The behavior of a woven E-glass–Vinylester composite in dry and seawater-saturated conditions was investigated for strain rates in the range of 0.001–100 s−1. Reliable data were obtained by conducting servo-hydraulic tests at high speed with DIC strain measurement. Issues related to inertial effects of the test system and controlling vibrational stress waves were resolved through a unique experimental setup and special attention to specimen geometry and fixturing. In addition, a rate-dependent constitutive model was adapted to characterize the elastic–viscoplastic response at various strain rates and validated by comparison to test data. The subject investigation demonstrates a viable methodology to identify strain rate sensitivities in high speed experiments and develop a representative material model for analysis of high rate phenomena.
HsiaoHMDanielIM. Strain rate behavior of composite materials. Compos Part B1998; 29B: 521–533.
3.
PardoSBaptisteDDécobertFet al.Tensile dynamic behaviour of a quasi-unidirectonal E-glass/polyester composite. Compos Sci Technol2002; 62: 579–584.
4.
FitoussiJMeraghniFJendliZet al.Experimental methodology for high strain-rates tensile behaviour analysis of polymer matrix composites. Compos Sci Technol2005; 65: 2174–2188.
5.
OkoliOI. The effects of strain rate and failure modes on the failure energy of fibre reinforced composites. Compos Struct2001; 54: 299–303.
6.
BrownKABrooksRWarriorNA. The static and high strain rate behaviour of a commingled E-glass/polypropylene woven fabric composite. Compos Sci Technol2010; 70: 272–283.
7.
BingQSunCT. Modeling and testing strain rate-dependent compressive strength of carbon/epoxy composites. Compos Sci Technol2005; 65: 2481–2491.
8.
KhanA.SColakOUCentalaP. Compressive failure strengths and modes of woven S2-glass reinforced polyester due to quasi-static and dynamic loading. Int J Plast2002; 18: 1337–1357.
9.
NinanLTsaiJSunCT. Use of split Hopkinson pressure bar for testing off-axis composites. Int J Impact Eng2001; 25: 291–313.
10.
OcholaROMarcusKNurickGNet al.Mechanical behaviour of glass and carbon fibre reinforced composites at varying strain rates. Compos Struct2004; 63: 455–467.
11.
RavikumarGPothnisJRJoshiMet al.Analytical and experimental studies on mechanical behavior of composites under high strain rate compressive loading. Mater Des2013; 44: 246–255.
GerlachRSiviourCRWiegandJet al.In-plane and through-thickness properties, failure modes, damage and delamination in 3D woven carbon fibre composites subjected to impact loading. Compos Sci Technol2001; 72: 397–411.
14.
GilatAGoldbergRKRobertsGD. Experimental study of strain-rate-dependent behavior of carbon/epoxy composite. Compos Sci Technol2002; 62: 1469–1476.
ShimVPWLimCTFooKJ. Dynamic mechanical properties of fabric armour. Int J Impact Eng2001; 25: 1–15.
17.
FitoussiJBocquetMMeraghniF. Effect of the matrix behavior on the damage of Ethylene-Propylene glass fiber reinforced composite subjected to high strain rate tension. Compos Part B2013; 45: 1181–1191.
18.
ShokriehMMOmidiMJ. Tension behavior of unidirectional glass/epoxy composites under different strain rates. Compos Struct2009; 88: 595–601.
19.
TodoMTakahashiKBéguelinPet al.Strain-rate dependence of the tensile fracture behaviour of woven-cloth reinforced polyamide composites. Compos Sci Technol2000; 60: 763–771.
20.
WangWMakarovGShenoiRA. An analytical model for assessing strain rate sensitivity of unidirectional composite laminates. Compos Struct2005; 69: 45–54.
21.
OkoliOISmithGF. The effect of strain rate and fibre content on the Poisson’s ratio of glass/epoxy composites. Compos Struct2000; 48: 157–161.
22.
OkoliOIAbdul-LatifA. Failure in composite laminates: overview of an attempt at prediction. Compos Part A2002; 33: 315–321.
23.
Shah KhanMZSimpsonG. Mechanical properties of a glass reinforced plastic naval composite material under increasing compressive strain rates. Mater Lett2000; 45: 167–174.
24.
HouJPRuizC. Measurement of the properties of woven CFRP T300/914 at different strain rates. Compos Sci Technol2000; 60: 2829–2834.
25.
SuttonMAOrteuJJSchreierH. Image correlation for shape, motion and deformation measurements: basic concepts, theory and applications, New York, NY: Springer, 2009.
26.
LagattuFBrillaudJLafarie-FrenotMC. High strain gradient measurements by using digital image correlation technique. Mater Characteriz2004; 53: 17–28.
