Shear Behavior of 3-D Biaxial Spacer Weft Knitted Composite under High Strain Rates

Abstract

The punch shear behavior of 3-D biaxial spacer weft knitted E-glass/ vinyl ester composite was investigated at quasi-static (0.01/s) and high strain rates ranging from 1200 to 3200/s in wale and course directions respectively. The quasi-static shear behavior was tested on a MTS 810.23 material tester and was compared with high strain rate shear behavior from a modified split Hopkinson pressure bar (SHPB) technique. The experimental results indicate that the shear stiffness, failure stress, and failure strain are rate sensitive both in wale and course directions. The shear stiffness and failure stress increase with the the increase of strain rate. The failure strains along the wale and course directions decrease with increasing strain rate. Furthermore, the shear failure becomes more severe in the course direction than in the wale direction at high strain rates. The damage mode in the wale direction at various strain rates is punch shear failure, while that of the course direction is filament tow breakage and matrix cracks. The unique features of this article are to conduct the punch shear tests at high strain rates successfully using a modified SHPB apparatus for the novel 3-D knitted composite and find the strain rate sensitivity both in shear behavior and failure mode. The results will benefit the structural design of the 3-D knitted composite owing to the higher in-plane tension stiffness and strength of the composite than any other 3-D textile structural composites.

Keywords

3-D biaxial spacer weft knitted composite shear failure strain rate.

Get full access to this article

View all access options for this article.

References

Huysmans, G. , Gommers, B. and Verpoest, I. (1996). Mechanical Properties of (2-D) Warp Knitted Fabric Composites: An Experimental and Numerical Investigation, In: The 17th International SAMPE Europe Conference Proceedings, pp. 97-108, Basel, Switzerland.

Ramakrishna, S. , Hamada, H. , Rydin, R.W. and Chou, T.W. (1995). Impact Damage Resistance of Knitted Glass-fiber Fabric Reinforced Polypropylene Composites, Science and Engineering of Composite Materials, 4(2): 61-72.

Kang, T.J. and Kim, C. (1997). Mechanical and Impact Properties of Composite Laminates Reinforced with Kevlar Multiaxial Warp Knit Fabrics, Polymers and Polymer Composites, 5(4): 265-272.

Kang, T.J. and Kim, C. (2000). Energy-absorption Mechanisms in Kevlar Multiaxial Warp-knit Fabric Composites under Impact Loading, Composites Science and Technology, 60(5): 773-784.

Putnoki, I. , Moos, E. and Karger-Kocsis, J. (1999). Mechanical Performance of Stretched Knitted Fabric Glass Fiber Reinforced Poly(Ethylene Terephthalate) Composites Produced from Commingled Yarn, Plastics Rubber and Composites, 28(1): 40-46.

Sugun, B.S. and Rao, R.M.V.G.K. (2000). Drop Weight Impact Studies on Rib-knit RTM Laminates, Journal of Reinforced Plastics & Composites, 19(6): 492-508.

Khondker, O.A. , Herszberg, I. and Hamada, H. (2004). Measurements and Prediction of the Compression-after-Impact Strength of Glass Knitted Textile Composites , Composites Part A., 35(2): 145-157.

Lam, S.W. , Tao, X.M. and Yu, T. (2004). Comparison of Different Thermoplastic Cellular Textile Composites on their Energy Absorption Capacity , Composites Science and Technology, 64(13-14): 2177-2184.

Zhou, R.X. , Hu, H. , Chen, N.L. and Feng, X.W. (2005). An Experimental and Numerical Study on the Impact Energy Absorption Characteristics of the Multiaxial Warp Knitted (MWK) Reinforced Composites, Journal of Composite Materials, 39(6): 525-542.

10.

Khondker, O.A. , Leong, K.H. , Herszberg, I. and Hamada, H. (2005). Impact and Compression-after-impact Performance of Weft-knitted Glass Textile Composites, Composites Part A., 36(5): 638-648.

11.

Bartels, V.T. (2003). Thermal Comfort of Aeroplane Seats: Influence of Different Seat Materials and the Use of Laboratory Test Methods, Applied Ergonomics, 34(4): 393-399.

