Evaluation of Bolt Bearing Behavior of Highly Loaded Composite Joints at Elevated Temperature

Abstract

The high load intensities and elevated temperature in the wing and fuselage of a supersonic transport aircraft will result in bolted joints stack-up thickness much greater than the current subsonic transport aircraft. Bolt bearing– bypass tests were conducted to develop a database and a bearing–bypass stress interaction for the design community. All test coupons are IM7/PETI-5 quasi-isotropic laminates (64 plies) with a bolt-hole for a 0.95 cm diameter fastener. Static tests were conducted at room temperature as well as at 177 C. Thermo-mechanical fatigue tests were conducted using a typical supersonic transport flight spectrum loading. Short-term creep tests,of 250 h,indicated that IM7/PETI-5 quasi-isotropic (64 plies) laminates has improved properties over IM7/K3B. Long-term creep tests, of 10,000 h, demonstrate that IM7/PETI-5 is highly creep resistant for long periods. Test results also show that these composites experience very little hole elongation before failing in a bearing mode.

Keywords

bearing bypass creep

Get full access to this article

View all access options for this article.

References

1. Counts,W. A. and Johnson,W. S. (2002). Bolt Bearing Fatigue of Polymer Matrix Composites at Elevated Temperature, International Journal of Fatigue, 24: 197–204.

2. Counts,W. A. and Johnson,W. S. (2002). Temperature Effect on Ultimate Bearing Strength of Polymeric Composite Joints, Journal of Composites Technology and Research, 24(1): 17–23.

3. Wright,R. J. , Johnson,W. S. , Sacks,S. and Ahmad,H. (January 2000). Bolt Bearing Behavior of Highly Loaded Polymer Matrix Composite Joints at Elevated Temperature with and without Clamp-Up, Journal of Composite Technology and Research, 22(1): 33–39.

4. Kallmeyer,A. R. and Stephens,R. I. (1997). Creep Elongation of Bolt Holes Subjected to Bearing Loads in a Polymer Matrix Composite Laminate. In: Armanios,E. A. (ed.), Composite Materials: Fatigue and Fracture,Vol. 6,ASTM STP 1285,pp. 452–467,American Society for Testing and Materials,West Conshohocken,PA.

5. Crews,Jr. , J. H. and Naik,R. V. A. (1986). Failure Analysis of a Graphite/Epoxy Laminate Subjected to Bolt Bearing Loads. In: Hahn,H. T. (ed.), Composite Materials: Fatigue and Fracture,ASTM 907,pp. 115–133,American Society for Testing and Materials,West Conshohocken,PA.