This work investigated the phenomenon of interfacial debonding due to hygrothermal aging (HA), which was quantified using Field Emission Scanning Electron Microscopy (FESEM) and Atomic Force Microscopy (AFM). Several micrographs of carbon fiber/epoxy cross-ply laminate coupons were analyzed, including unaged (HA/0) samples, as well as those aged for 1000 h (HA/1000) and 2000 h (HA/2000). To quantify the extent of debonding, an image thresholding tool was employed. For HA/0, HA/1000, and HA/2000 coupons, the average interfacial debonding arc length of inner plies was longer than that of the respective outer plies by 14%, 17%, and 21%, respectively. Residual stress variation across inner plies is more pronounced compared to outer plies due to the latter's freedom of expansion. The debonding that occurred without external loading was due to the combined effects of matrix and interface plasticization, chemical reaction, viscoelastic changes, and swelling. The AFM 3-D surface topography revealed that HA/0, HA/1000, and HA/2000 specimens had progressively lower peak-valley distances of 135 nm, 113 nm, and 82 nm, respectively, due to matrix swelling.
ZhangMJinLZhaiY, et al.Bio-inspired gallic acid-gelatin coating: A novel strategy for eco-friendly interfacial modification of carbon fiber composites. Compos Commun2021; 26: 100790.
2.
MengBWYueXZhangYR, et al.Direct visualization of interfacial debonding in FRP structure using an AIE molecule. Compos Commun2021; 27: 100816.
3.
WangZYangBXianG, et al.An effective method to improve the interfacial shear strength in GF/CF reinforced epoxy composites characterized by fiber pullout test. Compos Commun2020; 19: 168–172.
4.
RoyS, Moisture-induced degradation, long-term durability of polymeric matrix composites. Long-Term Durability of Polymeric Matrix Composites2012; 1: 181–236.
5.
AlamPRobertCÓ BrádaighCM. Tidal turbine blade composites – A review on the effects of hygrothermal aging on the properties of CFRP. Compos. Part B Eng2018; 149: 248–259.
6.
NiuYFWangDDYaoJW. Investigation of the performances for CFRP composites exposed to different aging environment at nanoscale. Polym Test2022; 116: 107771.
7.
XuPFengTWangY, et al.A novel approach based on stress-impedance effect to assess the interfacial properties in fiber-reinforced composites. Compos Commun2021; 27: 100854.
8.
WangYHahnTH. AFM characterization of the interfacial properties of carbon fiber reinforced polymer composites subjected to hygrothermal treatments. Compos Sci Technol2007; 67: 92–101.
9.
BeheraAVishwakarmaAThawreMM, et al.Effect of hygrothermal aging on static behavior of quasi-isotropic CFRP composite laminate. Compos Commun2020; 17: 51–55.
10.
BeheraADuparePThawreMM, et al.Effects of hygrothermal aging and fiber orientations on constant amplitude fatigue properties of CFRP Multidirectional composite laminates. Int J Fatigue2020; 136: 105590.
11.
BeheraADuparePThawreMM, et al.Effect of fatigue loading on stiffness degradation, energy dissipation, and matrix cracking damage of CFRP [±45]3S composite laminate. Fatigue Fract Eng Mat Struct2019; 42(10): 2302–2314.
12.
LiuTQLiuXFengP. A comprehensive review on mechanical properties of pultruded FRP composites subjected to long-term environmental effects. Compos. Part B Eng2020; 191: 107958.
13.
GuoXXiongCJinZ, et al.A review on mechanical properties of FRP bars subjected to seawater sea sand concrete environmental effects. J Build Eng2022; 58: 105038.
14.
AkayMAh MunSKStanleyA. Influence of moisture on the thermal and mechanical properties of autoclaved and oven-cured Kevlar-49/epoxy laminates. Compos Sci Technol1997; 57: 565–571.
15.
LiuXLiuTQFengP. Long-term performance prediction framework based on XGBoost decision tree for pultruded FRP composites exposed to water, humidity, and alkaline solution. Compos Struct2022; 284: 115184.
16.
