Influence of Environmental Cycling on the Mechanical Properties of Composite Materials

Abstract

Static and fatigue tests were carried out on CFRP specimens exposed to environmental conditions with the purpose of simulating the real environ mental conditions for today's aircraft.

The investigation has comprised ± 45° reinforced test specimens, 24 mm wide and 1 mm thick, built up from carbon-fiber prepreg THORNELL 300/NARMCO 5208. In the investigation polyurethane-covered specimens were also tested, in order to investigate the protecting ability of that mate rial.

The results show clear deteriorations in both static and fatigue proper ties due to environmental exposure. The material becomes more ductile under the influence of moisture, and after prolonged exposure one can notice a debonding effect between the fibers and the matrix. Environ mental degradation becomes more pronounced if the specimens are pre loaded prior to exposure.

Get full access to this article

View all access options for this article.

References

C.E. Browning , "The effects of moisture on the properties of high performance structural resins on composites," Society of Plastics Industry, SPI. Reinforced plastics/composites division. 28th Annual conference 1973, pp. 15A; 1—16.

P.N. Rao , K.E. Hofer , "Fatigue behavior of graphite composites," AD 738 492.

L.G. Bevan , J.B. Sturgeon , "Fatigue limits in CFRP," 2nd International Conference on Carbon Fibres, London, 18-20 February 1974, Paper 32.

E.L. McKague , Jr. , J.E. Halkias , J.D. Reynolds , "Moisture in composites - The effect of supersonic service on diffusion," J. Composite Materials , Vol. 9 (1975), p. 2.

E.L. McKague , Jr. , J.D. Reynolds , J.E. Halkias , "Thermomechanical testing of plastics for environmental resistance," J. Testing and Evaluation, Vol. 1 (1973), p. 468.