One failure mode of all-ceramic restorations is radial cracking at the cementation surface, from occlusally induced flexure of the stiffer ceramic layer(s) on the softer dentin underlayer. We hypothesize that such failure may be substantially mitigated by an appropriate grading of elastic modulus through the ceramic thickness. In this study, we fabricated graded structures by infiltrating glass into zirconia plates, with resulting diminished modulus in the outer surfaces. The plates were then bonded to a polymeric base and subjected to flexure by contact loading until fracture. Comparison of infiltrated specimens with non-infiltrated controls showed a significant increase in the fracture loads, by a factor of nearly 2. Finite element analysis revealed the cause of increase in the load-bearing capacity to be diminished tensile stresses within the lower-modulus graded zone, corresponding to an increase in material strength. The results confirmed that suitably graded structures can be highly beneficial in the design of next-generation all-ceramic restorations.
Get full access to this article
View all access options for this article.
References
1.
Anstis GR, Chantikul P, Marshall DB, Lawn BR (1981). A critical evaluation of indentation techniques for measuring fracture toughness: I. Direct crack measurements. J Am Ceram Soc64:533–538.
2.
Anusavice KJ, Tsai YL (1997). Stress distribution in ceramic crown forms as a function of thickness, elastic modulus, and supporting substrate. In: Proceedings of the Sixteenth Southern Biomedical Engineering Conference. Bumgardner JD, Puckett AD, editors. Biloxi, MS: IEEE, pp. 264–267.
3.
Chai H, Lawn BR, Wuttiphan S (1999). Fracture modes in brittle coatings with large interlayer modulus mismatch. J Mater Res14:3805–3817.
4.
Deng Y, Lawn BR, Lloyd IK (2002). Characterization of damage modes in dental ceramic bilayer structures. J Biomed Mater Res B63:137–145.
5.
Fradeani M, Aquilano A (1997). Clinical experience with Empress crowns. Int J Prosthodont10:241–247.
6.
Fradeani M, Redemagni M (2002). An 11-year clinical evaluation of leucite-reinforced glass-ceramic crowns: a retrospective study. Quintessence Int33:503–510.
7.
Huang M, Wang R, Thompson V, Rekow D, Soboyejo WO (2007). Bioinspired design of dental multilayers. J Mater Sci Mater Med18: 57–64.
8.
Jitcharoen J, Padture NP, Giannakopoulos AE, Suresh S (1998). Hertzian-crack suppression in ceramics with elastic-modulus-graded surfaces. J Am Ceram Soc81:2301–2308.
9.
Kelly JR (1997). Ceramics in restorative and prosthetic dentistry. Ann Rev Mater Sci27:443–468.
10.
Kelly JR (1999). Clinically relevant approach to failure testing of all-ceramic restorations. J Prosthet Dent81:652–661.
11.
Kelly JR (2004). Dental ceramics: current thinking and trends. Dent Clin North Am48:513–530.
12.
Kelsey WP, Cavel T, Blankenau RJ, Barkmeier WW, Wilwerding TM, Latta MA (1995). 4-year clinical study of castable ceramic crowns. Am J Dent8:259–262.
13.
Lawn BR (1993). Fracture of brittle solids. Cambridge: Cambridge University Press.
14.
Lawn BR, Bhowmick S, Bush MB, Qasim T, Rekow ED, Zhang Y (2007). Failure modes in ceramic-based layer structures: a basis for materials design of dental crowns. J Am Ceram Soc90:1671–1683.
15.
Lee JJ-W, Kwon J-Y, Lloyd IK, Bhowmick S, Rekow ED, Lawn BR (2008). Veneer vs. core failure in adhesively bonded all-ceramic crown layers. J Dent Res87:363–366.
16.
Malament KA, Socransky SS (1999a). Survival of Dicor glass-ceramic dental restorations over 14 years: I. Survival of Dicor complete coverage restorations and effect of internal surface acid etching, tooth position, gender and age. J Prosthet Dent81:23–32.
17.
Malament KA, Socransky SS (1999b). Survival of Dicor glass-ceramic dental restorations over 14 years: II. Effect of thickness of Dicor material and design of tooth preparation. J Prosthet Dent81:662–667.
18.
Malament KA, Socransky SS (2001). Survival of Dicor glass-ceramic dental restorations over 16 years: Part III: Effect of luting agent and tooth or tooth-substitute core structure. J Prosthet Dent86:511–519.
19.
McLaren EA, White SN (2000). Survival of In-Ceram crowns in a private practice: a prospective clinical trial. J Prosthet Dent83:216–222.
20.
McLean JW (1979). The science and art of dental ceramics. Vol. 1: The nature of dental ceramics and their clinical use. Chicago: Quintessence.
21.
Oliver WC, Pharr GM (1992). An improved technique for determining hardness and elastic-modulus using load and displacement sensing indentation experiments. J Mater Res7:1564–1583.
22.
Rekow D, Thompson VP (2007). Engineering long-term clinical success of advanced ceramic prostheses. J Mater Sci Mater Med18:47–56.
23.
Rudas M, Qasim T, Bush MB, Lawn BR (2005). Failure of curved brittle layer systems from radial cracking in concentrated loading. J Mater Res20:2812–2819.
24.
Scherrer SS, de Rijk WG (1993). The fracture resistance of all-ceramic crowns on supporting structures with different elastic moduli. Int J Prosthodont6:462–467.
25.
Sjogren G, Lantto R, Granberg A, Sundstrom BO, Tillberg A (1999a). Clinical examination of leucite-reinforced glass-ceramic crowns (Empress) in general practice: a retrospective study. Int J Prosthodont12:122–128.
26.
Sjogren G, Lantto R, Tillberg A (1999b). Clinical evaluation of all-ceramic crowns (Dicor) in general practice. J Prosthet Dent81:277–284.
27.
Zhang Y, Kim JW (2009). Graded structures for damage resistant and aesthetic all-ceramic restorations. Dent Mater25:781–790.
28.
Zhang Y, Ma L (2009). Optimization of ceramic strength using elastic gradients. Acta Mater57:2721–2729.