KrishnanP. Evaluation and methods of interfacial properties in fiber-reinforced composites. In: Mechanical and Physical Testing of Biocomposites, Fibre-Reinforced Composites and Hybrid Composites. Elsevier, 2018, pp. 343–385, DOI: 10.1016/B978-0-08-102292-4.00018-7.
17.
PavlidouSPapaspyridesCD. The effect of hygrothermal history on water sorption and interlaminar shear strength of glass/polyester composites with different interfacial strength. Compos. Part A2003; 34: 1117–1124.
18.
PavlidouSMaiSZorbasT, et al.Mechanical properties of glass fabric/polyester composites: Effect of silicone coatings on the fabrics. J Appl Polym Sci2004; 91: 1300–1308.
19.
ShettyKSrihariSManjunathaCM. Effect of hygrothermal aging on the interlaminar shear strength of a carbon fibre composite. Proc. Struct. Integrity2019; 14: 849–854.
20.
Yekani FardMRajiBPankretzH. Correlation of nanoscale interface debonding and multimode fracture in polymer carbon composites with long-term hygrothermal effects. Mech Mater2020; 150: 103601.
21.
Hex ply, IMA/M21 prepreg, Global Version, 2015.
22.
ASTM D5229/D5229M-14. Standard test method for moisture absorption properties and equilibrium conditioning of polymer matrix composite materials. West Conshohocken, PA: ASTM International, 2014.
23.
GrammatikosSAZafariBEverndenMC, et al.Moisture uptake characteristics of a pultruded fibre reinforced polymer flat sheet subjected to hot/wet aging. Polym Degrad Stab2015; 121: 407–419.
24.
StarkovaOBuschhornSTMannovE, et al.Water transport in epoxy/MWCNT composites. Eur Polym J2013; 49: 2138–2148.
25.
Yekani FardMRajiB. Statistical analysis of peak force atomic force microscopy data for the interphase thickness and modulus in carbon fiber–reinforced epoxy resin composites exposed to different heat and humidity levels. J Aerosp Eng2021; 34: 2.
26.
YangCZhuDYangF, et al.Quantitative analysis based on atomic force microscopy characterization of interfacial properties between carbon fibers and epoxy resin subjected to hygrothermal and thermal treatments. Compos Sci Technol2020; 198: 108278.
27.
ShenCHSpringerGS. Environmental Effects on the Elastic Moduli of Composite Materials. J Compos Mater1977; 11: 250–264.
28.
Mohd IshakZAriffinASenawiR. Effects of hygrothermal aging and a silane coupling agent on the tensile properties of injection molded short glass fiber reinforced poly(butylene terephthalate) composites. Eur Polym J2001; 37: 1635–1647.
29.
WeitsmanYJGuoYJ. A correlation between fluid-induced damage and anomalous fluid sorption in polymeric composites. Compos Sci Technol2002; 62: 889–908.
30.
MoriiTIkutaNKiyosumiK, et al.Weight-change analysis of the interphase in hygrothermally aged FRP: consideration of debonding. Compos Sci Technol1997; 57: 985–990.
31.
LiaoKSchultheiszCRHunstonDL. Effects of environmental aging on the properties of pultruded GFRP. Compos. Part B Eng1999; 30: 485–493.
32.
FritzNKKoppRNasonAK, et al.New interlaminar features and void distributions in advanced aerospace-grade composites revealed via automated algorithms using micro-computed tomography. Compos Sci Technol2020; 193: 108132.
33.
RosiniSMavrogordatoMNEgorovaO, et al.In situ statistical measurement of local morphology in carbon-epoxy composites using synchrotron X-ray computed tomography. Compos. Part A App. Sc. and Manuf2019; 125: 105543.
34.
SelmyAIElsesiARAzabNA, et al.Interlaminar shear behavior of unidirectional glass fiber (U)/random glass fiber (R)/epoxy hybrid and non-hybrid composite laminates. Compos. Part B Eng2012; 43: 1714–1719.
35.
AlsaadiMUglaAAErkligA, A comparative study on the interlaminar shear strength of carbon, glass, and Kevlar fabric/epoxy laminates filled with SiC particles, J Compos Mater2017; 51: 2835–2844.