Development of a dilatometer for shrinkage analysis of thermosetting resin systems at accurate processing conditions of liquid composite moulding processes and exemplary results of the effects of varying processing conditions on chemical shrinkage of an epoxy resin

Abstract

The processing of thermosetting resin systems in liquid composite moulding is accompanied by a change in density through chemical and thermal shrinkage during the curing reaction of the resin and cooling of a part from processing to operating temperature. These effects cause residual stresses and an undesired characteristic surface pattern in endless fibre reinforced plastics. However, the accurate measurement of the chemical and thermal shrinkage is challenging with state-of-the-art measurement devices, especially for highly reactive thermosetting resin systems. The main disadvantage is that it is not possible to recreate the processing conditions of modern liquid composite moulding processes during the measurement of the thermosetting resin systems and has therefore limited use for process optimisations. In this paper the development of a dilatometer, which is capable of measuring the shrinkage in highly reactive thermosetting resins providing the processing conditions of liquid composite moulding is presented. The effects of processing pressure and internal mould release agents on chemical shrinkage are analysed with the developed dilatometer for different epoxy resins. The trials demonstrate a significant effect of processing pressure on chemical shrinkage.

Keywords

Curing cross-linking reaction chemical shrinkage thermal shrinkage epoxy resin liquid composite moulding dilatometer shrinkage analysis

Get full access to this article

View all access options for this article.

References

Msallem

Jacquemin

Boyard

et al.

Material characterization and residual stresses simulation during the manufacturing process of epoxy matrix composites. Compos Part A 2010; 41: 108–115.

Harris

. Shrinkage stresses in glass/resin composites. J Mater Sci 1978; 13: 173–177.

Wisnom

Gigliotti

Ersoy

et al.

Mechanisms generating residual stresses and distortion during manufacture of polymer-matrix composite structures. Compos Part A 2006; 37: 522–529.

Nawab

Jacquemin

Casari

et al.

Evolution of chemical and thermal curvatures in thermoset-laminated composite plates during the fabrication process. J Compos Mater 2013; 47: 327–339.

Chekanov

Korotkov

Rozenberg

et al.

Cure shrinkage defects in epoxy resins. Polymer 1995; 36: 2013–2017.

Eom

Boogh

Michaud

et al.

Stress-initiated void formation during cure of a three-dimensionally constrained thermoset resin. Polym Eng Sci 2001; 41: 492–503.

Yua

Adams

da Silva Lucas

. Development of a dilatometer and measurement of the shrinkage behaviour of adhesives during cure. Int J Adhes Adhes 2013; 47: 26–34.

Lionetto

Maffezzoli

. Monitoring the cure state of thermosetting resins by ultrasound. Materials 2013; 6: 3783–3804.

Hopmann

Michaeli

Bastian

. Endlosfaserverstärkte kunststoffbauteile mit class-A-oberflächenqualität mittels spaltimprägnierverfahren. GAK – Gummi Fasern Kunststoffe 2012; 65: 45–53.

10.

Nawab

Park

Saouab

et al.

Shape distortion of carbon/epoxy composite parts during fabrication. Macromol Symp 2014; 340: 59–64.

11.

Wucher

Lani

Pardoen

et al.

Tooling geometry optimization for compensation of cure-induced distortions of a curved carbon/epoxy C-spar. Compos Part A: Appl Sci Manuf 2014; 56: 27–35.

12.

Hopmann

Michaeli

Bastian

. Gap impregnation process: CRP components with class a surfaces. Kunststoffe Int 2012; 6: 31–34.

13.

Babayevsky

Gillham

. Epoxy thermosetting systems: dynamic mechanical analysis of the reactions of aromatic diamines with the diglycidyl ether of bisphenol A. J Appl Polym Sci 1973; 17: 2067–2088.

14.

Gillham

Benci

Noshay

. Isothermal transitions of a thermosetting system. J Polym Sci Polym Symp 1974; 46: 279–289.

15.

Nawab

Shahid

Boyard

et al.

Chemical shrinkage characterization techniques for thermoset resins and associated composites. J Mater Sci 2013; 48: 1–8.

16.

Holst

Schänzlin

Wenzel

et al.

Time-resolved method for the measurement of volume changes during polymerization. J Polym Sci Part B Polym Phys 2005; 43: 2314–2325.

17.

Blumenstock

. Analyse der Eigenspannungen während der Aushärtung von Epoxidharzmassen 2003. PhD thesis, Fakultaet Verfahrenstechnik und Technische Kybernetik der Universitaet Stuttgart, 2003.

18.

Potter

Wisnom

et al.

In-situ measurement of chemical shrinkage of MY750 epoxy resin by a novel gravimetric method. Compos Sci Technol 2004; 64: 55–64.

19.

Rudolph M, Stockmann M and Ihlemann J. Experimental determination and modelling of volume shrinkage in curing thermosets, http://arxiv.org/abs/1404.0310 (accessed July 2015).

20.

Tardif

Agazzi

Sobotka

et al.

A multifunctional device to determine specific volume, thermal conductivity and crystallization kinetics of semi-crystalline polymers. Polym Test 2012; 31: 819–827.

21.

Nawab

Tardif

Boyard

et al.

Determination and modelling of the cure shrinkage of epoxy vinylester resin and associated composites by considering thermal gradients. Compos Sci Technol 2012; 73: 81–87.

22.

Thermophysical properties of fluid systems, http://webbook.nist.gov/chemistry/fluid/ (accessed July 2015).

23.

EPIKOTE™ Resin 05475, EPIKURE™ Curing Agent 05443, HELOXY™ Additive 112 data sheet, https://www.hexion.com/products/technicaldatasheet.aspx?id = 28410 (accessed July 2015).