12.

Meyers, M.C. (1995). Dynamic Behavior of Materials, John Wiley & Sons, Inc., New York.

13.

Hosur, M.V. , Adya, M. , Vaidya, U.K. , Mayer, A. and Jeelani, S. (2003). Effect of Stitching and Weave Architecture on the High Strain Rate Compression Response of Affordable Woven Carbon/Epoxy Composites, Composite Structures, 59(4): 507-523.

14.

Sun, B.Z. , Gu, B.H. and Ding, X. (2005). Compressive Behavior of 3-D Angle-interlock Woven Fabric Composites at Various Strain Rates, Polymer Testing, 24(4): 447-454.

15.

Sun, B.Z. , Yang, L. and Gu, B.H. (2005). Strain Rate Effect on Four-step Three-dimensional Braided Composite Compressive Behavior, AIAA Journal, 43(5): 994-999.

16.

Sun, B.Z. , Liu, F. and Gu, B.H. (2005). Influence of the Strain Rate on the Uniaxial Tensile Behavior of 4-step 3-D Braided Composites, Composites Part A, 36(11): 1477-1485.

17.

Hallett, S.R. , Ruiz, C. and Harding, J. (1999). The Effect of Strain Rate on the Interlaminar Shear Strength of a Carbon/Epoxy Cross-Ply Laminate: Comparison Between Experiment and Numerical Prediction, Composites Science and Technology, 59(5): 749-758.

18.

Khashaba, U.A. (2004). In-plane Shear Properties of Cross-ply Composite Laminates with different Off-axis Angles, Composite Structures, 65(2): 167-177.

19.

Tsai, J.L. and Sun, C.T. (2005). Strain Rate Effect on In-plane Shear Strength of Unidirectional Polymeric Composites, Composites Science and Technology, 65(13): 1941-1947.

20.

Hosur, M.V. , Islam, S.M.W. , Vaidya, U.K. , Dutta, P.K. and Jeelani, S. (2004). Experimental Studies on the Punch Shear Characterization of Satin Weave Graphite/Epoxy Composites at Room and Elevated Temperatures, Materials Science and Engineering A, 368(1-2): 269-279.

21.

Hosur, M.V. , Islam, S.M.W. , Vaidya, U.K. , Kumar, A. , Dutta, P.K. and Jeelani, S. (2005). Dynamic Punch Shear Characterization of Plain Weave Graphite/Epoxy Composites at Room and Elevated Temperatures , Composite Structures, 70(3): 295-307.

22.

Harding, J. and Li, Y.L. (1992). Determination of Interlaminar Shear-strength for Glass Epoxy and Carbon Epoxy Laminates at Impact Rates of Strain, Composites Science and Technology, 45(2): 161-171.

23.

Schlenker, U. (2004). 50 Years of Warp Knitting , International Textile Bulletin, 50(3): 80-82.

24.

Haque, A. and Hossain, M.K. (2003). Effects of Moisture and Temperature on High Strain Rate behavior of S2-glass-vinyl Ester Woven-composites, Journal of Composite Materials, 37(7): 627-647.

25.

Haque, A. (2005). High Strain Rate Responses and Failure Analysis in Polymer Matrix Composites - An Experimental and Finite Element Study, Journal of Composite Materials, 39(5): 423-450.

26.

Pandita, S.D. , Falconet, D. and Verpoest, I. (2002). Impact Properties of Weft Knitted Fabric Reinforced Composites, Composites Science and Technology, 62(7-8): 1113-1123.

27.

de Carvalho, L.H. , Cavalcante, J.M.F. and d'Almeida , J.R.M. (2006). Comparison of the Mechanical Behavior of Plain Weave and Plain Weft Knit Jute Fabric-polyester-reinforced Composites, Polymer-plastics Technology and Engineering, 45(7): 791-797.

28.

Wonderly, C. , Grenestedt, J. , Fernlund, G. and Cepus, E. (2005). Comparison of Mechanical Properties of Glass Fiber/vinyl Ester and Carbon Fiber/Vinyl Ester Composites , Composites Part B, 36(5): 417-426.