Solvent Degradation and Reduced Fracture Toughness in Aged Composites

Abstract

Quartz- and barium-glass-filled composites aged for more than one year in ethanol experienced a significant reduction in fracture toughness (K_Ic), essentially identical to that experienced after two months of aging. This reduction is mainly attributed to a softening of the resin matrix, but cracking within the resin and at the filler/ matrix interface, as revealed by SEM microscopy, may also have contributed. No significant cracking could be seen in the composites aged in water. Composites post-cured at temperatures approaching their glass-transition temperature also experienced a reduction in K_Ic after alcohol storage. Storage in water for one year had little effect on the K_Ic of composites cured at oral temperatures, but a significant increase was observed for those post-cured at elevated temperatures. This increase is difficult to explain, but appears to involve a filler/matrix interfacial phenomenon, because it was not observed in the unfilled resin. The results of this study demonstrate that an alteration in the fracture resistance and some degradation of the filler/matrix interface, as has been observed clinically, occur after long-term exposure of dental composites to certain solvents used as food-simulating liquids.

Get full access to this article

View all access options for this article.

References

Asmussen, E. (1984): Softening of BisGMA-based Polymers by Ethanol and by Organic Acids of Plaque, Scand J Dent Res 92:257-261.

Broutman, L.J. and Sahu, S. (1971): The Effect of Interfacial Bonding on the Toughness of Glass Filled Polymers, Mater Sci Eng 8:98-107.

Cook, W.D. and Johannson, M. (1987): The Influence of Post curing on the Fracture Properties of Photo-cured Dimethacrylate Based Dental Composite Resin, J Biomed Mater Res 21:979-989.

Crank, J. (1953): ATheoretical Investigation of the Influence of Molecular Relaxation and Internal Stress on Diffusion in Polymers, J Polym Sci 11:151-168.

Ferracane, J.L. (1988): Fracture Toughness of Experimental Dental Composites , Trans 3rd World Biomater Congr XI:252, Abstr. No. 4B1-22.

Ferracane, J.L. and Antonio, R.C. (1988): KIc and Compressive Yield of Aged Experimental Dental Composites, J Dent Res 67:260, Abstr. No. 1183.

Ferracane, J.L. ; Antonio, R.C. ; and Mathis, R.S. (1987a): Effect of Conversion and Solvents on Yield and Fracture of Composites, J Dent Res 66:Abst#1112.

Ferracane, J.L. ; Antonio, R.C. ; and Matsumoto, H. (1987b): Variables Affectingthe KIc of Dental Composites , J Dent Res 66:1140-1145.

Ferracane, J.L. and Greener, E.H. (1986): The Effect of Resin Formulation on the Degree of Conversion and Mechanical Properties of Dental Restorative Resins, J Biomed Mater Res 20:121-131.

10.

Hengchang, X. ; Tong, W. ; Vingerling, R.A. ; and Shiqing, S. (1989): A Study of Surfaces Developed on Composite Resins in vivo During 4-5 Years: Observations by SEM, J Oral Rehabil 16:407-416.

11.

Heymann, H.O. ; Wilder, A.D. ; May, K.N. ; and Leinfelder, K.F. (1986): Two-year Clinical Study of Composite Resins in Posterior Teeth, Dent Mater 2:37-41.

12.

Irwin, G.R. and DeWitt, R. (1983): A Summary of Fracture Mechanics Concepts, J Test Eval, ASTM 11:56-65.

13.

Lambrechts, P. (1983): Basic Properties of Dental Composites and Their Impact on Clinical Performance. Thesis, Lueven.

14.

Lambrechts, P. ; Ameye, C. ; and Vanherle, G. (1982): Conventional and Microfilled Composite Resins. Part II: Chip Fractures, J Prosthet Dent 48:527-538.

15.

Lloyd, C.H. (1984): The KIc of Dental Composites. III. The Effect of Environment Upon the Stress Intensification Factor (KIc) After Extended Storage, J Oral Rehabil 11:393-398.

16.

Lutz, F. ; Phillips, R.W. ; Roulet, J.F. ; and Setcos, J.C. (1984): In vivo and in vitro Wear of Potential Posterior Composites, J Dent Res 63:914-920.

17.

Mair, L.H. (1991): Staining of in vivo Subsurface Degradation in Dental Composites by Silver Nitrate, J Dent Res 70:215-220.

18.

Manson, J.A. and Sperling, L.H. (1976): Polymer Blends and Composites, London: Heydon, pp. 373-430.

19.

McKinney, J.E. and Wu, W. (1985): Chemical Softening and Wear of Dental Composites , J Dent Res 64:1326-1331.

20.

0ysaed, H. and Ruyter, I.E. (1986): Composites for Use in Posterior Teeth: Mechanical Properties Tested Under Dry and Wet Conditions, J Biomed Mater Res 20:261-271.

21.

Pilliar, R.M. ; Smith, D.C. ; and Maric, B. (1986): KIc of Dental Composites Using the Short-rod KIc Test, J Dent Res 65:1308-1314.

22.

Pilliar, R.M. ; Vowles, R. ; and Williams, D.T. (1987): The Effect of Environmental Aging on the KIc of Dental Composites, J Dent Res 66:722-726.

23.

Roulet, J.F. and Walti, C. (1984): Influence of Oral Fluid on Composite Resin and Glass Ionomer Cement, J Prosthet Dent 52:182-189.

24.

Spanoudakis, J. and Young, R.J. (1984): Crack Propagation in a Glass Particle-filled Epoxy Resin. Part 2 - Effect of Particle-Matrix Adhesion, J Mater Sci 19:487-496.

25.

Truong, V.-T. ; Cock, D.J. ; and Padmanathan, N. (1990): Fatigue Crack Propagation in Posterior Dental Composites and Prediction of Clinical Wear, J Appl Biomat 1:21-39.

26.

Truong, V.T. and Tyas, M.J. (1988): Prediction of in vivo Wear in Posterior Composite Resins: a Fracture Mechanics Approach, Dent Mater 4:318-327.

27.

Tyas, M. (1990): Correlation Between Fracture Properties and Clinical Performance of Composite Resins in Class IV Cavities, Aust Dent J 35:46-49.

28.

Van Dijken, J.W.V. ; Horstedt, P. ; and Meurman, J.H. (1985): SEM Study of Surface Characteristics and Marginal Adaptation of Anterior Resin Restorations After 3-4 Years, Scand J Dent Res 93:453-462.

29.

Van Groeningen, G. ; Jongebloed, W. ; and Arends, J. (1986): Composite Degradation in vivo, Dent Mater 2:225-227.

30.

Wu, W. (1982): Wear Mechanisms of Dental Composite Resins. In: Posterior Composites, Proceedings of the International Symposium on Posterior Composite Resins, D. Taylor, Ed., Chapel Hill, NC, pp. 127-146.

31.

Wu, W. and McKinney, J.E. (1982): Influences of Chemicals on Wear of Dental Composites , J Dent Res 61:1180-1183.

32.

Wu, W. ; Toth, E.E. ; and Ellison, J.A. (1984): Subsurface Damage Layer of in vivo Worn Dental Composite Restorations, J Dent Res 63:675-680.