The Strength Distribution of 90° Plies in 0/90/0 Graphite-Epoxy Laminates

Abstract

Graphite epoxy cross ply laminates show multiple cracking in the 90 ° ply before final rupture occurs. By the aid of a piezo-electric load cell crack formation was measured as a function of the applied load in (0₂/90₂)_s, (0₂/90₃)_s and (0₂/90₆)_s laminates. With these experimental results and a shear lag analysis, to account for the non-homogeneous stress distribution in cracked 90° plies, it was possible to estimate the Weibull strength distribution of the respective 90° ply. it was found that at decreasing 90° ply thickness the shape factor increases. This can be attributed to a suppression of defect growth close to the 90°/0° interface. Because of the changing shape parameter at decreasing ply thickness a description of the thickness effect by a Weibull shape parameter is im possible.

Get full access to this article

View all access options for this article.

References

Parvizi, A. , Garrett, K.W. , and Bailey, J.E. , "Constrained Cracking in Glass-fibre Reinforced Epoxy Cross-ply Laminates," J. of Mat. Sc., 13, pp. 195-201 (1978).

Flaggs, D.L. , and Kural, M.H. , "Transverse Lamina Strength in Graphite-epoxy Laminates," J. Comp. Mat. , 16, pp. 103-116 (March 1982).

Crossman, F.W. , and Wang, A.S.D. , "The Dependence of Transverse Cracking and Delamination on Ply Thickness in Graphite/Epoxy Laminates," ASTM STP-775, pp. 118-139(1982).

Wang, A.S.D. , "Growth Mechanisms of Transverse Cracks and Ply Delamination in Composite Laminates," ICCM IV, Paris, pp. 170-183 (1980).

Manders, P.W. , Chou, T.W. , Jones , F.R. , and Rock, J.W. , "Statistical Analyses of Multiple Fracture in 0/90/0 Glass Fiber/Epoxy Resin Laminates," J. of Mat. Sc., 18, pp. 2876-2889 (1983 ).

Fukunaga, H. , Chou, T.S. , Peters, P.W.M. , and Schulte, K. , "Probabilistic Failure Strength Analyses of Graphite/Epoxy Cross-Ply Laminates," to be published in J. of Comp. Mat.

Garrett, K.W. , and Bailey, J.E. , "Multiple Transverse Fracture in 90° Cross-ply Laminates of a Glass Fibre-Reinforced Polyester," J. of Mat. Sc., 12, pp. 157-168 (1977).

Parvizi, A. , and Bailey, J.E. , "On Multiple Transverse Cracking in Glass-Fibre Epoxy Cross-ply Laminates," J. of Mat. Sc., 13, pp. 2131-2136 (1978).

Peters, P.W.M. , "The Strength of 0/90 Graphite-epoxy Laminates with Cracked 90° Layers," Poster paper presented at Conf. Testing Evaluation and Quality Control of Composites, Univ. of Surrey , Guildford, U.K. (September 13-14, 1983).

10.

Highsmith, A.L. , Stinchcomb, W.W. , and Reifsnider , K.L. , "Stiffness Reduction Resulting from Transverse Cracking in Fiber-reinforced Composite Laminates," VPI-E-81.33, Dept. of Eng. Sc. and Mechanics, Virginia Polytechnic Inst. and State University, Blacksburg, Virginia 24061-4899 (November 1981).

11.

Sun, C.T. , and Yamada, S.E. , "Strength Distribution of a Undirectional Fiber Composite," J. Comp. Mat., Vol. 12, pp. 169-176 (1978).

12.

Rodini, B.T. , and Eisenmann, J.R. , "An Analytical and Experimental Investigation of Edge Delamination in Composite Laminates," Proc. 4th Conf, Fibrous Comp. in Structural Design , San Diego, CA, p. 441, Cited in [11] (November 1978).