Dental Composite Resins Containing Silica-fused Ceramic Single-crystalline Whiskers with Various Filler Levels

Abstract

Currently available direct-filling composite resins are susceptible to fracture and hence are not recommended for use in large stress-bearing posterior restorations involving cusps. The glass fillers in composites provide only limited reinforcement because of the brittleness and low strength of glass. The aim of the present study was to use ceramic single-crystalline whiskers as fillers to reinforce composites, and to investigate the effect of whisker filler level on composite properties. Silica particles were fused onto the whiskers to facilitate silanization and to roughen the whiskers, thereby improving retention in the matrix. The composite flexural strength, elastic modulus, hardness, and degree of polymerization conversion were measured as a function of whisker filler mass fraction, which ranged from 0% to 70%. Selected composites were polished simulating clinical procedures, and the surface roughness was measured with profilometry. The whisker composite with a filler mass fraction of 55% had a flexural strength (mean ± SD; n = 6) of 196 ± 10 MPa, significantly higher than 83 ± 14 MPa of a microfill and 120 ± 16 MPa of a hybrid composite control (family confidence coefficient = 0.95; Tukey's multiple comparison). The composite modulus and hardness increased monotonically with filler level. The flexural strength first increased, then plateaued with increasing filler level. The degree of conversion decreased with increasing filler level. The whisker composite had a polished surface roughness similar to that of a conventional hybrid composite (p > 0.1; Student's t). To conclude, ceramic whisker reinforcement can significantly improve the mechanical properties of composite resins; the whisker filler level plays a key role in determining composite properties; and the reinforcement mechanisms appear to be crack pinning by whiskers and friction from whisker pullout resisting crack propagation.

Keywords

composite resin reinforcement mechanism strength whisker filler level polishability

Get full access to this article

View all access options for this article.

References

American Society for Testing and Materials ( 1984). ASTM F417-78 : Standard test method for flexural strength of electrical grade ceramics. Philadelphia, PA: ASTM.

American Society for Testing and Materials ( 1991). ASTM E384: Standard test method for microhardness of materials. Philadelphia, PA: ASTM .

Antonucci JM , Stansbury JW (1990). Synthesis and properties of a polyfluorinated prepolymer multifunctional urethane methacrylate. In: Progress in biomedical polymers. Gebelein CG , Dunn RL , editors. New York: Plenum Press, pp. 121-131.

Antonucci JM , Fowler BO , Venz S. ( 1991). Filler systems based on calcium metaphosphates . Dent Mater 7:124-129.

Anusavice KJ (1996). Challenges to the development of esthetic alternatives to dental amalgam in an academic research center. Acad Dent Mater Trans 9:25-50.

Anusavice KJ , Hojjatie B. (1992). Tensile stress in glass-ceramic crowns: effect of flaws and cement voids. Int J Prosthodont 5:351-358.

Anusavice KJ , Zhang NZ , Moorhead JE (1994). Influence of colorants on crystallization and mechanical properties of lithiabased glass-ceramics. Dent Mater 10:141-146.

Bayne SC , Thompson JY (1996). Mechanical property analysis of two admixed PRIMM-modified commercial dental composites. Acad Dent Mater Trans 9:238.

Bayne SC , Heymann HO , Swift EJ Jr (1994). Update on dental composite restorations. J Am Dent Assoc 125:687-701.

10.

Bowen RL , Eichmiller FC , Marjenhoff WA (1992). Glass-ceramic inserts anticipated for "megafilled" composite restorations. J Am Dent Assoc 122:71-75.

11.

Braem M. , Finger W. , Van Doren VE , Lambrechts P. , Vanherle G. (1988). Mechanical properties and filler fraction of dental composites. Dent Mater 5:346-349.

12.

Carberry JL , Negrych JA (1992). Orthodontic bracket and associated fabricating method. US patent 5,078,596.

13.

Condon JR , Ferracane JL (1997). In vitro wear of composite with varied cure, filler level, and filler treatment. J Dent Res 76:1405-1411.

14.

Cross M. , Douglas WH , Fields RP (1983). The relationship between filler loading and particle size distribution in composite resin technology. J Dent Res 62:850-852.

15.

Eick JD , Byerley TJ , Chappell RP , Chen GR , Bowles CQ , Chappelow CC (1993). Properties of expanding SOC/epoxy copolymers for dental use in dental composites. Dent Mater 9:123-127.

16.

Eick JD , Kaufman GM , Chappelow CC (1997). Applications of polymers: what are the future trends? Acad Dent Mater Trans 10:89-98.

17.

Ferracane JL (1992). Using posterior composites appropriately. J Am Dent Assoc 123:53-58.

18.

Ferracane JL , Greener EH (1986). The effect of resin formulation on the degree of conversion and mechanical properties of dental restorative resins. J Biomed Mater Res 20:121-131.

