A compaction-agglomeration fabrication technique has been developed to produce polymethylmethacrylate dental implants having a porous coating on the root portion. This process allows control of pore structure enabling ingrowth of either bone or fibrous tissue. The relationships between mechanical properties and pore microstructure have been determined for materials produced by this process. The mechanical properties of the porous coating can be estimated from these relationships.
Klawitter, J.J. , and Hulbert, S.F. : Application of Porous Ceramics for the Attachment of Load Bearing Internal Orthopedic Applications, J Biomed Mater Res Symposium, No. 2 (Part 1): 161-229, 1971.
3.
Klawitter, J.J. ; Sauer, B.W.; Bagwell , J.G.; Weinstein, A.M.; Greer, K.G.; and Hulbert, S.F.: Characterization of Tissue Growth into Porous Biomaterials, Technical Report No. 6, Office of Naval Research Contract No. N00014-71-A-0339-0001 (Project No. NR 032-529), 1974.
4.
Taylor, P.F. , and Smith, F.B.: Porous Methylmethacrylate as an Implant Material, J Biomed Mater Res6:467, 1972.
5.
Ryshkewitch, E.: Compressive Strength of Porous Sintered Alumina and Zirconia, J Am Ceramic Soc36(2) :65, 1953.
6.
Rootare, H.M. , and Prenzlow, C.F.: Surface Areas from Mercury Porosimeter Measurements, J Phys Chem71:2733, 1967.