Bovine bone is burned at 400°C and the resulting ash is heat treated at 900°C for 90 min in order to obtain a white powder. Chemical analysis shows that this white powder is mainly hydroxyapatite (HA). Three different average particle sizes of this powder are produced by milling at three different times. The produced HA is surface treated with a silane coupling agent. Composite samples with 40% (by volume) of HA are produced by hot press molding, followed by mechanical testing in air and in Ringer’s solution. The results show that by increasing the molecular weight of polypropylene (PP), the creep strain of composites decreases proportionally, and the ultimate tensile strength (UTS) and impact resistance increase dramatically. In addition, the effect of testing in Ringer’s solution is to decrease UTS, creep, and impact properties of PP-HA composites. Furthermore, by decreasing the HA particle size, the creep strain decreases, while the UTS and impact resistance increase for the composites tested in air. Vice versa, in a wet condition decreasing of HA particle size causes UTS, creep, and impact resistance to fall. Fracture surfaces of the samples after impact tests are analyzed by a scanning electron microscope.
Yang, K., Yang, Q., Li, G., Sun, Y. and Feng, D. ( 2006). Morphology and Mechanical Properties of Polypropylene/Calcium Carbonate Nanocomposites, Materials Letters, 60: 805-809.
2.
Hou, M. and Friedrich, K. ( 1998). Adjustable Forming of Thermoplastic Composites for Orthopaedic Applications, Journal of Materials Science: Materials in Medicine , 9: 83-88.
3.
Latour Jr, R.A. and Black, J. (1992). Development of FRP Composite Structural Biomaterials: Ultimate Strength of the Fiber/Matrix Interfacial Bond in in vivo Simulated Environments, Journal of Biomedical Materials Research, 26: 593-606.
4.
Gao, X., Mao, L., Tian, M., Zhang, L. and Jin, R. ( 2006). Polycarbonate/Polypropylene/ Fibrillar Silicate Ternary Nanocomposites: Morphology and Mechanical Properties, Journal of Materials Science and Technology, 22: 87-92.
5.
Tong, X., Chen, Y. and Cheng, H. ( 2005). Influence of Carbon Nanofiber Addition on Mechanical Properties and Crystallization Behavior of Polypropylene, Journal of Materials Science and Technology, 21: 686-690.
6.
Chan, C.M., Wu, J.S., Li, J.X. and Ying-Kit, C. ( 2002). Polypropylene/Calcium Carbonate Nanocomposites , Polymer, 43: 2981-2992.
7.
Zuiderduin, W.C.J., Westzaan, C., Huetink , J. and Gaymans, R.J. (2003). Toughening of Polypropylene with Calcium Carbonate Particles, Polymer, 44: 261-275.
8.
Meng, M.R. and Dou, Q. ( 2008). Effect of Pimelic Acid on the Crystallization, Morphology and Mechanical Properties of Polypropylene/Wollastonite Composites , Materials and Engineering A, 492: 177-184.
9.
Bledzki, A.K. and Faruk, O. (2004). Creep and Impact Properties of Wood Fibre-Polypropylene Composites: Influence of Temperature and Moisture Content, Composites Science and Technology, 64: 693-700.
10.
Greco, A., Musardo, C. and Maffezzoli, A. ( 2007). Flexural Creep Behaviour of PP Matrix Woven Composite , Composites Science and Technology, 67: 1148-1158.
11.
Toro, P., Quijada, R., Yazdani-Pedram, M. and Arias, J.L. ( 2007). Eggshell, a New Bio-Filler for Polypropylene Composites , Materials Letters, 61: 4347-4350.
12.
Bonfield, W. , Grynpas, M., Tully , A.E., Bowman, J. and Abram, J. (1981). Hydroxyapatite Reinforced Polyethylene: A Mechanically Compatible Implant Materials for Bone-Replacement , Biomaterials, 2(3): 185-186.
13.
Wang, M., Deb, S. and Bonfield, W. ( 2000). Chemically Coupled Hydroxyapatite-Polyethylene Composites: Processing and Characterization, Materials Letters , 44: 119-124.
14.
Bonner, M., Ward, I.M., McGregor, W., Tanner, K.E. and Bonfield, W. ( 2001). Hydroxyapatite/Polypropylene Composite: A Novel Bone Substitute Material, Journal of Materials Science Letters , 20: 2049-2051.
15.
Fang, L., Leng, Y. and Gao, P. ( 2005). Processing of Hydroxyapatite Reinforced Ultrahigh Molecular Weight Polyethylene for Biomedical Applications, Biomaterials , 26: 3471-3478.
16.
Fang, L., Gao, P. and Leng, Y. ( 2007). High Strength and Bioactive Hydroxyapatite NanoParticles Reinforced Ultrahigh Molecular Weight Polyethylene, Composites B, 38: 345-351.
17.
Wen, J. , Li, Y., Zuo, Y., Zhou, G., Li, J., Jiang, L. and Xu, W. ( 2008). Preparation and Characterization of Nano-Hydroxyapatite/Silicone Rubber Composite, Materials Letters, 62: 3307-3309.
18.
Todo, M., Park, S.D., Arakawa, K. and Takenoshita, Y. ( 2006). Relation Between Microstructure and Fracture Behavior of Bioabsorbable HA/PLLA Composites, Composites A, 37: 2221-2225.
19.
Yi, Z., Yubao, L., Jidong, L., Xiang, Z., Hongbing, L., Yuanyuan, W. and Weihu, Y. ( 2007). Novel Bio-Composite of Hydroxyapatite Reinforced Polyamide and Polyethylene: Composition and Properties, Materials Science and Engineering A, 512: 452-453.
20.