19.

Ferracane JL , Marker VA (1992). Solvent degradation and reduced fracture toughness in aged composites. J Dent Res 71:13-19.

20.

Ferracane JL , Mitchem JC , Condon JR , Todd R. ( 1997). Wear and marginal breakdown of composites with various degrees of cure. J Dent Res 76:1508-1516.

21.

Hirata Y. , Matsushita S. , Nakagama S. , Ishihara Y. , Hori S. ( 1989). Rheological properties and consolidation of the suspension in the alumina powder-silicon nitride whisker system. J Ceram Soc Jpn 97:866-871.

22.

Htang A. , Ohsawa M. , Matsumoto H. (1995). Fatigue resistance of composite restorations: effect of filler content. Dent Mater 11:7-13.

23.

Iwanaga H. , Kawai C. (1998). Tensile strength of silicon nitride whiskers synthesized by reacting amorphous silicon nitride and titanium dioxide. J Am Ceram Soc 81:773-776.

24.

Johnson WW , Dhuru VB , Brantley WA (1993). Composite micro-filler content and its effect on fracture toughness and diametral tensile strength. Dent Mater 9:95-98.

25.

Jordan RE , Suzuki M. (1991). Posterior composite restorations. Where and how they work best. J Am Dent Assoc 122:30-37.

26.

Kelly JR , Tesk JA , Sorensen JA (1995). Failure of all-ceramic fixed partial dentures in vitro and in vivo: analysis and modeling. J Dent Res 74:1253-1258.

27.

Krause WR , Park SH , Straup RA (1989). Mechanical properties of . Bis-GMA resin short glass fiber composites. J Biomed Mater Res 23:1195-1211.

28.

Lawn BR ( 1993). Fracture of brittle solids. Ch. 8. London: Cambridge University Press.

29.

Leinfelder KF (1995). Posterior composite resins: the materials and their clinical performance. J Am Dent Assoc 126:663-676.

30.

Li Y. , Swartz ML , Phillips RW , Moore BK , Roberts TA (1985). Effect of filler content and size on properties of composites. J Dent Res 64:1396-1401.

31.

Loza-Herrero MA , Rueggeberg FA , Caughman WF , Schuster GS , Lefebvre CA , Gardner FM (1998). Effect of heating delay on conversion and strength of a post-cured resin composite. J Dent Res 77:426-431.

32.

Mazer RB , Leinfelder KF , Russell CM (1992). Degradation of microfilled posterior composite . Dent Mater 8:185-189.

33.

Rueggeberg FA , Hashinger DT , Fairhurst CW (1990). Calibration of FTIR conversion analysis of contemporary dental resin composites. Dent Mater 6:241-249.

34.

Sakaguchi RL , Cross M. , Douglas WH (1992). A simple model of crack propagation in dental restorations. Dent Mater 8 :131-136.

35.

St. Germain H. , Swartz ML , Phillips RW , Moore BK , Roberts TA (1985). Properties of microfilled composite resins as influenced by filler content. J Dent Res 64:155-160.

36.

Thompson JY , Anusavice KJ , Naman A. , Morris HF (1994). Fracture surface characterization of clinically failed all-ceramic crowns. J Dent Res 73:1824-1832.

37.

Tominaga I. , Sasaki T. (1987). Iron type golf club head. US patent 4,687,205.

38.

Wilder AD Jr , Bayne SC , Heymann HO (1996). Long-term clinical performance of direct posterior composites. Acad Dent Mater Trans 9:151-169.

39.

Willems G. , Lambrechts P. , Braem M. , Celis JP , Vanherle G. (1992). A classification of dental composites according to their morphological and mechanical characteristics. Dent Mater 8 :310-319.

40.

Wolf WD , Francis LF , Lin C. , Douglas WH (1993). Melt infiltration processing and fracture toughness of alumina glass dental composites. J Am Ceram Soc 76:2691-2694.

41.

Xu Hhk , Ostertag CP , Braun LM , Lloyd IK (1994). Short-crack mechanical properties and failure mechanisms of Si3N4matrix/SiC-fiber composites. J Am Ceram Soc 77:1889-1896.

42.

Xu Hhk , Jahanmir S. , Ives LK , Job LS , Ritchie KT (1996). Short-crack toughness and abrasive machining of silicon nitride. J Am Ceram Soc 79:3055-3064.

43.

Xu Hhk , Smith DT , Jahanmir S. , Romberg E. , Kelly JR , Thompson VP , et al. (1998). Indentation damage and mechanical properties of human enamel and dentin. J Dent Res 77:472-480.

44.

Xu Hhk , Martin TA , Eichmiller FC , Antonucci JM (1999). Ceramic whisker reinforcement of dental composite resins. J Dent Res 78:706-712.