A Method to Predict the Effect of Thermal Residual Stresses on the Free-Edge Delamination Behavior of Fibre Reinforced Composite Laminates

Abstract

A method is presented which accounts for the effect of process-induced thermal residual stresses on the free-edge delamination behavior of fibre reinforced laminates. A strain energy release rate fracture mechanics formulation is derived based upon the Irwin crack closure integral. The finite element method is then used to calculate Mode I and Mode II crack opening displacements and stiffnesses for free-edge delamination cracks originating at a specified ply interface from which strain energy release rates due to thermal and mechanical loading are then obtained. The effect of processing temperature on strain energy development is included in the calculation of thermal energy release rates by using experimentally measured material property data.

To verify the model, (+35₂/-35₂/0₂/90₂)_s graphite-reinforced PEEK tensile test specimens were manufactured and tested to failure. Measured delamination strains agree well with predictions when the effect of thermal residual stresses is included. Neglecting residual stresses over-estimates the tensile delamination strength by approximately 32%.

Keywords

thermal residual stress free-edge delamination fibre reinforced thermoplastics APC-2

Get full access to this article

View all access options for this article.

References

1. Unger, W.J. and J.S. Hansen . 1993. "The Effect of Thermal Processing on Residual Strain Development in Unidirectional Graphite Fibre Reinforced PEEK," Journal of Composite Materials, 27:59-82.

2. Unger, W.J. and J.S. Hansen . 1993. "The Effect of Cooling Rate and Annealing on Residual Stress Development in Graphite Fibre Reinforced PEEK Laminates," Journal of Composite Materials, 27:108-137.

3. Puppo, A.H. and H.A. Evensen . 1970. "Interlaminar Shear in Laminated Composites Under Generalized Plane Stress," Journal of Composite Materials, 4:204-220.

4. Pagano, N.J. , R.B. Pipes . 1971. "The Influence of Stacking Sequence on Laminate Strength," Journal of Composite Materials, 5:50-57.

5. Pipes, R.B. and N.J. Pagano . 1970. "Interlaminar Stresses in Composite Laminates Under Uniform Axial Extension," Journal of Composite Materials, 4:538-548.

6. Pipes, R.B. and I.M. Daniel . 1971. "Moiré Analysis of the Interlaminar Shear Edge Effect in Laminated Composites," Journal of Composite Materials, 5:255-259.

7. Pagano, N.J. and R.B. Pipes . 1973. "Some Observations of the Interlaminar Strength of Composite Laminates," International Journal of Mechanical Science, 15:679-688.

8. Whitney, J.M. and C.E. Browning . 1972. "Free-Edge Delamination of Tensile Coupons," Journal of Composite Materials, 6:300-303.

9. Rybicki, E.F. , D.W. Schmueser and J. Fox . 1977. "An Energy Release Rate Approach for Stable Crack Growth in the Free Edge Delamination Problem," Journal of Composite Materials, 11:470-487.

10.

10. Wang, A.S.D. and F.W. Crossman . 1977. "Edge Effects on Thermally Induced Stresses in Composite Laminates," Journal of Composite Materials, 11:300-312.

11.

11. Herakovich, C.T. 1976. "On Thermal Edge Effects in Composite Laminates," International Journal of Mechanical Sciences, 18:129-134.

12.

12. Farley, G.L. and C.T. Herakovich . 1978. "Influence of Two Dimensional Hygrothermal Gradients on Interlaminar Stresses Near Free Edges," Advanced Composite Materials—Environmental Effects, ASTM STP 658, J.R. Vinson , Editor, ASTM, pp. 143-159.

13.

13. Wang, S.S. and I. Choi . 1979. "Boundary Layer Thermal Stresses in Angle-Ply Composite Laminates," Modern Developments in Composite Materials and Structures, J.R. Vinson , Editor, ASME, New York, pp. 315-341.

14.

14. O'Brien, T.K. , I.S. Raju and D.P. Garber . 1986. "Residual Thermal and Moisture Influences on the Strain Energy Release Rate Analysis of Edge Delamination," Journal of Composites Technology and Research, 8:37-47.

15.

15. Schanz, U. and G. Kress . 1989. "Influence of Temperature and Moisture on Total Strain Energy Release Rates Associated with Edge Delamination of Composite Test Coupons," Composites Science and Technology, 35:219-233.

16.

16. Law, G.E. 1984. "A Mixed Mode Fracture Analysis of (±25/90n)s Graphite/Epoxy Composite Laminates," Effects of Defects in Composite Materials, ASTM STP 836, ASTM, pp. 143-160.

17.

17. Whitney, J.M. and M. Knight . 1989. "Effect of Residual Stresses on Edge Delamination in Composite Materials," Proceedings, 30th Structures, Structural Dynamics and Materials Conference, AIAA/ASME/ASCE/AHS/ASC, April 3-5, pp. 1666-1670.

18.

18. Adams, D.F. , R.S. Zimmerman and E.M. Odom . 1987. "Frequency and Load Ratio Effects on Critical Strain Energy Release Rate Gc Thresholds of Graphite/Epoxy Composites," Toughened Composites, ASTM STP 937, N.J. Johnston , Ed., ASTM, pp. 242-259.

19.

19. Poursartip, A. 1987. "The Characterization of Edge Delamination Growth in Laminates Under Fatigue Loading," Toughened Composites, ASTM STP 937, N.J. Johnston , Ed., ASTM, pp. 222-241.

20.

