In this study, in situ aluminum matrix composites were synthesized through pyrolysis of high temperature vulcanization silicone in commercially pure aluminum melt. For this purpose, 1 to 4 wt% of high temperature vulcanization silicone was added to a vortex of molten aluminum at 750℃ and the resulting slurries were cast in steel dies. Microstructure, hardness, and tensile properties of the as-cast samples were examined at ambient and high temperatures. The results revealed the in situ formation and distribution of reinforcement particles in the matrix. Energy-dispersive X-ray analysis indicated that the formed reinforcement particles consisted of O and Si elements. This confirms the in situ reinforcement formation by pyrolysis of high temperature vulcanization silicone in the melt. The size of the in situ formed particles was mostly in the range of 200–2000 nm. It was shown that the composites synthesized by the addition of 4 wt% high temperature vulcanization had the highest mechanical properties both at ambient and high temperatures. Room temperature hardness, tensile strength, and yield strength of this sample were increased by about 50%, 23%, and 19% compared to the monolithic sample, respectively.
ChawlaK. Composite materials, 3rd ed. New York-Heidelberg-Dordrecht-London: Springer, 2012.
2.
JagannathamMSankaranSHaridossP. Microstructure and mechanical behavior of copper coated multiwall carbon nanotubes reinforced aluminum composites. Mater Sci Eng A2015; 638: 197–207.
3.
KainerUK. Metal matrix composites: Custom-made materials for automotive and aerospace engineering, Weinheim: Wiley-VCH, 2006.
4.
YangXZouTShiCet al.Effect of carbon nanotube (CNT) content on the properties of in-situ synthesis CNT reinforced Al composites. Mater Sci Eng A2016; 660: 11–18.
5.
MiracleDB. Metal matrix composites – From science to technological significance. Compos Sci Technol2005; 65: 2526–2540.
6.
OzdemirIAhrensSMucklichS. Nanocrystalline Al–Al2O3p and SiCp composites produced by high-energy ball milling. J Mater Process Technol2008; 205: 111–118.
7.
ChenFChenZMaoFet al.TiB2 reinforced aluminum based in situ composites fabricated by stir casting. Mater Sci Eng A2015; 625: 357–368.
8.
SharifiEKarimzadehFEnayatiMH. Fabrication of aluminum matrix hybrid nanocomposite by mechanical milling. Int J Mod Phys B2009; 23: 4825–4832.
9.
ZhangQLiuYGuoB. Cyclic compressive creep-elastoplastic behaviors of in situ TiB2/Al-reinforced composite. Mater Sci Eng A2016; 666: 1–9.
10.
GasemZAliS. Low-cycle fatigue behavior of powder metallurgy 6061 aluminum alloy reinforced with submicron-scale Al2O3 particles. Mater Sci Eng A2016; 562: 109–117.
11.
ZhangLWangJWangHet al.Microstructures and mechanical properties of the Al2014 composites reinforced with bimodal sized SiC particles. Mater Sci Eng A2016; 637: 70–74.
12.
HuQZhaoHGeJ. Microstructure and mechanical properties of (B4C+Al3Ti)/Al hybrid composites fabricated by a two-step stir casting process. Mater Sci Eng A2016; 650: 478–482.
13.
WangX. Microstructure and mechanical properties of SiCp/MgZnCa composites fabricated by stir casting. Mater Sci Eng A2012; 534: 60–67.
14.
The composite materials handbook. Vol. 4, Metal matrix composite. Materials Park, OH: ASM International, 2002.
15.
KobashiMChohT. The wettability and the reaction for SiC particle/Al alloy system. Mater Sci1993; 28: 684–690.
16.
SajjadiSAEzatpourHRBeygiH. Microstructure and mechanical properties of Al–Al2O3 micro and nano composites fabricated by stir casting. Mater Sci Eng A2011; 528: 8765–8771.
17.
HashimJLooneyLHashmiMSJ. Particle distribution in cast metal matrix composites - Part I. J Mater Process Technol2002; 123: 251–257.
18.
ShayanMNiroumandB. Synthesis of A356 MWCNT nanocomposites through a novel two stage casting process. Mater Sci Eng A2013; 582: 262–269.
19.
GhahremanianMNiroumandB. Compocasting of an Al-Si-SiCp composite using powder injection method. Solid State Phenom2008; 141: 175–180.
20.
AbasipourBNiroumandBMonir VaghefiM. Compocasting of A356-CNT composite. Trans Nonferrous Met Soc China2010; 20: 1561–1566.
21.
AmirkhanlouSNiroumandB. Synthesis and characterization of 356-SiCp composites by stir casting and compocasting methods. Trans Nonferrous Met Soc China2010; 20: 788–793.
22.
MalekiAMeratianMNiroumandBet al.Synthesis of in situ aluminum matrix composite using a new activated powder injection method. Metall Mater Trans A2008; 39: 3034–3039.
23.
ReddyBSBDasKDasS. A review on the synthesis of in situ aluminum based composites by thermal, mechanical and mechanical-thermal activation of chemical reactions. Mater Sci2007; 42: 9366–9378.
24.
TjongSCMaZY. Microstructural and mechanical characteristics of in situ metal matrix composites. Mater Sci Eng R2000; 29: 49–113.
25.
RameshCSAhamedA. Friction and wear behaviour of cast Al 6063 based in situ metal matrix composites. Wear2011; 271: 1928–1939.
26.
SudarshanSurappaMKDongjoonAHNet al.Nanoceramic metal matrix composites by in-situ pyrolysis of organic precursors in a liquid melt. Metall Mater Trans A2008; 39: 3291–3297.
27.
CastellanEIschiaGMolinariAet al.A novel in situ method for producing a dispersion of a ceramic phase into copper that remains stable at 0.9Tm. Metall Mater Trans A2013; 44: 4734–4742.
28.
SenemarMMalekiANiroumandBet al.A novel and facile method for silica nanoparticles synthesis from high temperature vulcanization (HTV) silicon. Metall Mater2016; 22: 1–8.
29.
SaadatiMRMalekiANiroumandBet al.A novel low cost method for the synthesis of ceramic nano silicon oxycarbide powder. Ceram Int2016; 42: 8531–8536.
30.
DodiukHGoodmanSH. Handbook of thermoset plastics, 3rd ed. New York: William Andrew, 2014.
31.
ASTM E10-01. Standard test method for Brinell hardness of metallic materials, West Conshohocken, PA: ASTM International, 2004.
32.
ASTM E8-04. Standard test methods for tension testing of metallic materials, West Conshohocken, PA: ASTM International, 2004.
33.
AmirkhanlouSNiroumandB. Microstructure and mechanical properties of Al356/SiCp cast composites fabricated by a novel technique. J Mater Eng Perform2013; 22: 85–93.
34.
Chawla K and Chawala N. Metal matrix composites. An Oxford-Kobe Materials Text, New York: Springer, 2006.
35.
Issa H. Development of Al-Al/(SiO2)np composite by powder in tube method. Master Dissertation, Isfahan University of Technology, Iran, 2016.
36.
KapoorRKennethS. Deformation behavior and failure mechanisms in particulate reinforced 6061 Al metal-matrix composites. Mater Sci Eng A1995; 202: 63–75.
37.
MazaheryAOstad ShabaniM. Characterization of cast A356 alloy reinforced nano SiC composites. Trans Nonferrous Met Soc China2012; 22: 275–280.
38.
RazaghianAChandeaT. Fraction behavior of SiC particles reinforced aluminum alloy at high temperature. Compos Sci Technol2004; 36: 293–298.