Preliminary Surface Analysis of Etched,Bleached,and Normal Bovine Enamel

Abstract

X-ray photoelectron spectroscopic (XPS) and secondary ion-mass spectroscopic (SIMS) analyses were performed on unground un-pumiced, unground pumiced, and ground labial enamel surfaces of young bovine incisors exposed to four different treatments: (1) immersion in 35% H₂O₂ for 60 min; (2) immersion in 37% H₃PO₄ for 60 s; (3) immersion in 35% H₂O₂ for 60 min, in distilled water for two min, and in 37% H₃PO₄ for 60 s; (4) immersion in 37% H₃PO₄ for 60 s, in distilled water for two min, and in 35% H₂O₂ for 60 min. Untreated unground un-pumiced, unground pumiced, and ground enamel surfaces, as well as synthetic hydroxyapatite surfaces, served as controls for intra-tooth evaluations of the effects of different treatments. The analyses indicated that exposure to 35% H₂O₂ alone, besides increasing the nitrogen content, produced no other significant change in the elemental composition of any of the enamel surfaces investigated. Exposure to 37% H₃PO₄, however, produced a marked decrease in calcium (Ca) and phosphorus (P) concentrations and an increase in carbon (C) and nitrogen (N) concentrations in unground un-pumiced specimens only, and a decrease in C concentration in ground specimens.

These results suggest that the reported decrease in the adhesive bond strength of resin to 35% H₂O₂-treated enamel is not caused by a change in the elemental composition of treated enamel surfaces. They also suggest that an organic-rich layer, unaffected by acid-etching, may be present on the unground un-pumiced surface of young bovine incisors. This layer can be removed by thorough pumicing or by grinding. An awareness of its presence is important when young bovine teeth are used in a model system for evaluation of resin adhesiveness.

Get full access to this article

View all access options for this article.

References

Eisenmann, D.R. (1985); Enamel Structure, In: Oral Histology, Development, Structure and Function, A.R. Ten Cate , Ed., St. Louis: Mosby , pp. 198-215,

Feinman, R.A. ; Goldstein, R.E. ; and Garber, D.A. (1987): Bleaching Teeth, Chicago: Quintessence Pub. Co.

Glimcher, M.J. ; Friserg, U.A. ; and Levine, P.T. (1964): The Identification and Characterization of a Calcified Layer of Coronal Cementum in Erupted Bovine Teeth, J Ultrastr Res 10:76-88.

Petersson, L.G. ; Lodding, A. ; and Koch, G. (1978): Elemental Microanalysis of Enamel and Dantin by Secondary Ion Mass Spectrometry (SIMS), Swed Dent J 2:41-54.

Smith, D.C. ; Murray, D.G. ; Zuccolin, J.D. ; and Ruse, N.D. (1987): Surface Characteristics of Hydroxyapatite and Adhesive Bonding. l. Surface Characierization, J Adhesion 22:291-312.

Smith, D.C. and Ruse, N.D. (1987): Adhesion to Dentin. Characterization of the Substrate , Trans Soc Biomater, Abst, No, 153,

Titley, K.C. ; Torneck, C.D. ; Smith, D.C. ; and Adibfar, A. (1988): Adhesion of Composite Resin to Bleached and Unbleached Bovine Enamel, J Dent Res 67:1523-1528.