Cure Kinetic Model,Heat of Reaction,and Glass Transition Temperature of AS4/3501-6 Graphite

Abstract

A new isothermally-based, cure kinetic model for the carbon graphite–epoxy AS4/3501-6 prepreg is presented using an industrially supplied prepreg rather than the neat epoxy resin. A two-stage model is used: first, rate-controlled (autocatalytic); then diffusion-controlled. A Differential Scanning Calorimeter (DSC) is employed to investigate the prepreg’s cure kinetics using both isothermal and dynamic DSC scans, although only isothermal DSC scan data is used to fit the model’s parameters. A Thermogravimetric Analyzer (TGA) is used to determine the mass fraction of the epoxy resin in the prepreg. The coefficients are provided for a prepreg having 37.4% resin mass fraction; they must be re-evaluated for prepregs having significantly different resin mass fractions.

The ultimate heat of reaction of the resin incorporated within the prepreg is measured as 433.7 J/g (based upon a linear baseline) or 422.7 J/g (based upon a specific-heat-corrected baseline) using dynamic DSC scans at 20°C/min. This value is 8–17% less than the reported 472–508 J/g for the neat 3501-6 epoxy also measured using dynamic DSC scans at 20°C/min. Important to manufacturing applications, dynamic DSC scans reveal that the prepreg’s ultimate heat of reaction is sensitive to scan rate. Finally, the prepreg’s carbon fiber and/or sizing appears to suppress the curing reaction and decrease the ultimate heat of reaction over that for the neat epoxy resin.

The glass transition temperature T _g (°C) of partially-cured AS4/3501-6 prepregs is measured using DSC and is expressed as a function of degree of cure: T _g = 22.9 exp(2.16α) – markedly similar to 3501-6 neat resin T _g data measured earlier using a dynamic mechanical analyzer. The small specimen DSC thermal scans provide an effective means to measure the T _g of completely- or partially-cured prepregs. The T _g of the 100%-cured prepreg was experimentally determined to be 199°C, slightly higher than the 193°C reported for the 100%-cured neat epoxy resin. The AS4 fibers play little or no role in the degree-of-cure dependence of the AS4/3501-6 prepreg’s T _g.

Recommended for general purpose structural applications, the AS4/3501-6 prepreg is composed of continuous, PAN-based, AS4C carbon (graphite) fibers and an amine-cured epoxy resin system. The epoxy resin, 3501-6, is a tetraglycidyl diamino diphenyl methane (TGDDM) with diaminodiphenylsulfone (DDS) catalyzed with boron trifluoride monoethylamine. 3501-6 was developed to operate in atemperature environment of up to 350°F (177°C).

Keywords

cure kinetics heat of reaction enthalpy of reaction glass transition temperature graphite–epoxy prepreg amine-cured epoxy resin thermoset differential scanning calorimetry thermogravimetric analysis polymer composite composite processing process simulation

Get full access to this article

View all access options for this article.

References

1. Gupta, S. , Agarwal, B. D. and Kumar, A. (1994). Semianalytical Solution for Epoxy-amine Curing in the Presence of Nonisothermal Effects, Polymer Engineering Science, 34: 405–413.

2. Lee, J. H. and Lee, J. W. (1994). Kinetic Parameters Estimation for Cure Reaction of Epoxy Based Vinyl Ester Resin, Polymer Engineering Science, 34: 742–749.

3. Chiao, L. and Lyon R. E. (1990). A Fundamental Approach to Resin Cure Kinetics, Journal of Composite Materials, 24: 739–752.

4. Kamal, M. R. (1974). Thermoset Characterization for Mobility Analysis, Polymer Engineering and Science, 14: 231–239.

5. Sourour, S. and Kamal, M. R. (1976). Differential Scanning Calorimetry of Epoxy Cure: Isothermal Cure Kinetics, Thermochimica Acta, 14: 41–59.

6. Lee, W. I. , Loos, A. C. and Springer, G. S. (1982). Heat of Reaction, Degree of Cure, and Viscosity of Hercules 3501–6 Resin, Journal of Composite Materials, 16: 510–520.

7. Ryan, M. E. and Dutta, A. (1979). Kinetics of Epoxy Cure: A Rapid Technique for Kinetic Parameter Estimation, Polymer, 20: 203–206.

8. Mijovic, J. (1986). Cure Kinetics of Neat Versus Reinforced Epoxies, Journal of Applied Polymer Science, 31: 1177–1187.

9. Fava, R. A. (1968). Differential Scanning Calorimetry of Epoxy Resins, Polymer, 9: 137–151.

10.

10. Kim, D. S. and Kim, S. C. (1994). Rubber Modified Epoxy Resin. 1: Cure Kinetics and Chemorheology, Polymer Engineering Science, 34: 625–631.

11.

11. Prime, R. B. (1970). Dynamic Cure Analysis of Thermosetting Polymers, Analytical Calorimetry, 2: 201–210.

12.

12. Prime, R. B. (1973). Differential Scanning Calorimetry of the Epoxy Cure Reaction, Polymer Engineering and Science, 13: 365–371.

