Influence of Initial Flaw Size on Crack Growth in Air-tempered Porcelain

Abstract

Tempering of dental porcelain by forced convective cooling in air has been shown previously to inhibit the sizes of cracks induced in porcelain surfaces. However, the depth of compressive stress that is produced by tempering of feldspathic porcelain has not been determined. It can be assumed that the potential of tempered specimens to inhibit crack formation is reduced as the flaw size exceeds some critical value, since the compressive stress decreases with distance from the surface.

The objective of this study was to test the hypothesis that the effectiveness of tempering stress in porcelain decreases with the increasing size of initial surface flaws. Body porcelain discs, 16 mm in diameter and 2 mm in thickness, were tempered (T) by forced convective cooling in air from an initial temperature of 982°C at a pressure of 0.34 MPa for 90 s. Non-tempered control discs (NT) were slowly cooled by termination of power to the furnace. The half crack-lengths (c) of surface cracks induced by a Vickers microhardness indenter at loads ranging from 2.0 to 39.2 N were determined initially and over a period of 24 h. The initial half crack-lengths, c_o, for the tempered specimens were significantly smaller (p < 0.05) than the corresponding values for the slow-cooled specimens. The mean value of the stress corrosion susceptibility coefficient (n), which is inversely related to the slope of log crack size vs. log time, was only slightly smaller for the NT specimen groups (15.3), compared with the mean value for the T groups (17.1).

These results indicate that tempering stress can effectively inhibit the initial sizes of half-penny cracks with initial depths of at least 100 μm. However, in tempered specimens, the growth rate of initial cracks, which varied in length from 21.4 μm to 76.1 μm, was relatively insensitive to the compressive stress (78.1 MPa) produced by tempering.

Get full access to this article

View all access options for this article.

References

Anstis, G.R. ; Chantikul, P. ; Lawn, B.R. ; and Marshall, D.B. (1981): A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack Measurements, J Am Ceram Soc 64:533-538.

Anusavice, K.J. ; Dehoff, P.H. ; Hojjatie, B. ; and Gray, A. (1989a): Influence of Tempering and Contraction Mismatch on Crack Development in Ceramic Surfaces, J Dent Res 68 :1182-1187.

Anusavice, K.J. ; Hojjatie, B. ; and Gray, A. (1989b): Inhibition of Crack Propagation in Tempered Porcelain Surfaces, J Dent Res 68:324, Abst. No. 1137.

Creyke, W.E.C. (1968): Delayed Fracture of Glazed Porcelain, Trans Br Ceram Soc 67:339-365.

Dehoff, P.H. and Anusavice, K.J. (1989): Tempering Stresses in Feldspathic Porcelain, J Dent Res 68:134-138.

Gardon, R. (1980): Thermal Tempering of Glass. In: Glass Science and Technology, Vol. 5, Elasticity and Strength in Glasses, D.R. Uhlmann and N.J. Kreidl , Eds., New York: Academic Press, pp. 145-216.

Gardon, R. (1988): Tempering Glass with Modulated Cooling Schedules , J Am Ceram Soc 71:876-878.

Gupta, P.K. and Jubb, N.J. (1981): Post-Indentation Slow Growth of Radial Cracks in Glasses, JAm Ceram Soc 64:C112-C114.

Hojjatie, B. ; Anusavice, K.J. ; Lee, R.B. ; and Gray, A. (1989): Influence of Tempering Methods on Transient Incompatibility Stresses in Ceramics, J Dent Res 68:324, Abst. No. 1138.

10.

Lawn, B.R. and Marshall, D.B. (1977): Contact Fracture Resistance of Physically and Chemically Tempered Glass Plates: A Theoretical Model, Phys Chem Glasses 18:7-18.

11.

Marshall, D.B. and Lawn, B.R. (1977): An Indentation Technique for Measuring Stresses in Tempered Glass Surfaces, J Am Ceram Soc 60:86-87.

12.

Marshall, D.B. and Lawn, B.R. (1978a): Letters to the Editor, Measurement of Nonuniform Distribution of Residual Stresses in Tempered Glass Discs, Glass Tech 19:57-58.

13.

Marshall, D.B. and Lawn, B.R. (1978b): Strength Degradation of Thermally Tempered Glass Plates, J Am Ceram Soc 61:21-27.

14.

Narayanaswamy, O.S. and Gardon, R. (1965): Calculation of Residual Stresses in Glass, J Am Ceram Soc 52:554-558.

15.

Wiederhorn, S.M. (1974): Subcritical Crack Growth in Ceramics. In: Fracture Mechanics of Ceramic Materials, Vol. 2, R.C. Bradt , A.G. Evans , D.P.H. Hasselman , and F.F. Lange , Eds., New York: Plenum Press, pp. 613-646.