Effect of Fluoride Concentration and pH on Corrosion Behavior of Titanium for Dental Use

Abstract

Titanium is used as a metal for biocompatible materials such as dental implants or restorations because of its excellent chemical stability. However, the corrosion of Ti in the prophylactic fluoride-containing environment can become problematic. To clarify the effects of fluoride concentration and pH on the corrosion behavior of Ti, we conducted anodic polarization and immersion tests in NaF solution of various concentrations and pH values. The concentrations of dissolved Ti in the test solutions were analyzed by inductively coupled plasma mass spectroscopy. There were obvious limits of fluoride concentration and the pH value at which the corrosion behavior of Ti changed. The corrosion of Ti in the solution containing fluoride depended on the concentration of hydrofluoric acid (HF). When the HF concentration in the solution was higher than about 30 ppm, the passivation film of the Ti was destroyed. The results of this study revealed a relation between the fluoride concentrations and pH values at which Ti corrosion occurred and provided data on such corrosion in environments where the fluoride concentration and pH value are known.

Keywords

titanium corrosion fluoride

Get full access to this article

View all access options for this article.

References

Bard JA ( 1976). In: Encyclopedia of electrochemistry of the element. Titanium. Vol. V. James WJ , Straumanis ME , editors. New York: Marcel Dekker, pp. 305-395.

Boere G. (1995). Influence of fluoride on titanium in an acidic environment measured by polarization resistance technique. J Appl Biomater 6:283-288.

Lausmaa J. , Kasemo B. , Hansson S. (1985). Accelerated oxide grown on titanium implants during autoclaving caused by fluorine contamination. Biomaterials 6:23-27.

Mimura H. , Miyagawa Y. (1996). Electrochemical corrosion behavior of titanium castings: Part 1. Effects of degree of surface polishing and kind of solution . Jpn J Dent Mater Dev 15:283-295.

Oda Y. , Kawada E. , Yoshinari M. , Hasegawa K. , Okabe T. (1996). The influence of fluoride concentration on the corrosion of titanium and titanium alloys. Jpn J Dent Mater Dev 15:317-322.

Probster L. , Lin W. , Hutteman H. (1992). Effect of fluoride prophylactic agents on titanium surface. Int J Oral Maxillofac Implants :390-394.

Sillen LG , Martell AE ( 1970). Stability constants of metal-ion complexes. Suppl No. 1, Part I. Inorganic ligands. In: Special publication No. 25 . London: The Chemical Society , p. 152.

Toumelin-Chemla F. , Rouelle F. , Burdairon G. (1996). Corrosive properties of fluoride-containing odontologic gels against titanium. J Dentistry 24:109-115.