Comparative SEM and TEM Examination of the Ultrastructure of the Resin-Dentin Interdiffusion Zone

Abstract

The resin-dentin interdiffusion zone produced by a dentin-adhesive system that removes the smear layer and concurrently decalcifies superficial dentin was morphologically examined by both scanning and transmission electron microscopy. Cross-sectioned resin-bonded dentin discs were etched with an argon-ion beam to make the resin-dentin interface observable by SEM. For the TEM examination, the sections were partly decalcified by an aqueous EDTA solution to facilitate ultramicrotomy and to disclose the ultrastructure of the interdiffusion zone. Both SEM and TEM confirmed the presence of the resin-dentin interdiffusion zone as the junction between the deep unaltered dentin structure and the restorative resin. Within the interdiffusion zone, three sublayers with characteristic ultrastructure and staining were identified by TEM. An upper diffuse black layer contained few structural features. Underneath, partially-altered collagen fibrils were closely packed, mostly running parallel with the interface and perpendicular to the dentinal tubules. Their outline was electron-dense, forming tunnel-like structures. At the base of the upper layer, several stained projections were found to bulge out into the underlying collagen network and appeared to be confined by obstructive, parallel-running collagen fibrils. Finally, the third dense layer, containing hydroxyapatite crystals, demarcated the superficially demineralized dentin layer from the deeper unaltered dentin. Resin diffusion into the decalcified dentin surface layer was evident, but diminished with depth, presumably reducing deeper resin impregnation into the interfibrillar spaces. The citric acid dentin-pretreatment probably caused denaturation of the superficial collagen fibrils. Its decalcifying effect gradually weakened with depth, leaving behind hydroxyapatite crystals at the base of the interdiffusion zone. These crystals appeared to have been resistant to the EDTA TEM-sample decalcification procedure, which suggests that they were protected by resin encapsulation.

Get full access to this article

View all access options for this article.

References

Braem M. , Lambrechts P. , Van Doren V. , Vanherle G. (1986). The impact of composite structure on its elastic response. J Dent Res 65:648-653.

Chiba M. , Itoh K. , Wakumoto S. (1989). Effect of dentin cleansers on the bonding efficacy of a dentin adhesive. Dent Mater J 8:76-85.

Dickens-Venz S. , Bowen RL , Eichmiller FC (1992). TEM investigation of the dentin-adhesive interface of in vivo and in vitro bonded human teeth (abstract). J Dent Res 71:665.

EickJD ( 1992). Smear layer-materials surface. Proc Finn Dent Soc 88 (1 Suppl):225-242.

Erickson RL (1989). Mechanism and clinical implications of bond formation for two dentin bonding agents. Am J Dent 2:117-123.

Goldberg M. , Septier D. , Escaig-Haye F. (1987). Glycoconjugates in dentinogenesis and dentine . Progr Histochem Cytochem 17 :79-93.

Goret-Nicaise M. , Dhem A. ( 1987). Electron microscopic study of chondroid tissue in the cat mandible. Calcif Tissue Int 40 :219-223.

Hasegawa T. , Manabe A. , Itoh K. , Wakumoto S. (1989). Investigation of self-etching primers on dentin . Dent Mater 5:408-410.

Ikami K. , Fukushima M. , Yoshiba K. , Yamaga M. , Usami Y. , Iwaku M. (1992). Ultrastructural changes of the dentin by surface conditioners. Adhes Dent 10:141-142.

10.

Inagaki A. , Chigira H. , Itoh K. , Wakumoto S. (1989). Effect of self-etching primers on dentin. Dent Mater 5:404-407.

11.

Inokoshi S, Hosoda H, Harniratissai C, ShimidaY, Tatsumi T (1990). A study on the resin-impregnated layer of dentin: Part I. A comparative study on the decalcified and undecalcified sections

12.

and the application of argon ion beam etching to disclose the resin-impregnated layer of dentin. Jpn J Conserv Dent 33 :427-442.

13.

Luft JH ( 1961). Improvements in epoxy resin embedding methods. J Biophys Biochem Cytol 9:409-414.

14.

Nakabayashi N. , Ashizawa M. , Nakamura M. (1992). Identification of a resin-dentin hybrid layer in vital human dentin created in vivo: durable bonding to vital dentin. Quint Int 23:135-141.

15.

Nakabayashi N. , Kojima K. , Masuhara E. (1982). The promotion of adhesion by infiltration of monomers into tooth substrates. J Biomed Mater Res 16:265-273.

16.

Pashley DH (1990). Interactions of dental materials with dentin. Trans Acad Dent Mater 3:55-73.

17.

Pashley DH , Tao L. , Boyd L. , King GE , Horner JA (1988). Scanning electron microscopy of the structure of smear layers in human dentine. Arch Oral Biol 33:265-270.

18.

Prati C. , Biagini G. , Nucci C. , Castaldini C. , Zucchini C. (1990). Effects of chemical pretreatments on dentin bonding . Am J Dent 3 :199-206.

19.

Sugizaki J. (1991). The effect of the various primers on the dentin adhesion of resin composites-SEM and TEM observations of the resin-impregnated layer and adhesion promoting effect of primers. Jpn J Conserv Dent 34:228-265.

20.

Suzuki M. , Kato H. , Wakumoto S. (1991). Vibrational analysis by Raman spectroscopy of the interface between dental adhesive resin and dentin. J Dent Res 70:1092-1097.

21.

Van Meerbeek B. , Inokoshi S. , Braem M. , Lambrechts P. , Vanherle G. (1992). Morphological aspects of the resin-dentin interdiffusion zone with different dentin adhesive systems. J Dent Res 71 :1530-1540.

22.

WangT, Nikaido T. , Nakabayashi N. (1991). Photocure bonding agent containing phosphoric methacrylate. Dent Mater 7:59-62.

23.

Willems G. (1992). Multi-standard criteria for the selection of potential posterior composites (thesis). Leuven (Belgium).