Surface Characterization of Amalgams Using X-ray Photoelectron Spectroscopy

Abstract

This study is the first to report on the use of x-ray photoelectron spectroscopy (XPS or ESCA) for studying the surface films (less than 10 nm thick) of aged amalgams. The concentrations and electron binding energies of the elements on the surfaces of four different amalgams aged for 20 min, one day, seven days, and 30 days were determined quantitatively. For comparison, the bulk compositions of the amalgams aged for seven days were also determined after removal of approximately 5 nm of material from the surface by argon-ion-sputtering.

The XPS data revealed that the surface films of aged zinc-containing amalgams were not a simple oxide but were primarily composed of a (hydrated) tin and zinc oxy-hydroxide, whereas, in the zinc-free amalgams, the surface films were primarily a tin oxide. The concentration of mercury in this thin surface film after aging was depleted. This suggests that tin and/or zinc preferentially diffused to the surface and combined with oxygen, forming a surface film and diluting the mercury concentration in the surface. Another probable explanation for the depleted mercury is that a minimal amount of mercury in the surface film evaporated during the aging.

Get full access to this article

View all access options for this article.

References

Asami, K. (1976): A Precisely Consistent Energy Calibration Method for X-Ray Photoelectron Spectroscopy. J Electron Spectrose 9:469-478.

Asami, K. ; Hashimoto, K. ; and Shimodaira, S. (1977): XPS Determination of Compositions of Alloy Surfaces Surface Oxides on Mechanically Polished Iron-Chromium Alloys, Corros Sci 17:7 0-723.

Ausell R.O.; Dickinson, T. ; Povey, A.F. ; and Sher-Wood, P.M.A. (1977): X-Ray Photoelectron Spectroscopic Studies of Tin Electrodes after Polarization in Sodium Hydroxide Solution, J Electrochem Soc 124:1360-1364.

Averette, D.F. (1982): The Relationship between Corrosion and Mechanical Properties of Dental Amalgam. Ph.D. Dissertation at Georgia Institute of Technology.

Benjamin, D.J. (1984): The Effect of Gases and Vapors on Mercury Evaporation , Mater Sci Bull 19:443-450.

Brundle, C.R. (1974): The Application of Electron Spectroscopy to Surface Studies, J Vac Sci Technol 11:212-224.

de Freitas, J.F. (1979): A Survey of the Elemental Composition of Alloy for Dental Amalgam, Aust Dent J 24:17-25.

Frost, D.C. ; Ishitani, A. ; and McDowell, C.A. (1972): X-Ray Photoelectron Spectroscopy of Copper Compound , Mol Phys 24:861-877.

Fuggle, J.C. and Martensson, N. (1980): Core-Level Binding Energies in Metals, J Electron Spectrosc 21:275-281.

10.

Gaskell, D.R. (1973): Introduction to Metallurgical Thermodynamics, New York: McGraw-Hill Book Co., pp. 254, 269.

11.

Grenga, H.E. ; Garden, J.L. ; Okabe, T. ; and Hochman, R.F. (1975): Auger Analysis of Surface Film of Ag3Sn, J Biomed Mater Res 9:207.

12.

Hanawa, T. ; Matsuda, K. ; Ota, M. ; Shimokobe, H. ; Fer-Racane, J.L. ; Nelson, P. ; and Okabe, T. (1986): Thermal Behavior of Amalgams Under Argon Atmosphere , J Dent Res 65 (SpIss): 192, Abst. No. 208 (AADR).

13.

Hashimoto, K. and Asami, K. (1977): X-Ray Photoelectron Spectroscopy Applied to Analysis of Metal Surfaces, Corros Eng 26:375-387.

14.

Hirokawa, K. and Oku, M. (1977): Application of X-Ray Photoelectron Spectroscopy to Quantitative Analysis without Standards, Z Anal Chem 285:192-198.

15.

Holloway, P.H. (1980): Application of Surface Analysis for Electronic Devices. In: Applied Surface Analysis, J.B. Wheeler , Ed., Philadelphia: American Society for Testing and Materials, pp. 5-23.

16.

Holm, R. and Storp, S. (1976): Surface Analysis of Ag-Sn Alloys by ESCA, J Electron Spectrosc 8:459-468.

17.

Jrgensen, C.K. (1972): Chemical Effects on Inner Shells Studied by Photo-Electron Spectrometry, Theoret Chim Acta 24:241-250.

18.

Kasemo, B. and Lausmaa, J. (1986): Surface Science Aspects of Inorganic Biomaterials , CRC Crit Rev Biocompatibil 2 :335-380.

19.

Larson, P.E. (1974): X-Ray Induced Photoelectron and Auger Spectra of Cu, CuO, Cu2O, and Cu2S Thin Films, J Electron Spectrosc 4:213-218.

20.

Lin, J.-H.C. ; Marshall, G.W. ; and Marshall, S.J. (1983): Corrosion Product Formation Sequence on Cu-Rich Amalgams in Various Solutions, J Biomed Mater Res 17:913-920.

21.

Lumsden, J.B. (1986): X-Ray Photoelectron Spectroscopy. In: Metals Handbook, 9th ed., Vol. 10, Materials Characterization, K. Mills , Ed., Metals Park, OH: American Society for Metals, pp. 568-580.

22.

McIntyre, N.S. (1982): Analysis of Corrosion Films Using XPS, Advantages and Limitations. In: Applied Electron Spectroscopy for Chemical Analysis, H. Windawi , Ed., New York: John Wiley & Sons, Inc., pp. 89-103.

23.

Sarkar, N.K. and Eyer, C. (1982): Corrosion of Zinc in Dental Amalgams, IADR Prog and Abst 61: No. 446.

24.

Schon, G. (1973): ESCA Studies of Cu, Cu2O and CuO, Surf Sci 35:96-108.

25.

Scofield, J.H. (1976): Hartee-Slater Subshell Photoionization Cross-Sections at 1254 and 1487eV, J Electron Spectrosc 8:129-137.

26.

Takahashi, H. and Nagayama, M. (1985): Surface Films Formed on Aluminum by Different Pretreatments, I. XPS Analysis of Thickness and Chemical Composition, Kinzoku-Hyomen-Gijutsu 36:96-103.

27.

Tsutsumi, S. ; Nakamura, M. ; Schiller, T.L. ; Ferra-Cane, J. ; and Okabe, T. (1985): Thermal Analysis of Amalgams, J Dent Res 64 (Sp Iss): 181, Abst. No. 59.

28.

Vulli, M. and Starke, K. (1977): Experimental Determination of the Analyser Brightness of a Photoelectron Spectrometer, J Phys E10:158-160.

29.

Wagner, C.D. (1975): Chemical Shifts of Auger Lines and Auger Parameter , Faraday Discuss No. 60:291-318.

30.

Wagner, C.D. and Bileon, D. (1973): X-Ray Excited Auger and Photoelectron Spectra of Partially Oxidized Magnesium Surfaces, The Observations of Abnormal Chemical Shifts, Surf Sci 35 :82-95.

31.

Yoshida, R. and Ide, M. (1976): On Dispersed-Strengthened Amalgams, J Dent Eng (DE) 37:30-35.

32.

Zatko, D.A. and Prather, J.W. (1973): Photoelectron Spectroscopy Verification of Highly Charged Silver Ions in the Ethylenebis (Biguanide)-Silver(III) Complex Ion , J Electron Spectrosc 2:191-197.