Analysis of the Transverse Cracking of Cross-Ply Laminates: A Generalized Approach

Abstract

A generalized approach has been developed to evaluate the two-dimensional stress distribution in cracked cross-ply laminates. Comparisons between finite element analysis and analytical models show that a complete parabolic analysis extended to 0° and 90° layers yields a fairly good approximation of the strain and stress distributions in the case of [0°/90°]_s, with equal thicknesses of 0° and 90° layers. However a deviation is observed in the case of thick 0° layers. The analysis presented in this paper keeps a parabolic variation of the longitudinal displacement across the thickness of 90° layer, and generalizes the longitudinal displacement distribution across the thickness of 0° layers by taking an indeterminate distribution. The development of this analysis allows us to obtain the general form of the stress distributions in 0° and 90° layers. Finally, it is proposed a particular form of the variation of the longitudinal displacement across the thickness of 0° plies which yields a good agreement of the stress distributions with finite element analysis for the different stacking sequences investigated.

Keywords

transverse cracking cross-ply laminates stress and strain distributions analytical model

Get full access to this article

View all access options for this article.

References

1. Garret, K. W. and J. E. Bailey . 1977. "Multiple transverse fracture in 90° cross-ply laminates of a glass fibre-reinforced polyester," Journal of Materials Science, 12:157-168.

2. Highsmith, A. L. and K. L. Reifsnider . 1982. "Stiffness Reduction Mechanisms in Composite Laminates," Damage in Composite Materials, ASTM STP 775, K. L. Reifsnider Ed.: 103-117.

3. Manders, P. W. , T.-W. Chou , F. R. Jones and J. W. Rock . 1983. "Statistical analysis of multiple fracture in 0°/9°/0° glass fibre/epoxy resin laminates," Journal of Materials Science, 18:2876-2889.

4. Ogin, S. L. , P. A. Smith and P. W. R. Beaumont . 1985. "Matrix cracking and stiffness reduction during the fatigue of a (0/90)s GFRP laminate," Composites Science and Technology, 22:23-31.

5. Steif, P. S. 1984. "Parabolic shear lag analysis of a [0/90]s, laminate," in "Transverse ply crack growth and associated stiffness reduction during the fatigue of a simple cross-ply laminates," by S. L. Ogin, P. A. Smith and P. W. R. Beaumont, Report CUED/C//MATS/TR 105, Cambridge University.

6. Han, Y. M. , H. T. Hahn and R. B. Croman . 1988. "A simplified analysis of transverse ply cracking in cross-ply laminates," Composites Science and Technology, 31:165-177.

7. Laws, N. and G. Dvorak . 1988. "Progressive transverse cracking in composite laminates," Journal of Composite Materials, 22:900-916.

8. Smith, P. A. and J. R. Wood . 1990. "Poisson's ratio as a damage parameter in the static tensile loading of simple cross-ply laminates," Composites Science and Technology, 38:85-93.

9. Cox, H. L. 1952. "The elasticity and strength of paper and other fibrous materials," British Journal Applied Physics, 22:72-79.

10.

10. Fukunaga, H. , T.-W. Chou , P. W. M. Peters and K. Schulte . 1984. "Probabilistic failure strength analyses of graphite/epoxy cross-ply laminates," Journal of Composite Materials, 18:339-356.

11.

11. Lim, S. G. and C. S. Hong . 1989. "Effect of transverse cracks on the thermomechanical properties of cross-ply laminated composites." Composites Science and Technology, 34:145-162.

12.

12. Lee, J. W. and I. M. Daniel . 1980. "Progressive transverse cracking of cross-ply composite laminates," Composites Science and Technology, 24:1225-1243.

13.

13. Fan, J. and J. Zhang . 1993. "In-situ damage evolution and micro/macro transition for laminated composites," Composites Science and Technology, 47:107-118.

14.

14. Zhang, J. , J. Fan and C. Soutis . 1992. "Analysis of multiple matrix cracking in [±Om/90m]s composite laminates," Composites, 23(5):291-298.

15.

15. Hashin, Z. 1985. "Analysis of cracked laminates: a variational approach," Mechanics of Materials, 4:121-136.

16.

16. Nairn, J. A. 1989. "The strain energy release rate of composite microcracking: a variational approach," Journal of Composite Materials, 23:1106-1129.

17.

17. Berthelot, J. M. , P. Leblond , A. El Mahi and J. F. Le Corre . 1996. "Transverse cracking of crossply laminates: Part 1. Analysis," Composites, 27A:989-1001.