Tests were performed to assess the effects of processing conditions and laminate layup on the change in shape (springback). Twelve inch long and one inch wide coupons made of Fiberite T300/976 graphite/epoxy were tested. Coupons of different layups were cured using different types of molds and different types of vacuum bagging arrangements. The curing was performed with different temperature cycles. Springback was measured from the change in shape of initially flat coupons. The results indicated the effects of the applied temperature, applied pressure, material of the mold, arrangement of the teflon surrounding the coupon, and laminate layup on springback.
Get full access to this article
View all access options for this article.
References
1.
1. Hyer, M. W.1981. "Calculations of the Room-Temperature Shapes of Unsymmetric Laminates,"Journal of Composite Materials, 15:296-310.
2.
2. Hyer, M. W.1982. "The Room-Temperature Shapes of Four-Layer Unsymmetric Cross-Ply Laminates,"Journal of Composite Materials, 16:319-340.
3.
3. Pagano, N. J. and H. T. Hahn. 1976. "Evaluation of Composite Curing Stresses,"Journal of Composite Materials, 10:317-329.
4.
4. Hahn, H. T. and N. J. Pagano. 1975. "Curing Stresses in Composite Laminates,"Journal of Composite Materials, 9:91-106.
5.
5. Weitsman, Y.1979. "Residual Thermal Stresses Due to Cool-Down of Epoxy-Resin Composites,"Journal of Applied Mechanics, 46:563-567.
6.
6. Zewi, I. G., I. M. Daniel and J. T. Gotro. 1987. "Residual Stresses and Warpage in Woven-Glass/Epoxy Laminates,"Experimental Mechanics, 27:44-50.
7.
7. Hahn, T. A.1993. "Thermal Stress Relaxation Due to Plastic Flow in the Fiber Coating of a Continuous Fiber Reinforced Composite,"Journal of Composite Materials, 27:1545-1577.
8.
8. Daniel, I. M.. T. M. Wang, D. Karalekas and J. T. Gotro. 1990. "Determination of Chemical Cure Shrinkage in Composite Laminates,"Journal of Composites Technology and Research, 12:172-176.
9.
9. Crasto, A. S. and R. Y. Kim. 1993. "On the Determination of Residual Stresses in Fiber-Reinforced Thermoset Composites,"Journal of Reinforced Plastics and Composites, 12:545-558.
10.
10. Patterson, J. M., L. P. Kollar and G. S. Springer. 1991. "Experimental Observations of the Springback Phenomena,"Composites-Design, Manufacturing and Applications, Society for the Advancement of Material and Process Engineering, pp. 10D1-10D8.
11.
11. Daniel, I. M. and T. Liber. 1977. "Effect of Laminate Construction on Residual Stresses in Graphite/Polyimide Composites,"Experimental Mechanics, 17:21-25.
12.
12. Hahn, H. T.1976. "Residual Stresses in Polymer Matrix Composite Laminates,"Journal of Composite Materials, 10:266-278.
13.
13. White, S. R. and H. T. Hahn. 1993. "Cure Cycle Optimization for the Reduction of Processing-Induced Residual Stresses in Composite Materials,"Journal of Composite Materials, 27:1353-1378.
14.
14. Hahn, H. T.1984. "Effect of Residual Stresses in Polymer Matrix Composites,"The Journal of the Astronautical Science, 32:253-267.
15.
15. Dusi, M. R., W. I. Lee, P. R. Ciriscioli and G. S. Springer. 1987. "Cure Kinetics and Viscosity of Fiberite 976 Resin,"Journal of Composite Materials, 21:243-261.
16.
16. Loos, A. C. and G. S. Springer. 1983. "Curing of Epoxy Matrix Composites,"Journal of Composite Materials, 17:135-169.