Evaluation of Subsurface Defects Created During the Finishing of Composites

Abstract

The objective ofthis study was to test the hypothesis that a degraded subsurface layer containing microcracks is produced in dental composites as a result of finishing procedures. Various composites in the form of rectangular bars were finished with a 12-fluted carbide bur or a fine diamond within minutes of light-curing, and were subsequently stained with silver nitrate. Microscopic evaluation revealed that significant penetration of stain occurred in the unfinished as well as in the finished surfaces. The extent of dye penetration that could be directly attributed to a damaged layer produced by the finishing procedure was less than 10 μm, being greatest for a microfill (Silux Plus) and a hybrid (P-50) composite. There was no difference between the effects of the finishing instruments. SEM analysis of the subsurface showed an absence of any cracks for the composites. However, occasional disruption of the interface between the pre-polymerized resin fillers and the matrix was apparent for the microfill material. The results showed that only a very limited subsurface damage may be created in certain composites during the initial contouring of a restoration.

Get full access to this article

View all access options for this article.

References

Boghosian AA , Randolph RG , Jekkals VJ (1987). Rotary instrument finishing of microfilled and small-particle hybrid composite resins. J Am Dent Assoc 115:299-301.

Leinfelder KF , Wilder AD , Teixeira LC (1986). Wear rates of posterior composite resins. J Am Dent Assoc 112:829-833.

Lutz F. , Setcos JC , Phillips RW (1983). New finishing instruments for composite resins . J Am Dent Assoc 107:575-580.

Mair LH ( 1989). An investigation into the permeability of composite materials using silver nitrate. Dent Mater 5:109-114.

Mair LH ( 1991). Staining of in vivo subsurface degradation in dental composites by silver nitrate. J Dent Res 70:215-220.

Mathis RS , DeWald JP , Moody CR , Ferracane JL (1990). Marginal leakage in class V composite restorations with glass ionomer liners in vitro. J Prosthet Dent 63:522-524.

Ratanapridakul K. , Leinfelder KF , Thomas J. (1989). Effect of finishing on the in vivo wear rate of a posterior composite resin. J Am Dent Assoc 118:333-335.

Wu W. , Cobb EN ( 1981). A silver staining technique for investigating wear of restorative dental composites. J Biomed Mater Res 15 :343-348.

Wu W. , Toth EE , Moffa JF , Ellison JA (1984). Subsurface damage layer of in vivo worn dental composite restorations. J Dent Res 63 :675-680.