Concerns of Hydrothermal Degradation in CAD/CAM Zirconia

Abstract

Zirconia-based restorations are widely used in prosthetic dentistry; however, their susceptibility to hydrothermal degradation remains elusive. We hypothesized that CAD/CAM machining and subsequent surface treatments, i.e., grinding and/or grit-blasting, have marked effects on the hydrothermal degradation behavior of Y-TZP. CAD/CAM-machined Y-TZP plates (0.5 mm thick), both with and without subsequent grinding with various grit sizes or grit-blasting with airborne alumina particles, were subjected to accelerated aging tests in a steam autoclave. Results showed that the CAD/CAM-machined surfaces initially exhibited superior hydrothermal degradation resistance, but deteriorated at a faster rate upon prolonged autoclave treatment compared with ground and grit-blasted surfaces. The accelerated hydrothermal degradation of CAD/CAM surfaces is attributed to the CAD/CAM machining damage and the absence of surface compressive stresses in the fully sintered material. Clinical relevance for surface treatments of zirconia frameworks in terms of hydrothermal and structural stabilities is addressed.

Get full access to this article

View all access options for this article.

References

Aboushelib MN, Feilzer AJ, Kleverlaan CJ (2009). Bridging the gap between clinical failure and laboratory fracture strength tests using a fractographic approach. Dent Mater 25:383–391.

Chevalier J (2006). What future for zirconia as a biomaterial? Biomaterials 27:534–543.

Chevalier J, Cales B, Drouin JM (1999). Low-temperature aging of Y-YZP ceramics. J Am Ceram Soc 82:2150–2154.

Deville S, Chevalier J, Gremillard L (2006). Influence of surface finish and residual stresses on the ageing sensitivity of biomedical grade zirconia. Biomaterials 27:2186–2192.

Garvie RC (1972). Phase analysis in zirconia systems. J Am Ceram Soc 55:303–305.

Garvie RC, Hannink RH, Pascoe RT (1975). Ceramic steel? Nature 258:703–704.

Hannink RHJ, Kelly PM, Muddle BC (2000). Transformation toughening in zirconia-containing ceramics. J Am Ceram Soc 83:461–487.

Hirano M (1992). Inhibition of low-temperature degradation of tetragonal zirconia ceramics—a review. Br Ceram Trans J 91:139–147.

Jeong SM, Ludwig K, Kern M (2002). Investigation of the fracture resistance of three types of zirconia posts in all-ceramic post-and-core restorations. Int J Prosthodont 15:154–158.

10.

Kohal RJ, Att W, Bachle M, Butz F (2008). Ceramic abutments and ceramic oral implants. An update. Periodontol 2000 47:224–243.

11.

Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L (1999). The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic. Dent Mater 15:426–433.

12.

Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L (2000). Strength and reliability of surface treated Y-TZP dental ceramics. J Biomed Mater Res 53:304–313.

13.

Lawn BR (1993). Fracture of brittle solids. 2nd ed. Cambridge: Cambridge University Press.

14.

Piconi C, Maccauro G (1999). Zirconia as a ceramic biomaterial. Biomaterials 20:1–25.

15.

Pilathadka S, Vahalová D, Vosáhlo T (2007). The zirconia: a new dental ceramic material. An overview. Prague Med Rep 108:5–12.

16.

Quinn GD, Ives LK, Jahanmir S (2005). On the nature of machining cracks in ground ceramics: Part I: SRBSN strengths and fractographic analysis. Machining Sci Technol 9:169–210.

17.

Raigrodski AJ (2004). Contemporary all-ceramic fixed partial dentures: a review. Dent Clin North Am 48:531–544.

18.

Rainforth WM (2000). Microstructural evolution at the worn surface: a comparison of metals and ceramics. Wear 245:162–177.

19.

Sindel J, Petschelt A, Grellner F, Dierken C, Greil P (1998). Evaluation of subsurface damage in CAD/CAM machined dental ceramics. J Mater Sci Mater Med 9:291–295.

20.

Strub JR, Rekow ED, Witkowski S (2006). Computer-aided design and fabrication of dental restorations—Current systems and future possibilities. J Am Dent Assoc 137:1289–1296.

21.

Wolfart M, Lehmann F, Wolfart S, Kern M (2007). Durability of the resin bond strength to zirconia ceramic after using different surface conditioning methods. Dent Mater 23:45–50.

22.

Wurst JC, Nelson JA (1972). Linear intercept technique for measuring grain-size in 2-phase polycrystalline ceramics. J Am Ceram Soc 55:109.

23.

Yin L, Jahanmir S, Ives LK (2003). Abrasive machining of porcelain and zirconia with a dental handpiece. Wear 255:975–989.

24.

Yin L, Song XF, Song YL, Huang T, Li J (2006). An overview of in vitro abrasive finishing & CAD/CAM of bioceramics in restorative dentistry. Int J Machine Tools Manufacture 46:1013–1026.

25.

Zhang Y (2006). Silicon nitride and silicon carbide-based ceramics. In: Ceramic matrix composites. Low IM, editor. Cambridge, UK: Woodhead Publishing Limited, pp. 536–559.

26.

Zhang Y, Lawn BR (2005). Fatigue sensitivity of Y-TZP to microscale sharp-contact flaws. J Biomed Mater Res B Appl Biomater 72:388–392.

27.

Zhang Y, Cheng YB, Lathabai S (2000). Erosion of alumina ceramics by air- and water-suspended garnet particles. Wear 240:40–51.

28.

Zhang Y, Cheng YB, Lathabai S (2001). Influence of microstructure on the erosive wear behaviour of Ca alpha-sialon materials. J Eur Ceram Soc 21:2435–2445.

29.

Zhang Y, Pajares A, Lawn BR (2004a). Fatigue and damage tolerance of Y-TZP ceramics in layered biomechanical systems. J Biomed Mater Res B Appl Biomater 71:166–171.

30.

Zhang Y, Lawn BR, Rekow ED, Thompson VP (2004b). Effect of sandblasting on the long-term performance of dental ceramics. J Biomed Mater Res B Appl Biomater 71:381–386.

31.

Zhang Y, Lawn BR, Malament KA, Van Thompson P, Rekow ED (2006). Damage accumulation and fatigue life of particle-abraded ceramics. Int J Prosthodont 19:442–448.