Suwanprateeb, J., Tanner, K.E., Turner, S. and Bonfield, W. (1995). Creep in Polyethylene and Hydroxyapatite Reinforced Polyethylene Composites , Journal of Materials Science: Materials in Medicine, 6: 804-807.
21.
Suwanprateeb, J., Tanner, K.E., Turner, S. and Bonfield, W. (1997). Influence of Ringer’s solution on Creep Resistance of Hydroxyapatite Reinforced Polyethylene Composites , Journal of Materials Science: Materials in Medicine, 8: 469-472.
22.
Suwanprateeb, J., Tanner, K.E., Turner, S. and Bonfield, W. (1998). Influence of Sterilization by Gamma Irradiation and of Thermal Annealing on Creep of Hydroxyapatite-Reinforced Polyethylene Composites, Journal of Biomedical Materials Research , 39: 16-22.
23.
Bahrololoom, M.E., Javidi, M., Javadpour , S. and Ma , J. (2009). Characterization of Natural HA Extracted from Bovine Cortical Bone Ash, Journal of Ceramic Processing Research, 10(2): 129-138.
24.
Bertazzo, S. and Bertran, C.A. (2008). Effect of Hydrazine Deproteination on Bone Mineral Phase: A Critical View, Journal of Inorganic Biochemistry, 102: 137-145.
25.
Koutsopoulos, S. (2002). Synthesis and Characterization of Hydroxyapatite Crystals: A Review Study on the Analytical Methods, Journal of Biomedical Materials Research, 62: 600-612.
26.
Lin, F.H. , Liao, C.J., Chen, K.S. and Sun , J.S. (1998). Preparation of High-Temperature Stabilized β-Tricalcium Phosphate by Heating Deficient Hydroxyapatite with Na4P2O7·10H2O Addition, Biomaterials, 19: 1101-1107.
27.
Roger, R. ( 1995). Particulate-filled Polymer Composites, Longman Scientific and Technical Group, Essex, UK.
28.
Lawrence, E.N. and Robert, F.L. (1994). Mechanical Properties of Polymers and Composites, 2nd edn, Marcel Dekker, New York.
29.
Homaeigohar, S.S.H., Yari Sadi, A., Javadpour , J. and Khavandi, A. (2006). The Effect of Reinforcement Volume Fraction and Particle Size on the Mechanical Properties of β-Tricalcium Phosphate-High Density Polyethylene Composites , Journal of the European Ceramic Society, 26: 273-278.
30.
Zhang, Q., Tian, M., Wu, Y., Lin, G. and Zhang, L. ( 2004). Effect of Particle Size on the Properties of Mg (OH)2-Filled Rubber Composites, Journal of Applied Polymer Science, 94: 2341-2346.
31.
Lazzeri, A. , Thio, Y.S. and Cohen, R.E. (2004). Volume Strain Measurements on CaCO3/ Polypropylene Particulate Composites: The Effect of Particle Size , Journal of Applied Polymer Science, 91: 925-935.
32.
Suprapakorn, N. and Dhamrongvaraporn , S.S. (1998). Effect of CaCO3 on the Mechanical and Rheological Properties of a Ring-Opening Phenolic Resin: Polybenzoxazine, Polymer Composites, 19: 126-132.
33.
Singh, R.P. , Zhang, M. and Chan, D. (2002). Toughening of a Brittle Thermosetting Polymer: Effects of Reinforcement Particle Size and Volume Fraction , Journal of Materials Science, 37: 781-788.
34.
ASTM D2990-01. (2001 ). Standard Test Methods for Tensile, Compressive, and Flexural Creep and Creep Rupture of Plastics, ASTM International , West Conshohocken, PA, USA.
35.
Zhang, Z., Yang, J.L. and Friedrich, K. ( 2004). Creep Resistant Polymeric Nanocomposites, Polymer, 45: 3481-3485.
36.
Starkova, O. , Jing-Lei, Y. and Zhong, Z. ( 2007). Application of Time-Stress Superposition to Nonlinear Creep of Polyamide 66 Filled With Nanoparticles of Various Sizes, Composites, Science and Technology, 67: 2691-2698.
37.
Zhang, Y. and Tanner, K.E. ( 2003). Impact Behavior of Hydroxyapatite Reinforced Polyethylene Composites, Journal of Materials Science: Materials in Medicine , 14: 63-68.
38.
Kambour, R.P. (1964). Refractive Indices and Compositions of Crazes in Several Glassy Polymers, Journal of Polymer Science Part A, 2: 4159-4163.
39.
Kambour, R.P. (1965). Mechanism of Fracture in Glassy Polymers. I. Fracture Surfaces in Polymethyl Methacrylate, Journal of Polymer Science Part A, 3: 1713-1724.
40.
Wellinghof, S. and Baer, E. (1975). The Mechanism of Crazing in Polystyrene, Journal of Macromolecular Science: Physics , B11: 367-387.
41.
Freidrich, K. and Karsch, U.A. (1981). Failure Processes in Particulate Reinforced Polypropylene, Journal of Materials Science, 16: 2167-2175.
42.
Donald, A.M. and Kramer, E.J. ( 1982). Internal Structure of Rubber Particles and Craze BreakDown in High-Impact Polystyrene (HIPS) , Journal of Materials Science , 17: 2351-2358.
43.
Fu, S.Y. , Feng, X.Y., Lauke, B. and Mai, Y.W. ( 2008). Effects of Particle Size, Particle/Matrix Interface Adhesion and Particle Loading on Mechanical Properties of Particulate-Polymer Composites , Composites Part B, 39: 933-961.
44.
Lauke, B. ( 2008). On the Effect of Particle Size on Fracture Toughness of Polymer Composites, Composites Science and Technology, 68: 3365-3372.