. Using the pad-dry-cure method, the fabric is treated in aqueous baths with 20-45% owb concentrations of PEG and 8.0-9.0% DMDHEU, resulting in 12-38% PEG add-ons proportional to the PEG concentrations. Subsequently, using the pad-cure method, the fabric is treated in aqueous solutions with 2-6% owb softener concentrations. Thermal adaptability, measured by heat of fusion and crystallization on a DSC, improves as PEG add-on increases. The PEG-treated fabric is stiffer and less smooth, soft, and full than when untreated, according to measurements with the KES-FB system. The PEG-treated fabric's thermal storage and release are 30-60% lower after softening, but the hand improves. Optimum conditions for maximizing thermal adaptability and achieving a hand equivalent to the untreated fabric are 45% PEG-8000/9.0% DMDHEU in the finishing bath and 6% softener solution concentration.

Get full access to this article

View all access options for this article.

References

1. Bruno, J. S. , and Vigo, T. L. , Temperature-Adaptable Fabrics with Multifunctional Properties, Textile Chem. Color. 20 (3), 17–20 (1988).

2. Bruno, J. S. , and Vigo, T. L. , Thermally Active Fabrics Containing Polyethylene Glycols, J. Coated Fabrics 16 (2), 264–284 (1987).

3. Business Week, Tomorrow's Clothes May Have Built-in Thermostats, 77, June 9, 1986.

4. Chem. Week, Fibers with Built-in Antifreeze, 20, 22 (July 9, 1986).

5. Goynes, W. R. , Vigo, T. L. , and Bruno, J. S. , Microstructure of Fabrics Chemically Finished for Thermal Adaptability, Textile Res. J. 60, 277–284 (1990).

6. Harlan, S. L., A New Concept in Temperature-adaptable Fabrics Containing Polyethylene Glycols for Skiing and Skiing-like Activities, in “High-tech Fibrous Material: Composites, Biomedical Materials, Protective Clothing, and Geotextiles,” American Chemical Society, Washington, D.C., 1991, pp. 248-259.

7. Kawabata, S. , “The Standardization and Analysis of Hand Evaluation,” 2nd ed., The Textile Machinery Society of Japan, Osaka, 1980.

8. Vigo, T. L. , and Bruno, J. S. , Improvement of Various Properties of Fiber Surfaces Containing Crosslinked Polyethylene Glycols, J. Appl. Polym. Sci. 37, 371–379 (1989).

9. Vigo, T. L. , and Bruno, J. S. , Properties of Knits Containing Crosslinked Polyethylene Glycols, Textile Chem. Color. 21 (5), 13–17 (1989).

10.

10. Vigo, T. L. , and Bruno, J. S. , Temperature-Adaptable Textiles Containing Durably Bound Polyethylene Glycols, Textile Res. J. 57, 427–429 (1987).

11.

11. Vigo, T. L. , and Frost, C. M. , Temperature-Adaptable Fabrics, Textile Res. J. 55 (12), 737–743 (1987).