New Ideas on the Measurement of the In-Plane Shear Strength of Unidirectional Composites

Abstract

This paper addresses the issue of the measurement of the in-plane shear strength of unidirectional composites. It is shown from recently published material that for both Iosipescu and 100 off-axis tensile tests, failure under a homogeneous stress state is achieved. However, these stress states are not pure shear and it is shown that ignoring the presence of transverse tensile and compressive stresses, respectively in the 100 off-axis and the Iosipescu tests, would lead to important apparent differences in the in-plane shear strength measured from both tests.

An analysis using a quadratic failure criterion underlines the role of the transverse stresses and values of 95 and 98 MPa for the shear strength of unidirectional T300/914 are derived respectively from the 100 off-axis and the Iosipescu tests.

Keywords

in-plane shear Iosipescu test 100 off-axis test shear strength unidirectional lamina

Get full access to this article

View all access options for this article.

References

1. Broughton, W. R. , M. Kumosa and D. Hull . 1990. "Analysis of the Iosipescu Shear Test as Applied to Unidirectional Carbon-Fibre Reinforced Composites," Composites Science and Technology, 38:299-325.

2. Morton, J. , H. Ho , M. Y. Tsai and G. Farley . 1992. "An Evaluation of the Iosipescu Specimen for Composite Materials Shear Property Measurement," J. Composite Materials, 26(5):708-750.

3. Adams, D. F. and E. Q. Lewis . 1995. "Experimental Strain Analysis of the Iosipescu Shear Test Specimen," Experimental Mechanics, Dec., 95:352-360.

4. Pierron, F. and A. Vautrin . 1996. "The 100 Off-Axis Tensile Test: A Critical Approach," Composites Science and Technology, 56(4):483-488.

5. Pierron, F. and A. Vautrin . 1996. "Failure Analysis of 0° Composite Iosipescu Specimens," Submitted to Composites Science and Technology.

6. Pierron, F. and A. Vautrin . 1996. "Analysis of the Failure of Unidirectional Composite Iosipescu Specimens," Proceedings of ECCM-7 CiS-3, May 14-16, in London, pp. 183-188.

7. Chamis, C. C. and J. H. Sinclair . 1977. Ten-Deg Off-Axis Test for Shear Properties in Fibre Composites," Experimental Mechanics, 17(9):339-346.

8. Pindera, M.-J. and C. T. Herakovich . 1986. Shear Characterization of Unidirectional Composites with the Off-Axis Tension Test," Experimental Mechanics, 26:103-112.

9. Wu, E. M. and R. L. Thomas . 1968. "Off-Axis Test of a Composite," J. Composite Materials, 2(4):523-526.

10.

10. Pindera, M.-J. , G. Choski , J. S. Hidde and C. T. Herakovich . 1987. "A Methodology for Accurate Shear Characterization of Unidirectional Composites," J. Composite Materials, 21:1164-1185.

11.

11. Sun, C. T. and I. Chung . 1993. "An Oblique End-Tab Design for Testing Off-Axis Composite Specimens," Composites, 24(8):619-623.

12.

12. Walrath, D. E. and D. F. Adams . 1983. "The Iosipescu Shear Test as Applied to Composite Materials," Experimental Mechanics, 23:105-110.

13.

13. Pierron, F. and A. Vautrin . 1994. "Accurate Comparative Determination of the In-Plane Shear Modulus of T300/914 by the Iosipescu and 450 Off-Axis Tests. Composites Science and Technology, 52(1):61-72.

14.

14. Swanson, S. R. , M. Messick and G. R. Toombes . 1985. "Comparison of Torsion Tube and Iosipescu In-Plane Shear Test Results for a Carbon Fibre-Reinforced Epoxy Composite," Composites, 16(3):220-224.

15.

15. Adams, D. F. and D. E. Walrath . 1987. "Current Status of the Iosipescu Shear Test," J. Composite Materials, 21:494-506.

16.

16. Tsai, S. W. and E. M. Wu . 1971. "A General Theory of Strength for Anisotropic Materials;," J. Composite Materials, 5:58-80.

17.

17. Hart-Smith, L. J. 1993. "The Role of Biaxial Stresses in Discriminating between Meaningful and Illusory Composite Failure Theories," Composite Structures, 25:3-20.

18.

18. Kam, T. Y. and H. F. Sher . 1995. "Nonlinear and First-Ply Failure Analyses of Laminated Composite Cross-Ply Plates," J. Composite Materials, 29:463-482.