An energy-based continuum damage mechanics model was employed to investigate the effect of drilling-induced delamination on tensile strength of carbon fiber-reinforced polymer laminates and the residual strength was predicted. The decrease in tensile strength caused by delamination was investigated in detail by a finite element method (FEM) model. Experiments were also conducted to validate the numerical results. The drilling-induced delamination was measured with ultrasonic C-scan technique and modeled as deletions of corresponding cohesive elements in the FEM model. Different sizes of delamination zones were investigated and the predicted strengths were compared with experimental results. The FEM model showed that the decrease in strength is mainly caused by early failures of outer plies. Good correlation between numerical simulations and experimental results was also obtained.
Nilsson S, Bredberg A and Asp L. Size effects on strength of notched cfrp laminates loaded in bending. In: ICCM-17, Edinburgh, Scotland, 2009.
2.
ShyhaISooSLAspinwallD. Effect of laminate configuration and feed rate on cutting performance when drilling holes in carbon fibre reinforced plastic composites. J Mater Process Tech2010; 210: 1023–1034.
3.
PerssonEErikssonIZackrissonL. Effects of hole machining defects on strength and fatigue life of composite laminates. Compos Part A: Appl Sci Manuf1997; 28: 141–151.
4.
ZitouneRCrouzeixLCollombetF. Behaviour of composite plates with drilled and moulded hole under tensile load. Compos Struct2011; 93: 2384–2391.
5.
Wong T, Wu S and Croy G. An analysis of delamination in drilling composite materials. In: 14th national SAMPE technical conference, Atlanta, Georgia, 1982, pp. 1–483.
Davim JP. Drilling of composite materials. Hauppauge, New York, NY: NOVA Publishers, 2009.
8.
Krishnaraj V, Zitoune R and Davim JP. Drilling of polymer-matrix composites. Berlin, Heidelberg, Germany: Springer, 2013.
9.
TetiR. Machining of composite materials. Cirp Ann-Manuf Techn2002; 51: 611–634.
10.
HochengHTsaoCC. The path towards delamination-free drilling of composite materials. J Mater Process Tech2005; 167: 251–264.
11.
LiuDFTangYJCongWL. A review of mechanical drilling for composite laminates. Compos Struct2012; 94: 1265–1279.
12.
HochengHTsaoCC. Effects of special drill bits on drilling-induced delamination of composite materials. Int J Mach Tool Manuf2006; 46: 1403–1416.
13.
PiquetRFerretBLachaudF. Experimental analysis of drilling damage in thin carbon/epoxy plate using special drills. Compos Part A-Appl Sci2000; 31: 1107–1115.
14.
TsaoCC. Experimental study of drilling composite materials with step-core drill. Mater Design2008; 29: 1740–1744.
15.
AbraoAMRubioJCCFariaPE. The effect of cutting tool geometry on thrust force and delamination when drilling glass fibre reinforced plastic composite. Mater Des2008; 29: 508–513.
16.
RakeshPKSinghIKumarD. Drilling of composite laminates with solid and hollow drill point geometries. J Compos Mater2012; 46: 3173–3180.
17.
SardinasRQReisPDavimJP. Multi-objective optimization of cutting parameters for drilling laminate composite materials by using genetic algorithms. Compos Sci Technol2006; 66: 3083–3088.
18.
DavimJPReisP. Drilling carbon fiber reinforced plastics manufactured by autoclave—experimental and statistical study. Mater Des2003; 24: 315–324.
19.
KilickapE. Optimization of cutting parameters on delamination based on Taguchi method during drilling of GFRP composite. Expert Syst Appl2010; 37: 6116–6122.
20.
GaitondeVNKarnikSRRubioJC. Analysis of parametric influence on delamination in high-speed drilling of carbon fiber reinforced plastic composites. J Mater Process Tech2008; 203: 431–438.
21.
RubioJCAbraoAMFariaPE. Effects of high speed in the drilling of glass fibre reinforced plastic: Evaluation of the delamination factor. Int J Mach Tool Manuf2008; 48: 715–720.
22.
PalanikumarKRubioJCAbraoAM. Influence of drill point angle in high speed drilling of glass fiber reinforced plastics. J Compos Mater2008; 42: 2585–2597.
23.
PhadnisVAMakhdumFRoyA. Drilling in carbon/epoxy composites: experimental investigations and finite element implementation. Compos Part A-Appl Sci2013; 47: 41–51.
24.
IsbilirOGhassemiehE. Numerical investigation of the effects of drill geometry on drilling induced delamination of carbon fiber reinforced composites. Compos Struct2013; 105: 126–133.
25.
DavimJPRubioJCAbraoAM. A novel approach based on digital image analysis to evaluate the delamination factor after drilling composite laminates. Compos Sci Technol2007; 67: 1939–1945.
26.
GreenBGWisnomMRHallettSR. An experimental investigation into the tensile strength scaling of notched composites. Compos Part A-Appl Sci2007; 38: 867–878.
27.
PinhoSTIannucciLRobinsonP. Physically based failure models and criteria for laminated fibre-reinforced composites with emphasis on fibre kinking. Part II: FE implementation. Compos Part A-Appl Sci2006; 37: 766–777.
28.
PinhoSTIannucciLRobinsonP. Physically-based failure models and criteria for laminated fibre-reinforced composites with emphasis on fibre kinking: part I: development. Compos Part A-Appl Sci2006; 37: 63–73.
29.
MaimiPCamanhoPPMayugoJA. A continuum damage model for composite laminates: part II - computational implementation and validation. Mech Mater2007; 39: 909–919.
30.
MaimiPCamanhoPPMayugoJA. A continuum damage model for composite laminates: part I - constitutive model. Mech Mater2007; 39: 897–908.
31.
ChenBYTayTEBaizPM. Numerical analysis of size effects on open-hole tensile composite laminates. Compos Part A-Appl Sci2013; 47: 52–62.
PuckASchurmannH. Failure analysis of FRP laminates by means of physically based phenomenological models. Compos Sci Technol2002; 62: 1633–1662.
34.
CamanhoPPDavilaCGPinhoST. Prediction of in situ strengths and matrix cracking in composites under transverse tension and in-plane shear. Compos Part A-Appl Sci2006; 37: 165–176.
35.
BenzeggaghMKenaneM. Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus. Compos Sci Technol1996; 56: 439–449.
36.
AlfanoGCrisfieldMA. Finite element interface models for the delamination analysis of laminated composites: mechanical and computational issues. Int J Numer Meth Eng2001; 50: 1701–1736.
37.
Camanho PP and Dávila CG. Mixed-mode decohesion finite elements for the simulation of delamination in composite materials. In: NASA-technical paper, Hampton, Virginia, 2002, paper no. 211737, p.33.
CamanhoPPDavilaCGde MouraMF. Numerical simulation of mixed-mode progressive delamination in composite materials. J Compos Mater2003; 37: 1415–1438.
40.
HuNZembaYOkabeT. A new cohesive model for simulating delamination propagation in composite laminates under transverse loads. Mech Mater2008; 40: 920–935.
41.
BažantZPOhBH. Crack band theory for fracture of concrete. Matériaux et construction1983; 16: 155–177.
42.
HarperPWHallettSR. Cohesive zone length in numerical simulations of composite delamination. Eng Fract Mech2008; 75: 4774–4792.
43.
Nixon-PearsonOJHallettSR. An investigation into the damage development and residual strengths of open-hole specimens in fatigue. Compos Part A-Appl Sci2015; 69: 266–278.