An Investigation into the Fracture Behavior of a Particulate-filled bis-GMA Resin

Abstract

Dental composites are being increasingly used to restore occlusal surfaces of posterior teeth. If these restorations are not to fracture in service, an understanding of their fracture behavior is essential. The fracture parameter used is the stress-intensity factor at crack instability (K_IC). This has been calculated by means of the double-torsion test in a mechanical testing machine.

The fracture behavior of the composite was studied by varying: the amount of filler (7%, 15%, 26%, and 41% by volume); the surface treatment of the filler (coated or uncoated); the environment (air and water); and the cross-head rate (0.05, 0.5, 5, and 50 mmlmin).

Fracture was found to occur in either a continuous (stable) or stick-slip (unstable) manner. The stick-slip behavior was due to blunting of the crack tip, which was controlled by the yield behavior. When there was no significant blunting, continuous crack growth occurred. An unique relationship was found to exist between the yield stress and the stress-intensity factor for all conditions of testing.

Get full access to this article

View all access options for this article.

References

Beachem, C.D. ; Kies, J.A. ; and Brown, B.F. (1971): A Constant K Specimen for Stress Corrosion Cracking Tests, Mater Res and Stand 11:30.

Bowden, P.B. and Jukes, J.A. (1972): The Plastic Flow of Iso-trophic Polymers, J Mater Sci 7:52-63.

Bowen, R.L. and Cleek, G.W. (1969): X-ray Opaque Reinforcing Fillers for Composite Materials, J Dent Res 48:79-82.

Broutman, L.J. and Sahu, S. (1971): The Effect of Interfacial Bonding on the Toughness of Glass Filled Polymers, Mater Sci Eng 8:98-107.

Brown, S.K. (1980): Mechanics of Fracture in Filled Thermosetting Resins. Br Polymer J 12:24-30.

Evans, A.G. (1972): The Strength of Brittle Materials Containing Second Phase Dispersions, Phil Mag 26:1327-1344.

Green, D.J. ; Nicholson, P.S. ; and Embury, J.D. (1979): Fracture of a Brittle Particulate Composite - Part 1, J Mater Sci 14:1413-1420.

International Standards Organisation (1978 ): Resin Based Dental Filling Materials, Document No. IS040409 .

Irwin, G.R. (1957): Analysis of Stresses and Strains Near the End of a Crack Traversing a Plate, J Appl Mech 24:361-364.

10.

Kies, J.A. and Clark, A.B.J. (1969): Fracture Propagation Rates and Times to Fail Following Proof Stress in Bulk Glass. In: Proceedings of the Second International Conference on Fracture, Paper 42 (Session III).

11.

Kinloch, A.J. and Williams, J.G. (1980): Crack Blunting Mechanisms in Polymers, J Mater Sci 15:987-996.

12.

Koblitz, F.F. ; Luna, V.R. ; Glenn, J.F. ; DE Vries, K.L. ; and Draughn, R.A. (1979): Fracture Toughness Testing of Dental Biomaterials , Polymer Eng & Sci 19:607-608.

13.

Lange, F.F. (1970): Interaction of Crack Growth with Second Phase Dispersion, Phil Mag 22:983-992.

14.

Lange, F.F. and Radford, K.C. (1971): Fracture Energy of an Epoxy Composite System, J Mater Sci 6:1197-1203.

15.

Lilley, J. (1973): The Fracture of Filled Epoxy Resins, Ph.D. thesis, University of Keele, Great Britain .

16.

Lloyd, C.H. (1983): Resistance to Fracture in Posterior Composites , Br Dent J 155:411-414.

17.

Lloyd, C.H. and Iannetta, R.V. (1982): The Fracture Toughness of Dental Composites, J Oral Rehabil 9:55-66.

18.

Lloyd, C.H. and Mitchell, L. (1984): The Fracture Toughness of Tooth Coloured Restorative Materials, J Oral Rehabil 11 :257-272.

19.

Manson, J.A. and Sperling, L.H. (1976): Polymer Blends and Composites. London: Heyden, pp. 373-430.

20.

Moloney, A.C. ; Kausch, H.H. ; and Stieger, H.R. (1983): The Fracture of Particulate-filled Epoxide Resins - Part 1, J Mater Sci 18:208-216.

21.

Moloney, A.C. ; Kausch, H.H. ; and Stieger, H.R. (1984): The Fracture of Particulate-filled Epoxide Resins - Part 2, J Mater Sci 19:1125-1130.

22.

Roberts, J.H. ; Powers, J.M. ; and Craig, R.G. (1977): Fracture Toughness of Composite and Unfilled Restorative Resins, J Dent Res 56:748-753.

23.

Spanoudakis, J. and Young, R.J. (1984a): Crack Propagation in a Glass Particle-filled Epoxy Resin - Part 1, J Mater Sci 19:473-486.

24.

Spanoudakis, J. and Young, R.J. (1984b): Crack Propagation in a Glass Particle-filled Epoxy Resin - Part 2, J Mater Sci 19:487-496.

25.

Wambach, A. ; Trichke, K. ; and Di Benedetto, A. (1968): Fracture Properties of Glass Filled Polyphenylene Oxide Composites, J Comp Mater 2:266-283.

26.

Yamini, S. and Young, R.J. (1979): Crack Propagation in and Fractography of Epoxy Resins, J Mater Sci 14:1609-1618.

27.

Yamini, S. and Young, R.J. (1980): The Mechanical Properties of Epoxy Resins - Part 2, J Mater Sci 15:1823-1831.

28.

Young, R.J. and Beaumont, P.W.R. (1975): Failure of Brittle Polymers by Slow Crack Growth - Part 2, J Mater Sci 10 :1343-1350.

29.

Young, R.J. and Beaumont, P.W.R. (1977): Failure of Brittle Polymers by Slow Crack Growth - Part 3, J Mater Sci 12 :684-692.