Effect of Stitching on the Static and Fatigue Performance of Co-Cured Composite Single-Lap Joints

Abstract

The paper investigates the effect of Kevlar stitching on the tensile static and fatigue properties of co-cured single-lap joints with cross-ply graphite- epoxy adherends. The variables considered in this study were the overlap length, the stitch spacing, and the off-edge distance. Experimental results indicate that while stitching does not improve the static strength, stitched joints exhibit much better fatigue performance than unstitched joints. Ultrasonic analyses and continuous monitoring of stiffness change during fatigue life allowed us to follow delamination progression and to clearly identify the nucleation and the propagation stages, in particular, stitching was observed to increase the durations of both the crack initiation and crack propagation phases, with stitches remaining intact until complete failure. Moreover, in the range of values examined, the fatigue behavior of stitched joints is improved by reducing the stitch spacing, while it appears to be insensitive to the variation of the off-edge distance of stitches.

Keywords

stitching single-lap joints fatigue debonding

Get full access to this article

View all access options for this article.

References

1. Gillespie, J.W. , Bourban, P.E. and Tierney, J.J. (2000). Joining of Composites, In: Talreja, R. (ed.), Comprehensive Composite Materials - Polymer Matrix Composites, Vol. 2, Elsevier Science, Amsterdam.

2. Tong, L. and Steven, G.P. (1999). Analysis and Design of Structural Bonded Joints, Kluwer Academic Publishers, Boston.

3. Sawyer, J.W. and Cooper, P.A. (1981). Analytical and Experimental Results for Bonded Single Lap Joints with Preformed Adherend, AIAA Journal, 107(11): 1443-1451.

4. Zeng, Q. and Sun, C.T. (2001). Fatigue Performance of a Bonded Wavy Composite Lap Joints, In: Proc. 42nd AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference and Exhibit, Seattle, WA, Apr. 16-19, 2001, AIAA Paper 2001-1488.

5. Coates, C.W. and Armanios, E.A. (2000). An Assessment of Nested Overlap and Transverse Interfacial Layer in Co-cured Composite Single Lap Joints, In: Proceedings of the 15th American Society of Composites, September 24-27, Texas A&M University, College Station, Texas, pp. 1161-1171.

6. Jang, B.Z. (1998). Material Design Approach for Improving Impact Resistance of Composites, Key Engineering Materials, 141-143: 169-186.

7. Sawyer, J.W. (1985). Effect of Stitching on the Strength of Bonded Composite Single Lap Joints, AIAA Journal, 23: 1744-1748.

8. Dransfield, K. , Baillie, C. and Mai, Y.W. (1994). Improving the Delamination Resistance of CFRP by Stitching - A Review, Composites Science and Technology, 50: 305-317.

9. Mouritz, A.P. , Bannister, M.K. and Falzon, P.J. and Leong, K.H. (1999). Review of Applications for Advanced Three-Dimensional Fibre Textile Composites, Composites Part A: Applied Science and Manufacturing, 30: 1445-1461.

10.

10. Pelstring, R.M. and Madan, R.C. (1989). Stitching to Improve Damage Tolerance of Composites, In: Proceedings 34th International SAMPE Symposium, 8-11 May 1989, pp. 1519-1528.

11.

11. Dransfield, K.A. , Jain, L.K. and Mai, Y.W. (1998). On the Effects of Stitching in CFRPs - I. Mode I Delamination Toughness, Composites Science and Technology, 58: 815-828.

12.

12. Sankar, B.V. and Sharma, S.K. (1997). Mode II Delamination Toughness of Stitched Graphite/ Epoxy Textile Composites, Composites Science and Technology, 57: 729-737.

13.

13. Jain, L.K. , Dransfield, K.A. and Mai, Y.W. (1998). On the Effects of Stitching in CFRPs - II. Mode II Delamination Toughness, Composites Science and Technology, 58: 829-837.

14.

14. Aymerich, F. , Priolo, P. and Sun, C.T. (2003). Static and Fatigue Behaviour of Stitched Graphite/Epoxy Composite Laminates, Composites Science and Technology, 24: 907-917.

15.

15. Tada, Y. and Ishikawa, T. (1989). Experimental Evaluation of the Effects of Stitching on CFRP Laminate Specimens with Various Shapes and Loading, Key Engineering Materials, 37: 305-316.

16.

16. Lee, C. and Liu, D. (1990). Tensile Strength of Stitching Joint in Woven Glass Fabrics, Journal of Engineering Materials and Technology, 112: 125-130.

17.

17. Tong, L. , Cleaves, K. , Kruckenberg, T. and Steven, G.P. (1998). Strength of RTM Single Lap Joints with Transverse Stitching, Key Engineering Materials, 137: 195-202.

18.

18. Tong, L. , Jain, L.K. , Leong, K.H. , Kelly, D. and Herszberg, I. (1998). Failure of Transversely Stitched RTM Lap Joints, Composites Science and Technology, 58: 221-227.

19.

19. Jain, L.K. , Leong, K.H. , Mai, Y.W. and Tong, L. (1998). Effect of Through-Thickness Stitching on the Fatigue Life of Composite Single-Lap Joints, Applied Composite Materials, 5: 399-409.

20.

20. Glaessgen, E.H. , Raju, I.S. and Poe, C.C., Jr. (1999). Delamination and Stitch Failure in Stitched Composite Joints, In: Proc. 40th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference and Exhibit, April 12-15, St. Louis, Missouri, AIAA Paper 99-1247.