20. O'Brien, T.K. 1986. "Fatigue Delamination Behaviour of PEEK Thermoplastic Composite Laminates," Proceedings, Ist Technical Conference of the American Society for Composites, Dayton, Ohio, pp. 404-420.

21.

21. Unger, W.J. 1993. "Reduction of the Free-Edge Effect in Fibre-Reinforced Thermoplastic Laminates by Localized Reconsolidation," Ph.D. Thesis, University of Toronto.

22.

22. Griffith, A.A. 1920. "The Phenomena of Rupture and Flow in Solids," Philosophical Transactions, Royal Society of London, 221A:163-198.

23.

23. Irwin, G.R. 1957. "Relation of Stress Near a Crack to the Crack Extension Force," Proceedings, 9th International Congress on Applied Mechanics, 8:245-251.

24.

24. Irwin, G.R. 1958. "Fracture," Handbuch der Physik, Vol. VI, pp. 551-589.

25.

25. Rybicki, E.F. and M.F. Kanninen . 1977. "A Finite Element Calculation of Stress Intensity Factors by a Modified Crack Closure Integral," Engineering Fracture Mechanics, 9:931-938.

26.

26. O'Brien, T.K. 1984. "Mixed Mode Strain-Energy Release Rate Effects on Edge Delamination of Composites," Effects of Defects in Composite Materials, ASTM STP 836, ASTM, pp. 125-142.

27.

27. O'Brien, T.K. , N.J. Johnston , I.S. Raju , D.H. Morris and R.A. Simonds . 1987. "Comparisons of Various Configurations of the Edge Delamination Test for Interlaminar Fracture Toughness," Toughened Composites, ASTM STP 937, N.J. Johnston , Ed., ASTM, pp. 199-221.

28.

28. Anon ., Standard Tests for Toughened Resin Composites. Revised Edition, NASA Reference Publication 1092, July, 1983.

29.

29. Raju, I.S. and J.H. Crews Jr. 1981. "Interlaminar Stress Singularities at a Straight Free-Edge in Composite Laminates," Computers and Structures, 14:21-28.

30.

30. O'Brien, T.K. 1982. "Characterization of Delamination Onset and Growth in a Composite Laminate," Damage in Composite Materials, ASTM STP 775, K.L. Reifsnider , Ed., Philadelphia, pp. 140-167.

31.

31. Wang, A.S.D. , M. Slomiana and R.B. Bucinell . 1985. "Delamination Crack Growth in Composite Laminates," Delamination and Debonding of Materials, ASTM STP 876, W.S. Johnson , Ed., ASTM, Philadelphia, pp. 135-167.

32.

32. O'Brien, T.K. , and N.J. Johnston . 1982. "A Simple Test for the Interlaminar Fracture Toughness of Composites," SAMPE Journal, July/August, pp. 8-15.

33.

33. APC-2 Product Data, Lit. Ref. No. APC-2/2, Imperial Chemical Industries PLC, 1988.

34.

34. O'Brien, T.K. 1985. "Analysis of Local Delaminations and Their Influence on Composite Laminate Behaviour," Delamination and Debonding of Materials, ASTM STP 879, W.S. Johnston , Ed., ASTM, pp. 282-297.

35.

35. Hashemi, S. , A.J. Kinloch and J.G. Williams . 1990. "The Effects of Geometry, Rate and Temperature on the Mode I, Mode II and Mixed-Mode I/Il Interlaminar Fracture of Carbon-Fibre/Poly(ether-ether-ketone) Composites," Journal of Composite Materials, 24:918-956.

36.

36. Carlile, D.R. and D.C. Leach . 1983. "Damage and Notch Sensitivity of Graphite/Peek Composite," Proceedings, 15th SAMPE Conference, Oct. 4-6, pp. 83-93.

37.

37. Leach, D.C. and D.R. Moore . 1985. "Toughness of Aromatic Polymer Composites Reinforced with Carbon Fibres," Composites Science and Technology, 23:131-161.

38.

38. Crick, R.A. , D.C. Leach , P.J. Meakin and D.R. Moore . 1987. "Interlaminar Fracture Morphology of Carbon Fibre/PEEK Composites," Journal of Materials Science, 22:2094-2104.

39.

39. Leach, D.C. , D.C. Curtis , and D.R. Tamblin . 1987. "Delamination Behavior of Carbon Fiber/PEEK Composites," Toughened Composites, ASTM STP 937, N.J. Johnston , Ed., ASTM, pp. 358-380.

40.

40. Smiley, A.J. and R.B. Pipes . 1987. "Rate Effects on Mode I Interlaminar Fracture Toughness in Composite Materials," Journal of Composite Materials, 21:670-687.

41.

41. Ogale, A.A. and R.L. McCullough . 1987. "Influence of Microstructure on Elastic and Viscoelastic Properties of PEEK," Composites Science and Technology, 30:185-201.

42.

42. Tsai, S.W. , Composites Design-1985, Think Composites, 1985.

43.

43. Talbott, M.F. , G.S. Springer and L.A. Berglund . 1987. "The Effects of Crystallinity on the Mechanical Properties of PEEK Polymer and Graphite Fibre Reinforced PEEK," Journal of Composite Materials, 21:1056-1081.

44.

44. Magnamite Graphite Fibre/Type AS-4 Product Data, No. 847-3, Hercules Inc.

45.

45. Jeronimidis, G. and A.T. Parkyn . 1988. "Residual Stresses in Carbon Fibre-Thermoplastic Matrix Laminates," Journal of Composite Materials, 22:401-415.