27.
GodaraARaabeD. Influence of fiber orientation on the global mechanical behavior and mesoscale strain localization in a short glass-fiber-reinforced epoxy polymer composite during tensile deformation investigated using digital image correlation. Compos Sci Technol2007; 67: 2417–2427.
28.
LevequeDHuchetteCPaulmierPet al.Displacement field measurements and capitalizing on experience: Application to the analysis of the rupture of holed composite plates. Compos Sci Technol2009; 69: 67–72.
29.
LomovSVIvanovDSVerpoestIet al.Full-field strain measurements for validation of meso-FE analysis of textile composites. Compos Part A2008; 39: 1218–1231.
30.
De AlmeidaOLagattuFBrillaudJ. Analysis by a 3D DIC technique of volumetric deformation gradients: application to polypropylene/EPR/talc composites. Compos Part A2008; 39: 1210–1217.
31.
HufnerDRXingLAccorsiML. Failure assessment of a woven E-glass/vinyl ester composite subjected to large deformation loading. Sci Eng Compos Mater2012; 19: 183–193.
32.
WeitsmanYJ. Fluid effects in polymers and polymeric composites, New York, NY: Springer, 2012.
33.
RheeKYKimHJParkSJ. Effect of strain rate on the compressive properties of graphite/epoxy composite in a submarine environment. Compos Part B2006; 37: 21–25.
34.
KarbhariVMWangQ. Multi-frequency dynamic mechanical thermal analysis of moisture uptake in E-glass/vinylester composites. Compos Part B2004; 35: 299–304.
35.
SunCTChenJL. A simple flow rule for characterizing nonlinear behavior of fiber composites. J Compos Mater1989; 23: 1009–1020.
36.
ThiruppukuzhiSVSunCT. Models for the strain-rate-dependent behavior of polymer composites. Compos Sci Technol2001; 61: 1–12.
SunCTYoonKJ. Characterization of elastic-plastic behavior of AS4/PEEK thermoplastic composite for temperature variation. J Compos Mater1991; 25: 1297–1313.
39.
TsaiJSunCT. Constitutive model for high strain rate response of polymeric composites. Compos Sci Technol2002; 62: 1289–1297.
40.
OgiharaSReifsniderKL. Characterization of nonlinear behavior in woven composite laminates. Appl Compos Mater2002; 9: 249–263.
41.
HufnerDRAccorsiML. A progressive failure theory for woven polymer-based composites subjected to dynamic loading. Compos Struct2009; 89: 177–185.
42.
ReifsniderKLXingL. Large-deformation constitutive theories for structural composites: rate-dependent concepts and effect of microstructure. Strain2007; 44: 119–125.
43.
XingLReifsniderKLHuangX. Progressive damage modeling for large deformation loading of composite structures. Compos Sci Technol2009; 69: 780–784.
44.
OdegardGSearlesKKumosaM. Nonlinear analysis of woven fabric-reinforced graphite/PMR-15 composites under shear-dominated biaxial loads. J Compos Mater2000; 7: 129–152.
45.
SAE J2749. Surface vehicle recommended practice – high strain rate tensile testing of polymers. SAE International, 400 Commonwealth Drive, Warrendale, PA, 15096–15096.
46.
SEP 1230. The determination of the mechanical properties of sheet metal at high strain rates in high-speed tensile tests, STAHL-EISEN-Prüfblättep (SEP) des Stahlinstituts VDEh, Verlag Stahleisen GmbH, Postfach 10 51 64, 40042 Düsseldorf, Germany.
47.
ASTM D 3039. Standard test method for tensile properties of polymer matrix composite materials. ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA, 19428–2959–19428–2959.
48.
ASTM D695. Standard test method for compressive properties of rigid plastics. ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA, 19428–2959–19428–2959.
49.
ASTM E111. Standard test method for Young’s modulus, tangent modulus, and chord modulus. ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA, 19428–2959–19428–2959.
50.
RyouHChungKYuWR. Constitutive modeling of woven composites considering asymmetric/anisotropic, rate dependent, and nonlinear behavior. Compos Part A2007; 38: 2500–2510.
51.
MatsudaTNimiyaYOhnoNet al.Elastic–viscoplastic behavior of plain-woven GFRP laminates: Homogenization using a reduced domain of analysis. Compos Struct2007; 79: 493–500.
52.
XiaYYuanJYangB. A statistical model and experimental study of the strain-rate dependence of the strength of fibres. Compos Sci Technol1994; 52: 499–504.
53.
WangXXiaY. Experimental evaluation of the strength distribution of fibers under high strain rates by bimodal Weibull distribution. Compos Sci Technol1997; 57: 1599–1607.