Influence of Silane Treatment and Filler Fraction on Thermal Expansion of Composite Resins

Abstract

The coefficient of thermal expansion of experimental composite materials containing either silane-treated or untreated fillers in a triethylene glycol dimethacrylate (TEGDMA) matrix was investigated. The results show that an inverse linear relationship existed between volume fraction filler and coefficient of thermal expansion. No differences were seen between silane-treated and untreated composites, while it was found that repeated heating (aging) caused the thermal expansion to decrease for all material combinations.

Reduction in the coefficient of thermal expansion with increased filler fraction of unbonded filler indicates that the polymerization shrinkage of the matrix induces hoop stresses around the fillers.

By use of a simplified theoretical model (Appendix), these stresses could be estimated. These estimates revealed that the induced stresses were remarkably high, and that increased filler fraction increased the tensile stress level surrounding the filler particles. Since these tensile stresses could facilitate crazing and crack growth in the matrix, these estimates may explain why filled resins containing low fractions of microfilled particles seem to possess remarkably good clinical wear resistance when compared with composites containing higher filler concentrations, at least during the first years in service.

Get full access to this article

View all access options for this article.

References

Bowen, R.L. (1964): Effect of Particle Shape and Size Distribution in a Reinforced Polymer, JADA 69:481-495.

Buonocore, M.G. (1955): A Simple Method of Increasing the Adhesion of Acrylic Filling Materials to Enamel Surfaces, J Dent Res 34:849-853.

Christensen, R.P. and Christensen, G.J. (1982): In vivo Comparison of a Microfilled and a Composite Resin: a Three Year Report, J Prosthet Dent 48:657-663.

Craig, R.G. and Powers, J.M. (1976): Wear of Dental Tissues and Materials, Int Dent J 26:121-133.

Dennison, J.B. (1982): Status Report on Microfilled Composite Restorative Resins, JADA 105:488-492.

Draughn, R.A. (1979): Compressive Fatigue Limits of Composite Restorative Materials, J Dent Res 58:1093-1096.

Fahmy, A.A. and Ragai, A.N. (1970): Thermal-expansion of Two-phase Solids, J Appl Phys 41:5108-5111.

Goldberg, J. ; Tanzer, J. ; Munster, E. ; Amara, J. ; Thal, F. ; and Birkhed, D. (1981): Cross-sectional Clinical Evaluation of Recurrent Enamel Caries, Restoration of Marginal Integrity, and Oral Hygiene Status , JADA 102:635-641.

Hashin, Z. (1962): The Elastic Module of Heterogeneous Materials , J Appl Mech 29:143-150.

10.

Hembree, J.H. (1983): Marginal Leakage of Microfilled Composite Resin Restorations, J Prosthet Dent 50:632-635.

11.

Hult, J. (1968): Hållfasthetslara, 2nd ed. Uppsala, Sweden: Almquist & Wiksells Boktryckeri A.B., pp. 307-308.

12.

Jacobsen, P.H. (1981): The Current Status of Composite Restorative Materials , Br Dent J 150:15-18.

13.

Jrgensen, K.D. ; Hrsted, P. ; Janum, 0.; Krogh, J. ; and Schultz, J. (1979): Abrasion of Class I Restorative Resins, Scand J Dent Res 87:140-145.

14.

Knock, F.E. and Glenn, J.F. : Dental Material and Method. U.S. Patent No. 2558139, June, 1951.

15.

Livaditis, G.J. (1980): Cast Metal Resin-bonded Retainers for Posterior Teeth, JADA 101:926-929.

16.

Olgart, L. ; Brännström, M. ; and Johnson, G. (1974): Invasion of Bacteria into Dentinal Tubules. Experiments in vivo and in vitro, Acta Odontol Scand 32:61-70.

17.

Paffenbarger, G.C. ; Nelsen, R.J. ; and Sweeney, W.T. (1953): Direct and Indirect Filling Resins: A Review of Some Physical and Chemical Properties, JADA 47:516-524.

18.

Parks, V.J. and Durelli, A.J. (1965): Photoelastic Analysis of Plates Subjected to Restrained Shrinkage, J Appl Mech 87 :504-510.

19.

Smith, D.C. (1982): A Milestone in Dentistry, Oper Dent 7:14-25. SÖDERHOLM, K.-J. (1982): Relationship Between Compressive Yield Strength and Filler Fractions of PMMA Composites, Acta Odontol Scand 40:145-150.

20.

Soderholm, K.-J. (1983): Leaking of Fillers in Dental Composites, J Dent Res 62:126-130.

21.

Soderholm, K.-J. (1984): Unpublished data.

22.

Soderholm, K.-J. and Calvert, P.D. (1983): Effects of Water on Glass-Filled Methacrylate Resins, J Mater Sci 18:2957-2962. Tummala, R.R. and Friedberg, A.L. (1970): Thermal Expansion of Composite Materials, J Appl Phys 41:5104-5107.