The Initial Gap Around Large Composite Restorations in vitro: The Effect of Etching Enamel Walls

Abstract

Composite resin restorations in cavities are generally associated with the development of a contraction gap during the first minutes after insertion. Enamel-Bond-Concise composite restorations were placed on both approximal sides of extracted pre-molars. The cervical walls of all cavities extended beyond the enamel-cement junction. The enamel walls of one of the cavities in each tooth were acid-etched. The contraction gap was kept air-filled and open at the margin through the use of a special technique. Enamel Bond resin with a fluorescent additive was applied to occlusal and cervical margins of the restorations.

The fluorescent resin was "passively" drawn into the gap. In unetched cavities, resin penetrated both cervical and occlusal gaps and some areas of the gap at the axial wall. In cavities with etched enamel, the penetration occurred only at the cervical wall. The distance of penetration from the cervical margin varied from 1 to 6.5 mm, and the width of the contraction gap filled with the fluorescent resin varied from 3.5 to 16 μm.

Comparison of the width of the gap at the cervical wall in etched and unetched cavities suggested larger gaps for etched cavities. The method used offers a new technique for the measurement of the contraction gaps around composite resin restorations.

Get full access to this article

View all access options for this article.

References

Bergenholtz, G. ; Cox, C.F. ; Loesche, W.J. ; and Syed, S.A. : Bacterial Leakage around Dental Restorations: Its Effect on Dental Pulp, J Oral Pathol 11:439-450, 1982.

Bergvall, O. and Brannstrom, M. : Measurements of the Space between Composite Resin Fillings and the Cavity Walls, Swed Dent J 64 :217-226, 1971.

Bowen, R.L. ; Cobb, E.N. : and RAPSON, J.E.: Adhesive Bonding of Various Materials to Hard Tooth Tissues: Improvement in Bond Strength to Dentin, J Dent Res 61:1070-1076, 1982.

Brannstrom, M. ; Nordenvall, K.J. ; and Glantz, P.O. : The Effect of EDTA-containing Surface-active Solutions on the Morphology of Prepared Dentin, J Dent Res 59:1127-1131, 1980.

Brannstrom, M. ; Malmgren, 0. ; and Nordenvall, K.J. : Etching of Young Permanent Teeth with an Acid Gel, Am J Orthod 82:379-383, 1982.

Brannstrom, M. : Dentin and Pulp in Restorative Dentistry, London : Wolfe Med Publ Ltd., 1982, pp. 67-108.

Crim, G.A. and Mattingly, S.L. : Evaluation of Two Methods for Assessing Marginal Leakage, J Prosthet Dent 45:160-163, 1981.

Fitzgerald, M. ; Cox, C.F. ; Bergenholtz, G. ; Syed, D.R. ; Heys, D.R. ; and Baker, J.A. : Observations of Ca(OH)2 Bases After One Year Placement in Monkeys , AADR Progr & Abst 62:No. 733, 1983.

Hansen, E.K. : Visible Light-cured Composite Resins: Polymerization Contraction, Contraction Pattern and Hygroscopic Expansion, Scand J Dent Res 90:329-335, 1982.

10.

Nordenvall, K.J. and Brannstrom, M. : In vivo Resin Impregnation of Dentinal Tubules, J Prosthet Dent 44:630-637, 1980.

11.

Prevost, A.P. ; Fuller, J.L. ; and Peterson, L.C. : The Use of an Intermediate Resin in the Acid-etch Procedure: Retentive Strength, Microleakage and Failure Mode Analysis, J Dent Res 61 :412418, 1982.

12.

Prosser, H.J. ; Groffman, D.M. ; and Wilson, A.D. : The Effect of Composition on the Erosion Properties of Calcium Hydroxide Cements , J Dent Res 61:1431-1435, 1982 .

13.

Torstenson, B. ; Nordenvall, K.J. ; and Brannstrom, M. : Pulpal Reaction and Microorganisms under Clearfil Composite Resin in Deep Cavities with Acid Etched Dentin, Swed Dent J 6:167-176, 1982.