Fracture behaviour of SiC monofilament reinforced copper

Abstract

SiC monofilament-reinforced copper is a potential heat sink material for the divertor of future fusion reactors, where heat loads up to 15 MW/m² must be removed. The composite combines high mechanical strength (300 MPa at 300℃) with sufficient thermal conductivity (at least 200 W/mK) at temperatures up to 550℃. The bonding between fibres and matrix is essential for the mechanical behaviour. We investigated two different fibre types (SCS0 and SCS6, Specialty Materials Inc.) with different interlayers in a galvanic copper matrix. Tensile tests in combination with acoustic emission analysis showed the dependence of fracture behaviour of the composite material on the fibre type. The average ultimate tensile strength of composite samples with 20% fibre reinforcement was in the range of 600 MPa, with a Young's modulus of 160 GPa. The tensile tested composite with SCS6 fibres generated roughly twenty times the number of acoustic emission events in comparison with the SCS0 fibres composite. Acoustic emission events in tensile test specimens with SCS6 fibres are correlated with the failure of the carbon-enriched surface layer of the fibre. In the case of SCS0 fibre-reinforced specimens, acoustic emission events were only caused by fibre failure. Fracture area analysis after tensile tests showed the failure of the SCS6 fibres at the interface between the two outer carbon layers and no interface failure for the composite with SCS0 fibres.

Keywords

Metal-matrix composite fibre/matrix bond mechanical properties stress/strain curves acoustic emission

Get full access to this article

View all access options for this article.

References

You

Bolt

. Overall mechanical properties of fiber-reinforced metal matrix composites for fusion applications. J Nuclear Mater 2002; 305(1): 14–20.

You

J-H

. Design feasibility study of a divertor component reinforced with fibrous metal matrix composite laminate. J Nuclear Mater 2005; 336(1): 97–109.

Smith

. Heat treatment effects on SiC fiber. J Mater Sci 1998; 33(24): 5855–5872.

Brendel

. SiC-fibre reinforced copper as heat sink material for fusion applications. J Nuclear Mater 2004; 329–333(Part 1): 804–808.

Brendel

. Titanium as coupling agent in SiC fibre reinforced copper matrix composites. Mater Chem Phys 2005; 91(1): 116–123.

Brendel

. Interface modification of SiC-fibre/copper matrix composites by applying a titanium interlayer. Surf Coat Technol 2005; 200(1–4): 161–164.

Köck T. Herstellung und Charakterisierung eines SiC/Cu-Metall-Matrix-Verbundwerkstoffes mit angepasster Faser/Matrix-Grenzfläche. PhD Thesis, TU München, 2007.

Köck

Herrmann

Brendel

. Influence of different deposition parameters on the performance of a Ti-Ta-C interface layer in SiC-fiber reinforced copper matrix composites. Adv Mater Res 2008; 59: 138–142.

Brendel

. Mechanical properties of SiC long fibre reinforced copper. J Nuclear Mater 2009; 386–388: 837–840.

10.

Chawla

. Composite Materials, 2nd edn. New York: Springer-Verlag, 1998.

11.

Fukushima

. Effect of interfacial properties on tensile strength in SiC/Ti-15-3 composites. Mater Sci Eng A 2000; 276(1–2): 243–249.

12.

Kagawa

Fujita

Okura

. Temperature dependence of tensile mechanical properties in SiC fiber-reinforced Ti matrix composite. Acta Metall Mater 1994; 42(9): 3019–3026.

13.

Guo

Kagawa

Tanaka

. Microstructure and role of outermost coating for tensile strength of SiC fibre. Acta Mater 1998; 46: 4941–4954.

14.

Paffenholz V. Synthese und Charakterisierung von SiC_f/Cu-Matrix-Verbundwerkstoffen und ihre Anwendung in einem Modell einer Divertor-Komponente. PhD Thesis, TU München, 2010.

15.

Brendel

. Promising composite heat sink material for the divertor of future fusion reactors. J Nuclear Mater 2007; 367–370(Part 2): 1476–1480.

16.

Soboyejo

Rabeeh

. An investigation of the effects of microstructure on fatigue damage in a symmetric [0/90]2s silicon carbide (SCS6) fiber-reinforced titanium matrix composite. Mater Sci Eng A 1995; 200(1–2): 89–102.

17.

Bakuckas

Prosser

Johnsont

. Monitoring damage growth in titanium matrix composites using acoustic emission. J Compos Mater 1994; 28(4): 305–328.

Fracture behaviour of SiC monofilament reinforced copper – an acoustic emission study

Abstract

Keywords

Get full access to this article

References