Abstract
To develop dental restorative materials with enamel-like structures, ultralong hydroxyapatite (HA) nanowires were synthesized by a hydrothermal method, followed by functionalization with 3-methacryloxypropyltrimethoxysilane (KH-570). The mixture of HA nanowires, KH-570, and light initiator was stirred and centrifuged. The precipitate was vacuum filtered to remove excessive KH-570 and then pressured under cold isostatic pressing (10 MPa × 24 h). Finally, the block was polymerized by lighting. Scanning electron microscopy and transmission electron microscopy showed that HA nanowires with aspect ratios >1,000 were assembled into enamel rod–like microstructures and evenly dispersed in the polymerized KH-570 silane matrix to form enamel-like structures. Thermogravimetric analysis demonstrated that the content of HA nanowires reached 72 wt% in the composite. The enamel-like composite showed a similar hardness, frictional property, and acid-etching property to those of enamel and a comparable or even better diametral tensile strength and compressive strength than some commercial composite resins in mechanical tests in vitro. In addition, the enamel-like composite had good cytocompatibility. Such enamel-like composites may have the potential to be used in biomimetic tooth restorations in the future.
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.