Multifunctional hybrid composites are proposed as novel solutions to meet the demands in various industrial applications ranging from aerospace to biomedicine. The combination of carbon fiber and/or fabric, metal foil, and carbon nanotubes is utilized to develop such composites. This study focuses on processing and fracture toughness characterization of the carbon fiber-reinforced polymer–matrix composites and the carbon nanotube modified interface between the polymer–matrix composite and titanium foil. Vacuum Assisted Resin Transfer Molding (VARTM) process is used to fabricate the laminate. Double cantilever beam tests at both room temperature and high temperature are conducted to assess the mode I interlaminar fracture toughness. The experimental and characterization efforts suggest that carbon nanotubes improve bonding at the hybrid interface. Simple computational models are developed to assist the interpretation of experimental results and further investigate the damage modes. The numerical results agree well with the limited experiments at crack initiation and furthermore support the absence of mode mixity.
Alderliesten RC and Benedictus R. Fiber/metal composite technology for future primary aircraft structures. Journal of Aircraft 45(4): 1182–1189.
2.
VlotA. Impact loading on fibre metal laminates. Int J Impact Eng1996; 18(3): 291–307.
3.
Beumler T, Pellenkoft F, Tillich A, et al. Airbus costumer benefit from fiber metal laminates. Airbus Deutschland GmbH, Ref. no: L53PR0605135-Issue 1, 2006, pp.1–18.
4.
VogelesangLBVlotA. Development of fibre metal laminates for advanced aerospace structures. J Mater Process Technol2000; 103: 1–5.
5.
Vogelesang LB, Gunnink JW, Roebroeks GHJJ, et al. Towards the supportable and durable aircraft fuselage structure. In: Estimation, Enhancement and Control of Aircraft Fatigue Performance. ICAF 95(UK), 1, 1995, pp.257–271. Chameleon Press Ltd.
6.
AsundiAChoi AltaYN. Fiber metal laminates: An advanced material for future aircraft. J Mater Process Technology1997; 63: 384–394.
7.
AlderliestenR. On the development of hybrid material concepts for aircraft structures. Recent Pat Eng2009; 3: 25–38.
8.
BaldanA. Adhesion phenomena in bonded joints. Int J Adhes Adhes2012; 38: 95–116.
9.
FourcheG. An overview of the basic aspects of polymer adhesion. Part I: Fundamentals. Polym Eng Sci1995; 35(12): 957–967.
10.
BaldanA. Adhesively-bonded joints and repairs in metallic alloys, polymers and composite materials: Adhesives, adhesion theories and surface pretreatment. J Mater Sci2004; 39(1): 1–49.
11.
Gutowski TG, Zhong C, Wendy S, et al. The mechanics of composites deformation during manufacturing processes. In: American Society for Composites, First Technical Conference, 1986, pp.154–163.
AbdullahMRCantwellWJ. The impact resistance of polypropylene-based fibre–metal laminates. Compos Sci Technol2006; 66: 1682–1693.
14.
LangdonGSNurickGNCantwellWJ. The response of fibre metal laminate panels subjected to uniformly distributed blast loading. Eur J Mech A-Solid2008; 27: 107–115.
15.
KaragiozovaDLangdonGSNurickGN. Simulation of the response of fibre–metal laminates to localised blast loading. Int J Impact Eng2010; 37: 766–782.
16.
LangdonGSLemanskiSLNurickGN. Behaviour of fibre–metal laminates subjected to localised blast loading: Part I—experimental observations. Int J Impact Eng2007; 34: 1202–1222.
17.
LemanskiSLNurickGNLangdonGS. Understanding the behaviour of fibre metal laminates subjected to localised blast loading. Compos Struct2006; 76: 82–87.
18.
LangdonGSCantwellWJNurickGN. Localised blast loading of fibre metal laminates with a polyamide matrix. Compos Part B2007; 38: 902–913.
19.
LangdonGSCantwellWJNurickGN. The blast response of novel thermoplastic-based fibre–metal laminates—some preliminary results and observations. Compos Sci Technol2005; 65: 861–872.
20.
LemanskiSLNurickGNLangdonGS. Behaviour of fibre metal laminates subjected to localised blast loading—Part II: Quantitative analysis. Int J Impact Eng2007; 34: 1223–1245.
21.
SinmazçelikTEgemenAMustafaOB. A review: Fibre metal laminates, background, bonding types and applied test methods. Mater Des2011; 32(7): 3671–3685.
22.
AbelMLDigbyRPFletcherIW. Evidence of specific interaction between C-glycidoxypropyltrimethoxysilane and oxidized aluminium using high-mass resolution to F-SIMS. Surf Interface Anal2000; 29(2): 115–125.
23.
HobbsPMKinlochAJ. The computational molecular modelling of organosilane primers. J Adhes1998; 66: 203–228.
24.
BlohowiakKYAndersonRAGraceWBH. “TiGr” Laminates: Development of New Thin Adhesive Systems and Associated Test Methods. SAMPE Journal2009; 45(3): 30–36.
25.
WilliamsJGFracture mechanics of anisotropic materials. In: FriedrichK (ed). Application of fracture mechanics to composite materials, Amsterdam: Elsevier, 1989.
26.
Lafdi K, Harris R, and Memon MO. Aligned Carbon Nanotubes to Reduce Contact Thermal Impedance. Carbon 2011; 49(12): 3820–3828.
27.
Truong HTX. Processing, characterization and modeling carbon nanotube modified interfaces in hybrid polymer matrix composites. Master’s Thesis, Texas A&M University, TX, USA, 2012.
28.
Standard test method for mode I interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites. ASTM D 5528-01. Annual Book of ASTM Standards, 2007.
29.
HileyM. GARTEUR AG27 Fractographic Aspects of Fatigue Failure in Complex Laminates and Structures. GARTEUR Final Report TP-1512007.
30.
PurslowD. Matrix fractography of fibre-reinforced epoxy composites. Composites1986; 17(4): 289–303.
31.
GreenhalghES. Failure analysis and fractography of polymer composites, Cambridge: Woodhead Publishing, 2009.
32.
QiaoPWangJ. Mechanics and fracture of crack tip deformable bi-material interface. Int J Solids Struct2004; 41(26): 7423–7444.
33.
BennatiSColleluoriMCoriglianoD. An enhanced beam-theory model of the asymmetric double cantilever beam (ADCB) test for composite laminates. Compos Sci Technol2009; 69(11–12): 1735–1745.
34.
GereJ. Mechanics of materials, Belmont, CA: Thompson Learning, 2004.
35.
McLendon WR and Whitcomb JD. Characteristic Failure Initiation Sites in Plain Weave Textile Composites. Journal of Composite Materials 2012.