Water sorption (WS), mechanical strength, and ion release of polymeric composites formulated with 40% as-made or milled amorphous calcium phosphate (ACP) are compared after 1, 2 and 3 months of aqueous exposure. Ethoxylated bisphenol A dimethacrylate, triethylene glycol dimethacrylate, 2-hydroxyethyl methacrylate, and methacryloxyethyl phthalate comprised the resin. The WS (mass%) peaked at 3 months. WS of as-made ACP composites was significantly higher than WS of milled ACP composites and copolymers. Both composite groups experienced decreases in biaxial flexural strength (BFS) with water aging, with milled ACP composites retaining a significantly higher BFS throughout immersion. Ion release was moderately reduced in milled ACP composites, though they remained superior to as-made ACP composites due to significantly lower WS and higher BFS after prolonged aqueous exposure.
Skrtic, D., Hailer, A.W., Takagi, S., Antonucci, J.M. and Eanes, E.D. (1996). Quantitative Assessment of the Efficacy of Amorphous Calcium Phosphate/Methacrylate Composites in Remineralizing Caries-like Lesions Artificially Produced in Bovine Enamel, J. Dent. Res., 75(9): 1679-1686.
2.
Hollinger, J.O. , Brekke, J., Gruskin , E. and Lee , D. (1996). Role of Bone Substitutes, Clin. Orthop., 324: 55-65.
3.
LeGeros, R.Z. and LeGeros, J.P. (1996). Calcium Phosphate Biomaterials in Medical Application, Bioceramics , 9: 7-10.
4.
Yuan, H., Li, Y., de Bruijn, J., de Groot, K. and Zhang, X. (2000). Tissue Responses of Calcium Phosphate Cement. A Study in Dogs, Biomaterials, 21(12): 1283-1290.
5.
Skrtic, D., Antonucci, J.M. and Eanes, E.D. (2003). Amorphous Calcium Phosphate-based Bioactive Polymeric Composites for Mineralized Tissue Regeneration, J. Res. Natl. Inst. Stands. Technol., 108(3): 167-182.
6.
Skrtic, D., Antonucci, J.M., Eanes, E.D. and Eidelman, N. (2004). Dental Composites Based on Hybrid and Surface-modified Amorphous Calcium Phosphates - A FTIR Microspectroscopic Study, Biomaterials, 25(7-8): 1141-1150.
7.
Eanes, E.D., Gillessen, I.H. and Posner, A.S. (1965). Intermediate States in the Precipitation of Hydroxyapatite , Nature, 208: 365-367.
8.
ASTM F394-78 (1991). Standard Test Method for Biaxial Strength of Ceramic Substrates.
9.
Vogel, G.L., Chow, L.C. and Brown, W.E. (1983). A Microanalytical Procedure for the Determination of Calcium, Phosphate and Fluoride in Enamel Biopsy Samples, Caries. Res., 17: 23-31.
10.
Murphy, J. and Riley, J.P. (1962). Single Solution Method for the Determination of Phosphate in Natural Waters, Anal. Chim. Acta., 27: 31-36.
11.
Wetzel, B., Haupert, F. and Zhang, M.Q. (2003). Epoxy Nanocomposites with High Mechanical and Tribological Performance, Comp. Sci. Technol., 63(14): 2055-2067.
12.
Ramalho, A. , Antunes, P.V., de Carvalho, M.D.B., Gil , H. and Rocha, J. (2006). Mechanical Properties of Particle Reinforced Resin Composites, Advanced Materials Forum III, PTS 1 and 2, Material Science Forum, 514-516: 619-623.
13.
Toledano, M. , Osorio, R., Osorio, E., Fuentes, V., Prati, C. and Garcia-Godoy , F. (2003). Sorption and Solubility of Resin-based Restorative Dental Materials, J. Dent., 31(1): 43-50.
14.
Ortengren, U., Wellendorf, H., Karlsson , S. and Ruyter, I.E. (2001). Water Sorption and Solubility of Dental Composites and Identification of Monomers Released in an Aqueous Environment, J. Oral. Rehab., 28(12): 1106-1115.
15.
Antonucci, J.M. and Skrtic, D. (2007). Physicochemical Properties of Bioactive Polymeric Composites: Effects of Resin Matrix and the Type of Amorphous Calcium Phosphate Filler, Polymers for Dental and Orthopedic Applications , pp. 217-242, Taylor and Francis Group LLC, Boca Raton, FL.
16.
Antonucci, J.M., O'Donnell, J.N.R. and Skrtic, D. (2007). Polymerization Shrinkage Stress Development and Mechanical Strength of ACP Acrylic Resin Composites , Polym. Mater. Sci. and Eng., 96: 229-231.
17.
Antonucci, J.M. , Icenogle, T.B., Regnault , W.F., Liu , D.W., O'Donnell, J.N.R. and Skrtic, D. (2006). Polymerization Shrinkage and Stress Development in Bioactive Urethane Acrylic Resin Composites, Polymer Preprints , 47(1): 498-499.
18.
Wachtman, J.B. , Capps, W. and Mandel, J. (1972). Biaxial Flexure Tests of Ceramic Substrates, J. Matls., 7: 188-194.
19.
Kirstein, A.F. and Woolley, R.M. (1967). Symmetrical Bending of Thin Circular Elastic Plates on Equally Spaced Point Supports, J. Res. Natl. Bur. Stands, 71C: 1-10.
20.
Ban, S. and Anusavice, K.J. (1990). Influence of Test Method on Failure Stress of Brittle Dental Material, J. Dent. Res., 69: 1791-1799.
21.
O'Donnell, J.N.R. , Antonucci, J.M. and Skrtic, D. (2006). Amorphous Calcium Phosphate Composites with Improved Mechanical Properties , J. Bioact. Compat. Polym., 21(3): 169-184.