Tarnish and Corrosion of a Commercial Dental Ag-Pd-Cu-Au Casting Alloy

Abstract

The correlation between microstructure, tarnish, and corrosion behavior of a commercial dental Ag-Pd-Cu-Au casting alloy after various heat treatments was studied. The attacked structural components were identified by comparing SEM micrographs with light optical micrographs taken after exposure of the alloy to a 2% Na2S solution and after dynamic polarization in de-aerated artificial saliva. The characteristic dynamic polarization curves for the alloy after the heat treatments were established. The results were verified by analogous testing of two experimental alloys with compositions similar to those of the analyzed components in the commercial alloy annealed at 600°C for seven wk.

The matrix of the commercial alloy was decomposed, according to the heat treatments, into varying proportions of a tarnish- and corrosion-resistant Cu- and Pd-rich component (A) and a non-resistant Ag-rich component (B). The presence of A considerably increased the tarnish rate of B, due to galvanic coupling. Age-hardening of the alloy increased the proportion of the tarnish- and corrosion-prone component B.

Get full access to this article

View all access options for this article.

References

Gerischer, H. and Rickert, H. : Über das electrochemische Verhalten von Kupfer-Gold-Legierungen und den Mechanismus der Spannungskorrosion, Z Metallkd 46:681-689, 1955.

German, R.M. : The Role of Microstructure in the Tarnish of Low-Gold Alloys, Metallography 14:253-266,1981.

German, R.M. ; Wright, D.C. ; and Gallant, R.F. : In vitro Tarnish Measurements on Fixed Prosthodontic Alloys, J Prosthet Dent 47:399-406, 1982.

Gnieweh, J. ; Pezy, J. ; Baker, B.G. ; and Bockris, J.O.M. : The Effect of Noble Metal Additions upon the Corrosion of Copper: An Auger-Spectroscopic Study, J Electrochem Soc 125:17-23, 1978.

Holland, R.I. : Galvanic Currents between Gold and Amalgam, Scand J Dent Res 88:269-272, 1980.

Ishizaki, N. : Corrosion Resistance of Ag-Pd Alloy System in Artificial Saliva: An Electrochemical Study, J Osaka Dent Univ 3:121-133, 1969.

Lang, B.R. ; Bernier, S.H. ; Giday, Z. ; and Asgar, K. : Tarnish and Corrosion of Noble Metal Alloys, J Prosthet Dent 48 :245-252, 1982.

Laub, L.W. and Stanford, J.W. : Tarnish and Corrosion Behavior of Dental Gold Alloys, Gold Bull 14:13-18, 1981.

Niemi, L. and Her, H. : The Structure of a Commercial Dental Ag-Pd-Cu-Au Casting Alloy, J Dent Res 63:149-154, 1984.

10.

Pickering, H.W. and Byrne, P.J. : On Preferential Anodic Dissolution of Alloys in the Low-Current Region and the Nature of the Critical Potential, J Electrochem Soc 118:209-215, 1971.

11.

Sarkar, N.K. ; Fuys, R.A., Jr. ,; and Stanford, J.W. : The Chloride Corrosion of Low-Gold Casting Alloys, JDent Res 58: 568-575,1979.

12.

Sastri, S. ; Vaidyanathan, T.K. ; and Mukherjee, K. : Potentiodynamic Polarization Analysis of Silver-Palladium Alloys in Chloride Solutions, Metal Trans A13A:313-317, 1982.

13.

Tuccillo, J.J. and Nielsen, J.P. : Observations of Onset of Sulfide Tarnish on Gold-Base Alloys, J Prosthet Dent 25 :629-637,1971.

14.

Tuccillo, J.J. and Nielsen, J.P. : Microprobe Analysis of an in vivo Discoloration, J Prosthet Dent 31:285-289, 1974.

15.

Vaidyanathan, T.K. and Prasad, A. : In vitro Corrosion and Tarnish Analysis of the Ag-Pd Binary System , J Dent Res 60: 707-715,1981.