Thermal Diffusivity of Glass-ionomer Cements

Abstract

Thermal diffusivity, a property related to the thermal insulative efficiency of a material, was measured in nine glass-ionomer cements and compared with results from a silicate and a polycarboxylate cement. Each cement was mixed at various powder-liquid ratios (P/L) and moulded into a rectangular prism of approximate dimensions 2 cm cube with a thermocouple embedded in it. The prism was immersed in a constant-temperature bath at 1°C, and the fall in temperature was observed over a period of three min. Except for the initial and later stages, the plot of the logarithmic difference between external and internal temperatures of each block of cement against time showed a straight line in accord with theoretical prediction. From the slope, the thermal diffusivity of the material was calculated. The values for the silicate, polycarboxylate, and glass-ionomer-metal (cermet) showed a marked rise with increasing P/L, whereas at higher P/L, glass ionomer cements showed gradual change, with values being only slightly higher than the thermal diffusivity of dentin. Glass-ionomer cements are good thermal insulators over a wide range of PIL, and close agreement between experimental and theoretical data shows that glass-ionomer cements are homogeneous isotropic materials.

Get full access to this article

View all access options for this article.

References

Bertenshaw, B.W. and Combe, E.C. (1972): Studies on Polycarboxylate and Related Cement. 2. Analysis of Cement Powders, J Dent 1:65-68.

Braden, M. (1964): Heat Conduction in Teeth and the Effect of Lining Materials, J Dent Res 43:315-322.

Braden, M. (1976): Biophysics of the Tooth, Oral Physiol 2 :1-37.

Carslaw, H.S. and Jaeger, J.C. (1959): Conduction of Heat in Solids, 2nd ed., Oxford: Oxford University Press.

Civjan, S. ; Barone, J.J. ; Reinke, P.E. ; and Selting, W.J. (1972): Thermal Properties of Nonmetallic Restorative Materials, J Dent Res 5:1030-1037.

Craig, R.G. (1980): Restorative Dental Materials, 6th ed., St. Louis: C.V. Mosby Co. , p. 54.

McLean, J.W. and Gasser, O. (1985): Glass-cermet Cements, Quintessence Int 16:333-343.

Pearson, G.J. ; Wills, D.J. ; Braden, M. ; and McCabe, J.F. (1980): The Relationship Between the Thermal Properties of Composite Filling Materials, J Dent 8:178-181.

Touloukian, Y.S. ; Powell, R.W. ; Ho, C.Y. ; and Nico-Laou, N. (1973): Thermophysical Properties of Matter, Vol. 10: Thermal Diffusivity. New York: IFI/Plenum.

10.

Watts, D.C. and Smith, R. (1981): Thermal Diffusivity in Finite Cylindrical Specimens of Dental Cements, J Dent Res 60 :1972-1976.

11.

Watts, D.C. and Smith, R. (1984): Thermal Diffusion in Some Polyelectrolyte Dental Cements: The Effect of Powder/Liquid Ratio, J Oral Rehabil 11:285-288.