Full-field displacement measurements between intralaminar cracks in cross-ply laminates were performed to evaluate the accuracy of shear lag models and Hashin’s model. The dependence of the average crack opening displacement on the crack density was measured and compared with model predictions. It was found that Hashin’s model overestimates the average COD by at least 25%. The value of the shear lag parameter was back-calculated by fitting. With the same goal the strain in the middle between two cracks was measured rendering shear lag parameter which was only 1% different. The found value does not agree with any of the used shear lag models. Measurement shows nonzero intralaminar shear zones in both layers covering a part of the ply thickness.
Talreja R. Damage characterization by internal variables. In: Talreja R (ed.) Damage mechanics of composite materials. Amsterdam: Elsevier, 1994; 53–78.
2.
NairnJAHuSBarkJS. A critical evaluation of theories for predicting microcracking in composite laminates. J Mater Sci1993; 28(18): 5099–5111.
3.
BerthelotJ-M. Transverse cracking and delamination in cross-ply glass-fiber and carbon-fiber reinforced plastic laminates: static and fatigue loading. Appl Mech Rev2003; 56(1): 111–147.
4.
LundmarkPVarnaJ. Constitutive relationships for laminates with ply cracks in in-plane loading. Int J Damage Mech2005; 14(3): 235–261.
5.
KashtalyanMSoutisC. Analysis of composite laminates with intra- and interlaminar damage. Prog Aerospace Sci2005; 41: 152–173.
6.
GarrettKWBaileyJE. Multiple transverse fracture in 90° cross-ply laminates of a glass fibre-reinforced polyester. J Mater Sci1977; 12(1): 157–168.
7.
MandersPWChouTWJonesRJRockJW. Statistical analysis of multiple fracture in 0°/90°/0° glass fibre/epoxy resin laminates. J Mater Sci1983; 18(10): 2876–2889.
8.
SmithPAWoodJR. Poisson’s ratio as a damage parameter in the static tensile loading of simple cross-ply laminates. Compos Sci Technol1990; vol. 38: 23–31.
9.
NuismerRJTanSC. Constitutive relations of a cracked composite lamina. J. Compos Mater1988; 22: 306–321.
10.
KashtalyanMSoutisC. Modelling stiffness degradation due to matrix cracking in angleply composite laminates. Plast Rubber Compos2000; 29(9): 482–488.
11.
ZhangJFanJSoutisC. Analysis of multiple matrix cracking in [±θm/90n]s composite laminates, Part I: in-plane stiffness properties. Composites1992; 23(5): 291–298.
12.
KashtalyanMSoutisC. Stiffness degradation in cross-ply laminates damaged by transverse cracking and splitting. Composites A2000; 31: 335–351.
13.
HashinZ. Analysis of cracked laminates: a variational approach. Mech Mater1985; 4(2): 121–136.
14.
VarnaJBerglundLA. Multiple transverse cracking and stiffness reduction in cross-ply laminates. J Compos Technol Res1991; 13(2): 97–106.
15.
KrasnikovsAVarnaJ. Transverse cracks in cross-ply laminates. Part 1. Stress analysis. Mech Compos Mater1997; 33(6): 565–582.
16.
JoffeRKrasnikovsAVarnaJ. COD-based simulation of transverse cracking and stiffness reduction in laminates. Compos Sci Technol2001; 61(5): 637–656.
KaterelosDTGKashtalyanMSoutisCGaliotisC. Matrix cracking in polymeric composite laminates: modeling and experiments. Compos Sci Technol2008; 68(12): 2310–2317.
19.
Rastogi PK. Measurement of static surface displacements, derivatives of displacements and 3D surface shapes - Examples of applications to nondestructive testing. In: Rastogi PK (ed.) Digital speckle pattern interferometry and related techniques. Chichester: John Wiley & Sons, 2001; 141–225.
Loukil M, Varna J and Ayadi Z. Applicability of solutions for periodic intralaminar crack distributions to non-uniformly damaged laminates, J Compos Mater 2011 (accepted).
22.
FargeLVarnaJAyadiZ. Damage characterization of a cross-ply carbon fiber/epoxy laminate by an optical measurement of the displacement field. Compos Sci Technol2010; 70(1): 94–101.
23.
PeterPWMChouT-W. On Cross-ply cracking in glass and carbon fibre reinforced epoxy laminates. Composites1987; 18: 40–46.
24.
ButtersJNLeendertzJA. A double exposure technique for speckle pattern interferometry. J Phys E: Scient Instrum1971; 4(4): 277–279.
25.
KashtalynMSoutisC. Analysis of local delaminations in composite laminates with angle-ply cracks. Int J Solids Struct2002; 39: 1515–1537.
26.
McCartneyLN. The prediction of cracking in biaxially loaded cross-ply laminates having brittle matrices. Composites1993; 24(2): 84–92.