Fracture Mechanics Parameters for Failure Prediction of Composite Resins

Abstract

This study contains the first part of a research project in which the applicability of fracture mechanics parameters to predict failure of a restored tooth was investigated. Fracture mechanics parameters have been used in dental research before, but were restricted to comparative studies between various brands of composites. The critical values of the opening mode stress intensity factor (K_I), its equivalents, the strain energy release rate (G_I), and the J integral (J_I), were measured with single-edge notched-bend (SENB) specimens of dental composite in a three-point bend test. The measured values of K_Ic for Silux (K_Ic = 0.99 ± 0.03 MNm^-3/2) and P-30 (K_Ic = 1.88 ± 0.12 MNm^-3/2), compared with values from the literature, show quantitative agreement. The J integral was computed by means of finite element analysis (FEA) on a two-dimensional model of the SENB specimens.

The critical value of the J integral (measured with SENB specimens, notch depth-to-width ratio (a/W) = 1/2) was used to predict failure of specimens having an arbitrary geometry. In this study, failure was predicted for SENB specimens with notch depth-to-width ratio (a/W) = 1/4 and 3/4. The predicted deflection and load at failure correspond well with the measured deflection and load.

Get full access to this article

View all access options for this article.

References

ASTM Standard E399-78A , Standard Test Method for Plane-Strain Fracture Toughness of Metallic Materials, 1979 Annual Book of ASTM Standards, Part 10, pp. 540-561, Philadelphia, 1979.

ASTM Standard E813-81 , Standard Test Method for JIc, A Measure of Fracture Toughness, 1982 Annual Book of ASTM Standards, Part 10, Metals-Physical. Mechanical Corrosion Testing, pp. 822-840, Philadelphia , 1982.

Bakker, A. (1984): The Three-dimensional J-integral. An investigation into its Use for Post-yield Fracture Safety Assessment, WTHD 167, PhD Thesis , Delft: Delft University of Technology .

Boyer, D.B. ; Chan, K.C. ; and Reinhardt, J.W. (1984): Buildup and Repair of Light-cured Composites: Bond Strength, J Dent Res 63:1241-1244.

Broek, D. (1982): Elementary Engineering Fracture Mechanics, The Hague: Martinus Nijhoff Publishers.

Cruickshanks-Boyd, D.W. and Lock, W.R. (1983): Fracture Toughness of Dental Amalgams, Biomaterials 4:234-242.

De Lorenzi, H.G. (1985): Energy Release Rate Calculations by the Finite Element Method, Eng Fract Mech 21:129-143.

Ewalds, H.L. and Wanhill, R.J.H. (1984): Fracture Mechanics, Delft: Delftse Uitgevers Maatschappij BV.

Finger, W. (1974): Der Elastizitatsmodul von Composite-Füllungsmaterialien , Schweiz Mschr Zahnheilk 84:648-661.

10.

Goldman, M. (1985): Fracture Properties of Composite and Glass Ionomer Dental Restorative Materials, J Biomed Mater Res 19 :771-783.

11.

Hellen, T.K. (1975): On the Method of Virtual Crack Extensions, Int J Numer Meth Eng 9:187-207.

12.

Lloyd, C.H. (1982): The Fracture Toughness of Dental Composites. II. The Environmental and Temperature Dependence of the Stress Intensification Factor (KIc), J Oral Rehabil 9:133-138.

13.

Lloyd, C.H. (1983): Resistance to Fracture in Posterior Composites , Br Dent J 155:411-414.

14.

Lloyd, C.H. (1984): The Fracture Toughness of Dental Composites. III. The Effect of Environment upon the Stress Intensification Factor (KIC) after Extended Storage, J Oral Rehabil 11:393-398.

15.

Lloyd, C.H. and Adamson, M. (1985): The Fracture Toughness (KIC) of Amalgam, J Oral Rehabil 12:59-68.

16.

Lloyd, C.H. and Ianetta, R.V. (1982): The Fracture Toughness of Dental Composites. I. The Development of Strength and Fracture Toughness, J Oral Rehabil 9:55-66.

17.

Lloyd, C.H. and Mitchell, L. (1984): The Fracture Toughness of Tooth Coloured Restorative Materials, J Oral Rehabil 11 :257-272.

18.

Marc (1984): MARC: a General Purpose Finite Element Program, version Kl-3, Palo Alto, CA: MARC Analysis Research Corporation.

19.

Morin, D. ; DE Long, R. ; and Douglas, W.H. (1984): Cusp Reinforcement by the Acid-etch Technique , J Dent Res 63 :1075-1078.

20.

Parks, D.M. (1974): A Stiffness Derivative Finite Element Technique for Determination of Crack Tip Stress Intensity Factors, Int J Fracture 10:487-502.

21.

Reinhardt, K.-J. and Vahl, J. (1983a): Die Bedeutung des Elastizitatsmoduls fur die Randstandigkeit von Kompositen (1. Mitteilung) , Dtsch Zahnärztl Z 39:946-948.

22.

Reinhardt, K.-J. and Vahl, J. (1983b): Beeinflußt Feuchtigkeit die Polymerisationsreaktion von Kompositen? (1. Mitteilung), Dtsch Zahnärztl Z 38:1070-1072.

23.

Rice, J.R. (1968): A Path Independent Integral and the Approximate Analysis of Strain Concentration by Notches and Cracks, J Appl Mech 35:379-386.

24.

Rice, J.R. , Paris, P.C. ; and Merkle, J.G. (1973): Some Further Results of J Integral Analysis and Estimates, ASTM STP 536, pp. 231-245.

25.

Roberts, J.C. ; Powers, J.M. ; and Craig, R.G. (1977): Fracture Toughness of Composite and Unfilled Restorative Resins, J Dent Res 56:748-753.

26.

Srawley, J.E. (1976a): On the Relation of J, to Work done per Unit Uncracked Area: Total or Component due to Crack, Int J Fracture 12:470-474.

27.

Srawley, J.E. (1976b): Wide Range Stress Intensity Factor Expressions for ASTM E-399 Standard Fracture Toughness Specimens, Int J Fracture 12:475-476.

28.

Whiting, R. and Jacobson, P.H. (1980): A Non-destructive Method of Evaluating the Elastic Properties of Anterior Restorative Materials, J Dent Res 59:1978-1984.

29.

Williams, J.G. (1973): Stress Analysis of Polymers, London: Longman Group Limited, p. 129.