In this study, the mechanical performance assessment of a newly developed carbon fibre-reinforced polyimide composite system T650/NEXIMID® MHT-R is presented. This system was subjected to a series of mechanical tests at ambient and elevated temperature (320℃) to determine basic material properties. Moreover, an additional test was conducted, using a T650/NEXIMID® MHT-R laminate in which the fibre sizing was thermally removed prior to laminate manufacturing, to investigate the effect of fibre treatment on mechanical performance. The experimental results indicated that the T650/NEXIMID® MHT-R composites along with exceptionally high Tg (360–420℃) exhibited competitive mechanical properties to other commercially available polyimide and epoxy-based systems. At elevated temperature, the fibre-dominated properties were not affected whilst the properties defined by matrix and fibre/matrix interface were degraded by approximately 20–30%. Finally, the fibre sizing removal did not affect the tensile and compressive strength, however, the shear strength obtained from short-beam shear test was deteriorated by approximately 15%.
Gates TS and Zureick A-H. High temperature and environmental effects on polymeric composites (STP). Philadelphia, PA: American Society for Testing & Materials, 1998.
2.
Yu BaiTK. High temperature performance of polymer composites, 1st ed. Weinheim, Germany: Wiley-VCH Verlag GmbH & Co. KGaA, 2014.
3.
MouritzAGibsonA. Fire properties of polymer composite materials, 1st ed. Dordrecht, The Netherlands: Springer Netherlands, 2006.
4.
DeMeuseM. High temperature polymer blends, Cambridge, UK: Woodhead Publishing in Materials, 2014.
5.
Beyler CL and Hirschler MM. Thermal decomposition of polymers. In: Hurley MJ, Gottuk DT, Hall JR, Jr, et al. (eds) SFPE handbook of fire protection engineering, 2001, pp.110–131.
6.
HergenrotherP. The use, design, synthesis, and properties of high performance/high temperature polymers: An overview. High Perform Polym2003; 15: 3–45.
7.
Mittal KL. Polymides and other high temperature polymers: Synthesis, characterization, and applications, Vol. 3. Leiden, The Netherlands: VSP, 2005.
McConnellVP. Resins for the Hot Zone, Part II: BMIs, CEs, benzoxazines and phthalonitriles. High-Perform Compos2009; 17: 1–6.
14.
Morgan RJ, Shin EE and Lincoln JE. Thermal properties of high temperature polymer matrix fibrous composites. In: Cheng S (ed.) Handbook of thermal analysis and calorimetry: Applications to polymers and plastics, vol. 3. 2002.
15.
Winters W and Serafini T. PRM polyimides-Processable high temperature composite matrix resins. NASA TM X-71676, NASA Lewis Research Center; Cleveland, OH, US, 1974.
16.
ChuangKCBowmanCLTsotisTKAC. 6F-Polyimides with phenylethynyl endcap for 315-370℃ applications. Perform Polym2003; 15: 459–472.
17.
Bain S, Ozawa H and Criss JM Jr. Mechanical properties of thermally aged peti-330 laminates fabricated by resin transfer molding. In: Proceedings of international SAMPE symposium and exhibition, Baltimore, MD, 2007, p.15.
18.
GuptaVAnandKGrapeJ. Failure of woven carbon–polyimide laminates under off-axis compression loading. Acta Mater1998; 46: 711–718.
19.
Connell JW, Smith JG and Hergenrother PM. High temperature transfer molding resins: Status of PETI-298 and PETI-330. Hampton, VA: NASA Langley Research Center.
20.
ConnellJWSmithJGHergenrotherPMet al.High temperature transfer molding resins: Laminate properties of PETI-298 and PETI-330. High Perform Polym2003; 15: 375–394.
21.
Xiao-Su Y. Research, development and enhancement of high-performance polymer matrix composites for aerospace in China. In: 17th international conference on composite matererials (ICCM17). Jeju Island, South Korea, 2009.
22.
HicTac. High performance composites for demanding high temperature applications, Brussels, Belgium: CleanSky – Research and Technology Development Projects, 2012.
23.
Connell JW, Smith JG Jr and Hergenrother PM. High temperature transfer molding resins: Composite properties of PETI-330. In: Interantional SAMPE technical conference series, Covina, CA, 2003, pp.1076–1086.
24.
Nexam Chemical. NEXIMID® MHT-R Product Data Sheet. Lund, Sweden, 2016.
Fernberg P, Joffe R, Tsampas S, et al. Influence of post-cure on carbon fibre polyimide composites with glass transition temperatures above 400℃. In: 20th International conference on composite materials, Copenhagen, Denmark, 2015.
27.
Fernberg P. Fibre reinforced polyimide composites and structures manufactured with resin transfer moulding – Overview of procedures and properties Germany, 2016. In: 17th European conference on composite materials (ECCM17), Munich, 2016.
28.
Fernberg P, Gong G and Mannberg P. Processing and properties of new polyimide composites with high temperature ability. In: 16th European conference on composite materials (ECCM16), Seville, Spain, 2014.
29.
Fernberg P, Gong G and Mannberg P. Processing and properties of new polyimide composites with high temperature ability. In: 16th European conference on composite materials (ECCM16), Seville, Spain, 2014.
30.
FernbergSGongGMannbergPet al.Processing properties of a 6-FDA based phenylethynyl-terminated polyimide with 370 C-ability tailored for Resin Transfer Moulding. J Compos Mater2017.
31.
ASTM. Standard test method for tensile properties of polymer matrix composite materials, D 3039, 2007.
32.
Joffe R. Effects of test methods on measured compressive strength of polymer composites. In: 3rd Nordic meeting on Materials and Mechanics, Ålborg, Denmark, 2000.
33.
ASTM. Standard test method for short-beam strength of polymer matrix composite materials and their laminates, D 2344, 2006.
34.
ASTM. Standard test method for Mode I interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites, D 5528, 2007.
35.
ASTM. Standard test method for compressive properties of polymer matrix composite materials with unsupported gage section by shear loading, D3410, 2003.
36.
BrandtF. New load introduction concept for improved and simplified delamination beam testing. Exp Tech1998; 22: 17–20.
37.
Tsampas S, Fernberg P and Joffe R. The effect of high temperature on the mechanical performance of novel high Tg polyimide-based carbon fibre-reinforced laminates. In: 17th European conference composite materials (ECCM17), Munich, Germany, 2016.
38.
GarcíaHM. Modeling fire behavior of a carbon fiber reinforced polyimide composite, Luleå, Sweden: Luleå University of Technology, 2015.
39.
Tsampas SA, Fernberg P and Joffe R. Mechanical performance of novel high Tg polyimide matrix carbon fibre reinforced laminates. In: 20th International Conference on Composite Materials, ICCM20, Copenhagen, Denmark, 2015.
40.
Connell JW, Smith JG and Hergenrother PM. High temperature transfer molding resins: Preliminary composite properties of PETI-375. In: SAMPE 2004 symposium and exhibition, Long Beach, CA, 2004.