13.

13. Bhi, S. T. , Hansen, R. S. , Wilson, B. A. , Calius, E. P. and Springer, G. S. (1987). Degree of Cure, and Viscosity of Hercules HBRF-55 Resin, 32nd International SAMPE Symposium, pp. 1114–1118.

14.

14. Dusi, M. R. , Lee, W. I. , Ciriscioli, P. R. and Springer, G. S. (1987). Cure Kinetics and Viscosity of Fiberite 976 Resin, Journal of Composite Materials, 21: 243–261.

15.

15. White, S. R. and Hahn, H. T. (1992). Process Modeling of Composite Materials: Residual Stress Development during Cure. Part II. Experimental Validation, Journal of Composite Materials, 26: 2423–2453.

16.

16. Pappalardo, L. T. (1977). DSC Evaluation of Epoxy and Polyimide-impregnated Laminates (Prepreg), Journal of Applied Polymer Science, 809–820.

17.

17. Shin, D. D. and Hahn, H. T. (2000). A Consistent Cure Kinetic Model for AS4/3502 Graphite/Epoxy, Composites: Part A Applied Science and Manufacturing, 31: 991–999.

18.

18. Muzzy, J. D. , Abouelnasr, D. M. and Kays, A. O. (1988). Melting and Solidification of APC-2. In: Proceedings of 33rd International SAMPE Symposium and Exhibition, pp. 1319–1330.

19.

19. Thomason, J. L. (1993). Fiber-induced Acceleration of Matrix Degradation in Thermoplastic Composites, Plastic, Rubber and Composites Processing and Applications, 20: 265–270.

20.

20. Hou, T. H. and Bal, J. M. (1988). A Semi-empirical Approach for the Chemoviscosity Modeling of Reactive Resin System, SAMPE Journal, 24(6): 43–51.

21.

21. Brennan, W. P. (1970). Theory and Practice of Thermoanalytical Calorimetry, PhD Dissertation, Princeton University, Princeton, NJ.

22.

22. Chern, B. -C. (1994). Heat Transfer Analysis of In-situ Curing for Thermoset Preimpregnated Tape-hoop-wound Structures Using Infrared Heating, PhD Dissertation, The University of Texas at Austin.

23.

23. Chern, B. -C. , Moon, T. J. , Howell, J. R. and Tan, W. (2002). New Experimental Data for Enthalpy of Reaction and Temperature- and Degree-of-Cure-Dependent Specific Heat and Thermal Conductivity of the Hercules 3501-6 Epoxy System, Journal of Composite Materials, 36: 2061–2072.

24.

24. Brennan, W. P. and Cassel, R. B. (1978). Applications of Thermal Analysis in the Electrical and Electronics Industries, Thermal Analysis Application Study 25, Perkin Elmer Co., Wellesley, MA, pp. 1–13.

25.

25. White, S. R. and Kim, C. (1993). A Simultaneous Lay-up and In-situ Cure Process for Thick Composites, Journal of Reinforced Plastics and Composites, 12: 520–535.

26.

26. Prime, R. B. and Sacher, E. (1972). Kinetics of Epoxy Cure: 2. The System Bisphenol-A Diglycidyl Ether/Polyamide, Polymer, 13: 455–458.

27.

27. Turi, E. A. (1981). Thermal Characterization of Polymeric Materials, Academic Press, San Diego, CA.

28.

28. Hoffman, R. E. and Boll, D. J. (1984). The Use of Dynamic Gel Temperatures to Develop Cure Cycles, 29th National SAMPE Symposium, pp. 1411–1421.

29.

29. Flory, P. J. (1953). Principles of Polymer Chemistry, Cornell University Press, Ithaca, NY.

30.

30. Kamal, M. R and Sourour, S. (1973). Kinetics and Thermal Characterization of Thermoset Cure, Polymer Engineering and Science, 13: 59–64.

31.

31. SAS/STAT User’s Guide (1990). Version 6, 4th Edn. SAS Institute, Cary, NC.

32.

32. Carlsson, L. A. (1991). Thermoplastic Composite Materials, Composite Materials Series, Vol. 7, Elsevier Science Publishers, Oxford UK.

33.

33. Brennan, W. P. (February 1975). Differential Scanning Calorimetry – A Method for Polymer Quality Control, American Laboratory.

34.

34. Gray, A. P. (1972). Establishing a Correlation Between the Degree of Cure and the Glass Transition Temperature of Epoxy Resins, Thermal Analysis Application Study 2, Perkin Elmer Co., Wellesley, MA, pp. 1–9.

35.

35. Kim, Y. K. and White, S. R. (1996). Stress Relaxation Behavior of 3501–6 Epoxy Resin During Cure, Polymer Engineering Science, 36(23): 2852–2862.

Cure Kinetic Model,Heat of Reaction,and Glass Transition Temperature of AS4/3501-6 Graphite–Epoxy Prepregs

Abstract

Keywords

Get full access to this article

References