Tarnishing and Structures of Some Annealed Dental Low-gold Alloys

Abstract

Tarnishing of low-gold alloys in a Tuccillo-Nielsen test with 2% Na2S is avoided when a single-phase structure is present as compared with multi-phase structures, unless the Ag content of the single-phased alloy is high. In all multi-phase structures, only the Ag-rich phase is attacked. The possibility of annealing alloys to a single-phase structure decreases with the reduction of Au content and with increasing amounts of Pd and Zn, which tend to follow the Cu-rich phase. In static polarization testing of single-phase materials in weak sulphide solutions, the Ag-rich alloys display considerably higher anodic current densities (5-10 μA/cm²) than do the Cu-rich low-gold and high-gold alloys (1 μA/cm²). No significant differences between the alloys were observed with respect to cathodic currents.

Get full access to this article

View all access options for this article.

References

Barett, C.S. and Massalski, T.B. : Structure of Metals, 3rd ed., New York: McGraw-Hill, 1966, p. 627.

German, R.M. ; Guzowski, M.M. ; and Wright, D.C. : Color and Color Stability as Alloy Design Criteria, J Metals 32: 20-27 1971.

German, R.M. ; Wright, D.C. ; and Gallant, R.F. : In vitro Tarnish Measurements on Fixed Prosthodontic Alloys, J Prosthet Dent 47: 399-406, 1982.

Hansen, M. and Anderko, K. : Constitution of Binary Alloys, 2nd ed., New York: McGraw-Hill, 1958, pp. 5, 18-19.

Her, H. and Jrgensen, R.B. : Tarnishing of a Low-gold Dental Alloy in Different Structural States , J Dent Res 62: 371-376,1983.

Her, H. ; Jrgensen, R.B. ; and Srbrden, E. : A Low-gold Dental Alloy: Structure and Segregations, J Dent Res 61: 1292-1298,1982.

Hultquist, G. and Her, H. : Surface Enoblement by Dissolution of Cu, Ag and Zn from Single Phase Gold Alloys, to be published.

Ingersoll, C. : A Sulphide Tarnish Test for Dental Casting Alloys, IADR Progr & Abst 56: No. 467, 1975.

Lang, B.R. ; Bernier, S.H. ; Giday, Z. ; and Asgar, K. : Tarnish and Corrosion of Noble Metal Alloys, J Prosthet Dent 48: 245-252,1982.

10.

Massalski, T.B. : Structure of Solid Solutions. In: Physical Metallurgy , R.W. Rahn , Ed., Amsterdam: North-Holland Publishing Company, 1979, p. 164.

11.

McMullin, J.G. and Norton, J.T. : On the Structure of Gold-Silver-Copper Alloys, Trans AIME 185: 46-48, 1949.

12.

Ntukogu, A.O. : Solid Solution Miscibility Gap in the Ternary System Cu-Ag-Au. PhD. thesis , Polytechnic Inst. of New York , 1979.

13.

Popp, W. ; Kaiser, H. ; Kaesche, H. ; Bramer, W. ; and Spern-Er, F. : Electro-chemical Behaviour of Noble Metal Dental

14.

Alloys in Different Artificial Saliva Solutions, Proc 8th Int Congr on Metallic Corrosion, Frankfurt, 1981, pp. 76-81. Tuccillo, J.J. and Nielsen, J.P. : Observations of Onset of Sulphide Tarnish on Gold-Based Alloy, J Prosthet Dent 25: 629-637, 1971.