In this work, stress curve and energy-based (linear elastic strain energy, and hysteresis loop energy) fatigue failure criteria are compared with a new, entropy-based model for the prediction of fatigue life in a woven glass/epoxy laminate. Extensive experimental results are reported that involve load-controlled tension–tension fatigue test with two different stress ratios as well as constant- and variable-loading of a woven glass/epoxy laminate with various load angles. The plot of fracture fatigue entropy vs. fatigue life is compared with the energy plotted vs. number of cycle and stress plotted vs. number of cycle (i.e., the so-called S–N curve) plots.
PetermannJPlumtreeA. A unified fatigue failure criterion for unidirectional laminates. Compos Part A Appl Sci Manufact2001; 32: 107–118.
2.
PlumtreeAChengGX. A fatigue damage parameter for off-axis unidirectional fiber reinforced composites. Int J Fatig1999; 21: 849–856.
3.
ShokriehMMTaheri-BehroozF. A unified fatigue life model based on energy method. Compos Struct2006; 75: 444–450–444–450.
4.
Varvani-FarahaniAHaftchenariHPanbechiM. An energy-based fatigue damage parameter for off-axis unidirectional FRP composites. Compos Struct2007; 79: 381–389.
5.
HashinZRotemR. A fatigue failure criterion for fiber reinforced materials. J Compos Mater1973; 7: 448464–448464.
6.
SimsDFBrogdonVH. Fatigue behavior of composites under different loading modes. In: ReifsniderKLLauraitisKN (eds). Fatigue of filamentary composite materials1977; 636, Philadelphia: ASTM, 185–205.
7.
RotemANelsonHG. Failure of a laminated composite under tension-compression fatigue loading. Compos Sci Technol1989; 36: 45–62.
8.
GoodmanJ. Mechanics applied to engineering1899Harlow: Longman Green.
9.
FawazZEllyinF. Fatigue failure model for fiber-reinforced materials under general loading conditions. JCompos Mater1994; 28: 1432–1451–1432–1451.
10.
KawaiM. A phenomenological model for off-axis fatigue behavior of unidirectional polymer matrix composites under different stress ratios. Compos Part A Appl Sci Manuf2004; 35: 955–963.
11.
HuangZM. Fatigue life prediction of a woven fabric composite subjected to biaxial cyclic loads. Compos Part A Appl Sci Manuf2002; 33: 253–266.
12.
OwenMJGriffithsJR. Evaluation of biaxial stress failure surfaces for a glass fabric reinforced polyester resin under static and fatigue loading. J Mater Sci1978; 13: 1521–1537.
13.
AmijimaSFujiiTHamaguchiM. Static and fatigue tests of a woven glass fabric composite under biaxial tension torsion loading. Composites1991; 22: 281–289.
14.
KhanRHKhanZAl-SulaimanFMerahN. Fatigue life estimates in woven carbon fabric/epoxy composites at non-ambient temperatures. J Compos Mater2002; 36: 2517–2535–2517–2535.
15.
EllyinFElkadiH. A fatigue failure criterion for fiber reinforced composite laminate. Compos Struct1990; 15: 61–74.
16.
ElkadiHEllyinF. Effect of stress ratio on the fatigue of unidirectional glass-fiber epoxy composite laminae. Composites1994; 25: 917–924.
17.
BryantMDKhonsariMMLingFF. On the thermodynamics of degradation. Proc R Soc A Math Phys Eng Sci2008; 464: 2001–2014.
18.
DoellingKLLingFFBryantMDHeilmanBP. An experimental study of the correlation between wear and entropy flow in machinery components. J Appl Phys2000; 88: 2999–3003.
19.
NaderiMAmiriMKhonsariMM. On the thermodynamic entropy of fatigue fracture. Proc R Soc A Math Phys Eng Sci2010; 466: 423–438.
20.
NaderiMKhonsariMM. A thermodynamic approach to fatigue damage accumulation under variable loading. Mater Sci Eng A Struct Mater Prop Microstruct Process2010; 527: 6133–6139.
21.
GiancaneSPanellaFWDattomaV. Characterization of fatigue damage in long fiber epoxy composite laminates. Int J Fatig2010; 32: 46–53.
22.
LemaîtreJChabocheJ-L. Mechanics of solid materials1990Cambridge: Cambridge University Press.
23.
NaderiMKhonsariMM. Real-time fatigue life monitoring based on thermodynamic entropy. Struct Health Monitor 2010; DOI: 10.1177/1475921710373295.
24.
MorrowJ. Cyclic plastic strain energy and fatigue of metals. ASTM STP1965; 378: 45–87.
25.
DasguptaAAgarwalRKBhandarkarSM. Three-dimensional modeling of woven-fabric composites for effective thermo-mechanical and thermal properties. Compos Sci Technol1996; 56: 209–223–209–223.