Effects of Ultraviolet Radiation on Mechanical Properties of Glass/Polyester Composites

Abstract

The increased use of fiber-reinforced polyester composites in an outdoor environment has led to questions concerning the environmental durability of these materials, particularly as related to ultraviolet (UV) exposure. In this research the effects of UV radiation on mechanical properties of glass/polyester composites were studied. Since the photo degradation is a surface mechanism and is restricted to degradation of mechanical properties of resin (fiber is not degraded), this research is focused on resin properties. For this reason, test samples made of polyester resin were prepared and treated in a UV chamber through accelerated tests. Three types of specimen were manufactured. The tensile testing samples were prepared based on ASTM D638 standard with a nominal thickness of 1 mm. Also, Arcan specimens for shear tests and ASTM D3410 for compression tests were manufactured. To obtain time dependent mechanical properties of polyester resin under UV radiation, samples were radiated in three different time intervals, equivalent to 3, 6 and 12 months, using an artificial UV exposure chamber. Test specimens were tested under tension load and showed a decrease of up to 15% in average failure strain, a decrease of up to 30% in ultimate strength, and 18% decrease in tensile modulus after 100 h exposure. Also, significant changes were considered in shear modulus and strength of polyester. The effect of ultraviolet absorbers (UVA) on preventing polyester mechanical properties degradation is also studied. The results showed that the samples which have UVA additives were not degraded after UV exposure.

After obtaining matrix properties due to exposure, mechanical properties of unidirectional laminate of glass/polyester composites under UV radiation were simulated using micromechanics theories. The results of simulation were validated with tensile testing of ASTM D3039 specimens of [0/90]s glass/polyester laminated composites. The results show that shear modulus of this laminate decreased about 20% due to UV exposure.

Keywords

ultraviolet accelerated tests glass/polyester mechanical properties degradation absorbers.

Get full access to this article

View all access options for this article.

References

Jones, M.S. (2002). Effects of UV Radiation on Building Materials , Building Research Association of New Zealand (BRANZ) , 26—28 March 2002, Antarctic Centre , Christchurch, New Zealand.

Andrady, A.L. , Hamid, S.H. , Hu , X. and Torikai, A. (1998). Effects of Increased Solar Ultraviolet Radiation on Materials, Journal of Photochemistry and Photobiology B: Biology, 46: 96—103.

Owen, E.D. (Ed.) (1984). Degradation and Stabilization of PVC, Elsevier Applied Science, London, pp. 81—136.

Chin, J.W. , Martin, J. , and Nguyen, T. (2001). Gap Analysis for Durability of Fiber Reinforced Polymer Composites in Civil Infrastructure, Chapter 8, Effects of Ultraviolet (UV) Radiation, American Society of Civil Engineers.

Jacques, L.F.E. (2000). Accelerated and Outdoor/Natural Exposure Testing of Coatings, Prog. Polym. Sci., 25: 1337—1362.

Andrady, A.L. , Hamid, H.S. and Torikai, A. (2003). Effects of Climate Change and UV-B on Materials, Photochem. Photobiol. Sci., 2(1): 68—72.

Bauer, D.R. (2000). Interpreting Weathering Acceleration Factors for Automotive Coatings Using Exposure Models, Polymer Degradation and Stability, 69: 307—316.

Weathering Test Methods, http://www.atlaswsg.com/testmeth.html

10.

Bauer, D.R. (2000). Global Exposure Models for Automotive Coating Photo-oxidation, Polymer Degradation and Stability, 69: 297—306.

11.

ASTMD 638-96, Standard Test Method for Tensile Properties of Plastics.

12.

ASTMD 3039-76, Standard Test Method for Tensile Properties of Fiber—Resin Composites.

13.

ASTMD 3410-87, Standard Test Method for Compressive Properties of Unidirectional Fiber— Resin Composites.

14.

Adams, D.F. , Carlsson, L.A. and Pipes, B. (2003). Experimental Characterization of Advanced Composites Materials, CRC Press, Boca Raton , USA.

15.

ASTMD 5071-91, Standard Practice for operating Xenon Arc Type Exposure Apparatus with Water for Exposure of Photodegradable Plastics.

16.

Hyer, M.W. (1997). Stress Analysis of Fiber-Reinforced Composite Materials, McGraw-Hill Book Company, New York.

17.

Agarwall, B.D. and Broutman, L.J. (1990). Analysis and Performance of Fiber Composites, John Wiley & Sons Inc.

18.

Tsai, S.W. and Hahn, H.T. (1980). Introduction to Composite Materials, Technomic Publishing Company.