This work fabricated CoMoNiTa3 medium-entropy alloys using the vacuum hot pressing process of powder metallurgy technology. Micron-grade cobalt (6.3 μm), molybdenum (13.2 μm), nickel (2.4 μm) and tantalum powders (25.0 μm) were combined using ball milling. The experiments utilised various hot pressing temperatures (1000, 1050, 1100, and 1150 °C) and hot pressing pressures (20, 35, and 50 MPa) to identify the optimal parameters for CoMoNiTa3 alloys, while simultaneously investigating the differences in microstructures. The experimental results reveal that the optimal hot pressing parameters of this alloy were 1100 °C at 50 MPa for 1 h. The sintering density was enhanced to 9.65 ± 0.01 g cm−3, while the hardness, transverse rupture strength, and flexural modulus reached 85.5 ± 0.1 HRA, 1370.3 ± 90.1 MPa and 168.6 ± 12.7 GPa, respectively. Moreover, the electrical conductivity was 6.53 ± 0.13 × 104 S cm−1. Furthermore, the electron probe microanalyser, electron backscatter diffraction, and transmission electron microscopy results confirmed the face-centred cubic solid solution, Ni3Ta, and μ phases of the CoMoNiTa3 structure, and no preferred grain orientation was found.
AmarAWangMLZhangLK, et al.Additive manufacturing of VCoNi medium-entropy alloy: microstructure evolution and mechanical properties. Addit Manuf2023; 68: 103522.
2.
SonSKwakJHaftlangF, et al.Corrosion behavior of VCrFeCoNi medium-entropy alloy in chloride solution. J Mater Res Technol2023; 22: 2372–2382.
3.
ChangYCLinKMaJL, et al.Improvement of corrosion and wear resistance of CoCrNiSi0.3 medium-entropy alloy by sputtering CrN film. Materials2023; 16: 1482.
4.
GaoNHuQWangYS, et al.Controlled precipitation and strengthening in a CuFeNiMn medium-entropy alloy. Mater Sci Eng A2022; 852: 143694.
5.
LiuXWLaplancheGKostkaA, et al.Columnar to equiaxed transition and grain refinement of cast CrCoNi medium-entropy alloy by microalloying with titanium and carbon. J Alloy Compd2019; 775: 1068–1076.
6.
WuJWTangXHZhangXM, et al.Realizing the combination of high strength and good ductility of Cu matrix composites with CrCoNi reinforcement particles and microlaminated structure. J Alloy Compd2021; 872: 159632.
7.
LaplancheGKostkaAReinhartC, et al.Reasons for the superior mechanical properties of medium-entropy CrCoNi compared to high-entropy CrMnFeCoNi. Acta Mater2017; 128: 292–303.
8.
RomankovSParkYCShchetininIV. Mechanical intermixing of components in (CoMoNi)-based systems and the formation of (CoMoNi)/WC nanocomposite layers on Ti sheets under ball collisions. Appl Surf Sci2017; 422: 544–556.
9.
ChengZZhuWWYangL, et al.Tuning the mechanical properties of Fex(CoMoNi)100-x high-entropy alloys via controlled formation of hard μ phase. Mater Sci Eng A2020; 773: 138881.
10.
ChangSHHsiaoYCHuangKT. Investigation of the vacuum hot pressing process on the mechanical properties, microstructures and material characteristics of Ni–35Mo–15Cr alloys. Powder Metall2022; 65: 141–150.
11.
ZhouCYGuoCPLiGG, et al.Investigation on the intermetallic compound Co3Ta and high-temperature phase equilibria in the Co–Ni–Ta system. Intermetallics2019; 108: 1–18.
12.
ZhaoCCChuKJMeiQS, et al.Laves phase strengthening in ultrafine-grained Co–Cr–Ta micropillars under uniaxial compression at modest temperature. Mater Sci Eng A2020; 791: 139782.
13.
ChangSHWangCLHuangKT. Influence of the vacuum hot pressing process on the microstructure, mechanical properties, and material characteristics of CrCoNiTa3 alloys. Vacuum2023; 207: 111637.
14.
ChangSHShihLCHuangKT. Effects of the vacuum hot pressing process on the microstructures, strengthening mechanisms, and mechanical properties of Ni–35Cr–12Mo–3Nb alloys. Vacuum2023; 213: 112139.
15.
LiXCuiLYLiJK, et al.Automation of intercept method for grain size measurement: A topological skeleton approach. Mater Des2022; 224: 111358.
16.
ASTM International. Standard test methods for apparent porosity, liquid absorption, apparent specific gravity, and bulk density of refractory shapes by vacuum pressure, designation: C830-00. West Conshohocken, PA: American Society for Testing and Materials, 2023, pp. 1–3.
17.
ASTM International. Standard test method for hardness testing of metallic materials, designation: E18-15. West Conshohocken, PA: American Society for Testing and Materials, 2016, pp. 1–38.
18.
ASTM International. Standard test method for transverse rupture strength of powder metallurgy (PM) specimens: B528-12. West Conshohocken, PA: American Society for Testing and Materials, 2016, pp. 1–3.
19.
ChangSHChangCYHuangKT, et al.Effect of process parameters on the microstructure and mechanical properties of vacuum hot-press sintered Co–50 mass% Cr alloys. Powder Metall2018; 61: 323–333.
20.
ChangSHLiaoCLHuangKT, et al.Investigation of the characteristics of submicron-structured powder-fabricated Cr50Ni50 alloys via different hot-press sintering pressures. Mater Trans2016; 57: 732–737.
21.
ASTM International, Standard test method for elastic modulus by thermomechanical analysis using three-point bending and controlled rate of loading: E2769-16. West Conshohocken, PA: American Society for Testing and Materials, 2018, pp. 1–5.
22.
OuyangBLPengDMLiaoJH, et al.First-principle investigation of the stability and mechanical properties of the binder phase B(B=Co and Ni) with the maximum solubility of the transition-group elements M(M=V, Ti, Ta, Mo, W and Cr). Mater Today Commun2023; 34: 105217.
23.
BaldanA. Review progress in Ostwald ripening theories and their applications to nickel-base superalloys. J Mater Sci2002; 37: 2171–2202.
24.
HallEO. The deformation and ageing of mild steel: III discussion of results. Proc Phys Soc B1951; 64: 747–753.
25.
PetchNJ. The cleavage strength of polycrystals. J Iron Steel Inst1953; 174: 25–28.
26.
HansenN. Hall-Petch relation and boundary strengthening. Scr Mater2004; 51: 801–806.
27.
JiangHHanKMQiaoDX, et al.Effects of Ta addition on the microstructures and mechanical properties of CoCrFeNi high entropy alloy. Mater Chem Phys2018; 210: 43–48.
28.
LiPZhangJXZhangYJ, et al.Density functional theory calculations of the double gamma prime Ni3Ta phase under pressure: structural, mechanical, and electronic properties. J Phys Chem Solids2020; 138: 109248.
29.
Van LooFJJBastinGFVrolijkJWGA, et al.Phase relations in the systems Fe–Ni–Mo, Fe–Co–Mo and Ni–Co–Mo at 1100°C. J Less-Common Met1980; 72: 225–230.
30.
ChangSHLinSSHuangKT. Effect of CrSi/CrSi2 content on the microstructure and properties of vacuum hot-pressed Cr–50 wt% Si alloys. Vacuum2019; 162: 54–62.
31.
ChangSHLinLYHuangKT. In situ TEM observation of the microstructural characteristics and mechanical properties of vacuum hot-press sintered Co–30Cr–6Mo alloys. Vacuum2020; 176: 109333.