Gauge Length and Surface Damage Effects on the Strength Distributions of Silicon Carbide and Sapphire Filaments

Abstract

The assumption of the constancy of the Weibull distribution parameters with variations in gauge length was tested for SiC-on-carbon and sapphire filaments. Surface damage was superimposed on the gauge length variations to investigate the effect of the additional flaw spectrum on the gauge length conclusions. The results have demonstrated that, even when failure is due to a single flaw spectrum, the Weibull m parameter is not constant over a gauge length range of 40 times the shortest length. When failure is due to overlapping flaw distributions the possibility of extrapolations assuming constant Weibull parameters is even more remote. The constant gauge length data was used in a modified form of the Poisson distribution proposed by Phoenix to compare to the extrapolative ability of the Weibull distribution. Very little difference in accuracy was found with the former approach being marginally better.

Get full access to this article

View all access options for this article.

References

B.W. Rosen , "Mechanics of Composite Strengthening," in Fiber Composite Materials papers from a Seminar of ASM, ( 1964), p. 37.

C. Zweben and B.N. Rosen , "A Statistical Theory of Material Strength with Application to Composite Materials," J. Mech. Phys. Solids, Vol. 18 (1970), p. 189.

C. Zweben , "On the Strength of Notched Composites," J. Mech. Phys. Solids, Vol. 19 (1971), p. 103.

J.M. Lifshitz and A. Rotem , "Longitudinal Tensile Failure of Unidirectional Fibrous Composites," J. Mater. Sci., Vol. 7 (1972), p. 861.

S.L. Phoenix , "Probabilistic Concepts in Modeling the Tensile Strength Behavior of Fiber Bundles and Unidirectional Fiber/Matrix Composites," in Composite Materials: Testing and Design (Third Conference) ASTM STP 546, American Society for Testing and Materials, ( 1974), p. 130.

A.G. Metcalfe and G.K. Schimtz "Effect of Length on the Strength of Glass Fibers," Proc. ASTM, Vol. 64 (1964), p. 1075.

H.E. Labelle and A.I. Mlvasky , "Growth of Controlled Profile Crystals from the Melt: Part I — Sapphire Filaments," Mat. Res. Bull., Vol. 6 (1971), p. 571.

G.F. Hurley and J.T.A. Pollock , "Mechanical and Structural Characterization of Sapphire Ribbons and Continuous Filaments," Met. Trans. , Vol. 3 (1972), p. 397.

R.E. Tressler and T.L. Moore , "Mechanical Property and Interface Reaction Studies of Titanium — Alumina Composites," Metals Engineering Quarterly, Vol. 11 (1971), p. 16.

10.

H. Debolt and V. Krukonis , U.S. Air Force Material Laboratory Technical Report TR-73-140 ( 1973).

11.

R.E. Tressler and R.L. Crane in "Advanced Materials: Composites and Carbon ," edited by J. Buckley, (Proceedings of Amer. Ceram. Soc., Symposium, Chicago, III., (1971), p. 59.

12.

D.M. Kotchick and R.E. Tressler , "Surface Damage and Environmental Effects on the Strain-Rate Sensitivity of the Strength of Sapphire and Silicon Carbide Filaments," J. Matl. Sci., Vol. 10 (1975), p. 608.

13.

S.L. Phoenix , "Statistical Analysis of Flaw Strength Spectra of High Modulus Fibers " ASTM Comp. Reliability Conf, Las Vegas, Nevada, (1974).

14.

S.L. Phoenix and R.G. Sexsmith , "Clamp Effects in Fiber Testing ," J. Comp. Matl., Vol. 6 (1972), p. 322.

15.

S.M. Wiederhorn , "Moisture Assisted Crack Growth in Ceramics ," Inter. J. Fracture Mech., Vol. 4 (1968), p. 171.